Acid-modified white ash compound basic lead phosphate auxiliary and preparation method thereof

A technology of lead phosphite additives and white soot, which is applied in the field of acidification modified white soot compound salt-based lead phosphite additives and its preparation, which can solve the problems of large fluctuations in phase composition, difficult processing methods, complex soot components, etc. Problems, to achieve the effect of good product performance, avoid poisoning, wide source of raw materials and low price

Inactive Publication Date: 2018-05-04
NORTHWEST RES INST OF MINING & METALLURGY INST
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the influence of raw materials, process methods and process conditions, the soot produced by copper smelting has complex components and large fluctuations in phase composition, so it is difficult to have a unified treatment method, especially the tailings leaching valuable metals still contain soluble metals and Toxic and harmful heavy non-ferrous metal elements, direct discharge will cause environmental pollution, and can only be stored and disposed of as hazardous waste, which has a great impact on environmental protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Acid-modified white ash compound basic lead phosphate auxiliary and preparation method thereof
  • Acid-modified white ash compound basic lead phosphate auxiliary and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] (1) Raw materials for the test: The copper smelting product of the copper smelting plant of the Baiyin Nonferrous Metals Group Co., Ltd. was used as the raw material for electro-recovery comprehensive soot (white soot). The composition of the white soot is shown in Table 1.

[0023] (2) Preparation method:

[0024] a. Add water, white soot and glacial acetic acid into the acid-resistant leaching tank in sequence according to the solid-to-liquid ratio of 1:3:0.005, start stirring at a speed of 120r / min, and stir to form a slurry;

[0025] b. Weigh phosphorus trichloride with 20% of the mass of white soot, and then slowly drop it into the above slurry under stirring, the dropping time is 60min, and the stirring speed is 120r / min; the dropping process and the leaching process must be ventilated Good, to prevent the generation of arsine or phosphine.

[0026] c. After adding phosphorus trichloride, heat to 50°C and continue the leaching reaction for 5 hours.

[0027] d. A...

Embodiment 2

[0031] (1) Raw materials for the test: The copper smelting product of the copper smelting plant of the Baiyin Nonferrous Metals Group Co., Ltd. was used as the raw material for electro-recovery comprehensive soot (white soot). The composition of the white soot is shown in Table 1.

[0032] (2) Preparation method:

[0033] a. Add water, white soot and glacial acetic acid into the acid-resistant leaching tank in sequence according to the solid-to-liquid ratio of 1:5:0.02, start stirring at a speed of 90r / min, and stir to form a slurry;

[0034] b. Weigh phosphorus trichloride with 40% mass of white soot, and then slowly drop it into the above slurry under stirring, the dropping time is 30min, and the stirring speed is 90r / min; the dropping process and leaching process must be ventilated Good, to prevent the generation of arsine or phosphine.

[0035] c. After adding phosphorus trichloride, heat to 50°C and continue the leaching reaction for 2 hours.

[0036] d. After the leach...

Embodiment 3

[0040] (1) Raw materials for the test: The copper smelting product of the copper smelting plant of the Baiyin Nonferrous Metals Group Co., Ltd. was used as the raw material for electro-recovery comprehensive soot (white soot). The composition of the white soot is shown in Table 1.

[0041] (2) Preparation method:

[0042] a. Add water, white soot and glacial acetic acid into the acid-resistant leaching tank in sequence according to the solid-to-liquid ratio of 1:4:0.01, start stirring at a speed of 120r / min, and stir to form a slurry;

[0043] b. Weigh phosphorus trichloride with 30% of the mass of white soot, and then slowly drop it into the above slurry under stirring, the dropping time is 45min, and the stirring speed is 120r / min; the dropping process and the leaching process must be ventilated Good, to prevent the generation of arsine or phosphine.

[0044] c. After adding phosphorus trichloride, heat to 70°C and continue the leaching reaction for 4 hours.

[0045] d. Af...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an acid-modified white ash compound basic lead phosphate auxiliary. White ash which is produced in a copper smelting process and is collected by virtue of an electrical dust precipitation process and phosphorus trichloride are adopted as raw materials, reaction is carried out under the catalytic action of glacial acetic acid for removing soluble metal ions, insoluble metalions are modified to generate precipitates, and filtering and drying are carried out, so that the acid-modified white ash compound basic lead phosphate auxiliary is obtained. The acid-modified white ash compound basic lead phosphate auxiliary disclosed by the invention has the advantages that industrial waste slag is adopted as a raw material, the raw material is extensive in source and low in price; and a preparation method of the acid-modified white ash compound basic lead phosphate auxiliary is simple and reasonable in operation, poisoning caused by lead dust during production and use is avoided, and product performance is good, so that the acid-modified white ash compound basic lead phosphate auxiliary is applicable to industrial production.

Description

technical field [0001] The invention specifically relates to an acidified modified white soot composite base lead phosphite additive and a preparation method thereof. Background technique [0002] Dibasic lead phosphite is a white or slightly yellow powder. Because of its excellent properties such as weather resistance, thermal stability, electrical insulation, etc., it also has the properties of anti-oxidation and UV shielding. Therefore, it is widely used as heat stabilizer for polyvinyl chloride and polyvinyl chloride / polyethylene copolymer, especially opaque hard and soft products such as outdoor cables, building boards, corrugated boards, and pipes. The traditional dibasic lead phosphite is produced from green lead, acetic acid, liquid caustic soda and phosphorous acid, or from lead oxide and phosphorous acid. The production process is complicated, the cost is high, and the dust is large during use. The number of measurements is large, and measurement errors are prone...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08K3/32C08K3/34C08L27/06
CPCC08K3/32C08K3/34C08L2201/08C08L27/06
Inventor 王永斌吴克富王怡霖周俊涛吴斌周涛黄建芬张红许素敏
Owner NORTHWEST RES INST OF MINING & METALLURGY INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap