Tickling-feeling-free moisture-absorbing quick-drying wool knitted fabric and preparation method thereof

A wool knitted fabric, moisture absorption and quick drying technology, applied in knitting, weft knitting, textiles and papermaking, etc., can solve the problems of itching, poor anti-pilling performance, fast drying and slow drying, etc., achieve no itching, easy to promote , The effect of simple preparation process

Inactive Publication Date: 2018-05-18
SHANGHAI CHALLENGE TEXTILE
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the characteristics of its fiber structure, the fabrics and clothing made of wool not only have the advantages of good moisture absorption, good warmth retention, and good resilience, but also have low strength, itching, fast drying and slow, and anti-pilling properties. Insufficient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Tickling-feeling-free moisture-absorbing quick-drying wool knitted fabric and preparation method thereof
  • Tickling-feeling-free moisture-absorbing quick-drying wool knitted fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Use 60N / 1 shrink-proof wool 18.5M and 2D modified polyester as raw materials, and blend them into yarns according to the ratio of wool 35 / modified polyester 65; weave the blended yarns into weft-knitting single-jersey knitting with concave-convex network structure Fabric, specific weaving structure such as figure 2 Shown; the fabric is deoiled and impurity-removed, using 1g / L DEPICOL JT (ZSCHIMMER&SCHWARZ Sima Chemical Co., Ltd.), treated at 60°C for 20min, and then wool comfort finishing, using 2% owf HS-3732 (Shanghai Hansong Textile Co., Ltd. Technology Co., Ltd.) and 1% owf SILIGEN SIH NANO (Archroma Chemicals (China) Co., Ltd.), treated at 40°C for 20 minutes to produce non-itchy moisture-absorbing and quick-drying wool knitted fabrics, such as figure 1 As shown, it can be seen that the fabric is a concave-convex mesh single-sided structure.

[0024] The wicking height of the fabric prepared in this embodiment: 16cm; water absorption speed: 1S; evaporation rate:...

Embodiment 2

[0026] 90N / 1 shrink-proof wool 15.5M and 1.5D modified polyester are used as raw materials, blended into yarn according to the ratio of wool 50 / modified polyester 50; the blended yarn is woven into weft-knitted single-sided with concave-convex network structure Knitted fabrics; the fabrics were degreased and impurity-removed, using 1g / L DEPICOL JT (ZSCHIMMER&SCHWARZ Sima Chemical Co., Ltd.), treated at 60°C for 20 minutes, and then treated for wool comfort, using 2% owf HS-3732 (Shanghai Hansong Textile Co., Ltd. Technology Co., Ltd.) and 1% owf SILIGEN SIH NANO (Archroma Chemicals (China) Co., Ltd.), treated at 40°C for 20 minutes to obtain a non-itchy moisture-absorbing and quick-drying wool knitted fabric.

[0027] The wicking height of the fabric prepared in this embodiment: 15.6cm; water absorption speed: 1S; evaporation rate: 0.22g / hr, can achieve breathability, quick drying; and no itching, skin-friendly and soft characteristics.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a tickling-feeling-free moisture-absorbing quick-drying wool knitted fabric and a preparation method thereof. The fabric has a concave and convex mesh-shaped weft knitted single stitch structure. The preparation method comprises the steps that wool with the fineness not exceeding 18.5 M and modified polyester with the fineness not exceeding 2D are selected and blended intoyarn; the blended yarn is knitted into the weft knitted single knitted fabric with the concave and convex mesh-shaped stitch structure; fabric finishing is conducted, and the tickling-feeling-free moisture-absorbing quick-drying wool knitted fabric is obtained. The fabric has the functions of absorbing moisture, achieving ventilation, keeping warm and achieving quick drying, the fabric is soft inhandfeeling, friendly to skin and comfortable; the fabric preparation technology is simple, and popularization is easy.

Description

technical field [0001] The invention belongs to the technical field of functional textile fabrics, in particular to a non-itchy, moisture-absorbing, quick-drying wool knitted fabric and a preparation method thereof. Background technique [0002] Wool is an important high-grade raw material for the textile industry. Wool fiber contains a lot of air, which can insulate heat and cold; it has high hygroscopicity, and the quality of water vapor absorbed can reach more than 30% (cotton only has about 8%), and there is no damp feeling when wearing, and it can adjust the microclimate of clothing. The micropores in the cells of the fiber surface allow water vapor to pass through freely. These properties allow wool fabrics to be worn in both warm and cold conditions, and they occupy an important place in the high-end sportswear market in developed countries. With the development of the economy and the gradual improvement of people's living standards, the requirements for the comfort...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D04B1/10D04B1/12D04B1/14D04B1/16
CPCD04B1/12D04B1/102D04B1/14D04B1/16D10B2211/02D10B2331/04
Inventor 王任杨启东张义男赖俊杰陈小湘
Owner SHANGHAI CHALLENGE TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap