A kind of preparation method of non-mold water corrugated glazed ceramic brick

A corrugated glaze and water ripple technology, which is applied in the field of preparation of non-mold water ripple glazed ceramic tiles, can solve the problems of increased production and research and development costs, difficulty in new changes, and single and fixed effects.

Active Publication Date: 2021-02-05
广东永航新材料实业股份有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The traditional antique brick glaze texture effect is mostly reflected by the ligand mold (screen or rubber roller) effect, but the use of mold will greatly increase the production and development costs, and the effect is single and fixed, so it is difficult to make new changes

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0024] A method for preparing a non-mold water ripple type glazed ceramic tile, comprising:

[0025] The step of preparing the embryo body: ball milling, pressing, and firing the raw material of the embryo body in the prescribed amount to form the embryo body;

[0026] The step of preparing the corrugated glaze: pour the corrugated glaze in the formula amount into a ball mill for ball milling, mill for 4-6 hours, filter and remove iron with a 120-150 mesh screen to obtain the corrugated glaze;

[0027] The step of applying corrugated glaze: putting the corrugated glaze into a glaze pourer, using the glaze pourer to cover the corrugated glaze on the surface of the obtained embryo body to obtain a glaze blank;

[0028] Firing steps: Then the glaze body is sent to the kiln for firing, and the position of the air duct opening and the wind force are controlled in the kiln to obtain the water ripple glazed ceramic tile.

[0029] As a further embodiment, in the step of preparing the...

Embodiment 1-3 and comparative example 1

[0038] Weigh the raw materials according to the proportions in Table 1 respectively, and prepare according to the following steps. The difference is that the added raw material proportions are different, and the products are prepared. See Table 1 for details:

[0039] Table 1: Raw material ratio table of the corrugated glaze of embodiment 1-3 and comparative example 1

[0040] Example 1 Example 2 Example 3 Comparative example 1 Potassium feldspar / part 35 40 40 40 albite / part 10 15 20 15 Calcite / part 35 40 45 5 barium carbonate / part 5 8 10 8 burnt talc / part 5 8 10 8 Aluminum powder / part 10 12 15 12 Air Knife Soil / part 5 8 10 8

[0041] The glaze of the comparative example is the glaze commonly used in antique bricks. The biggest difference between the glaze of the comparative example and the corrugated glaze of the present invention is that the amount of calcite is different. Since the addition ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing a non-mold water corrugated glazed ceramic tile, which comprises the steps of preparing an embryo body: ball milling, pressing and firing the embryo body raw material in a formula quantity to form an embryo body; preparing the corrugated glaze Steps: Pour the formula amount of corrugated glaze into a ball mill for ball milling, ball milling for 4-6 hours, use a 120-150 mesh screen to filter and remove iron, and obtain the corrugated glaze; the step of applying corrugated glaze: put the corrugated glaze Put the material into the glaze pourer, use the glaze pourer to cover the corrugated glaze on the surface of the obtained embryo body, and obtain the glaze blank; the firing steps: then send the glaze blank to the kiln for firing, and control the air duct opening in the kiln The location and the wind, that is, water ripple glazed ceramic tiles. The present invention creates corrugated textures on the basis of flat bricks through the regulation of the corrugated glaze, the setting of the air channel opening in the kiln and the adjustment of the wind force, thereby getting rid of the dependence on the embryo body mould.

Description

technical field [0001] The invention relates to a ceramic building material technology, in particular to a method for preparing a non-mold water ripple glazed ceramic tile. Background technique [0002] At present, the traditional ceramic tile surface decoration process is commonly referred to as the printing process, which means that the colors, patterns and patterns of the surface decoration of the brick body are very rich and lifelike. At present, there are three main printing technologies: screen printing, rubber roller printing, and inkjet printing. The surface effects of products presented by different printing technologies are quite different. [0003] The traditional antique brick glaze texture effect is mostly reflected by the ligand mold (screen or rubber roller) effect, but the use of mold will lead to a great increase in production and development costs, and the effect is single and fixed, making it difficult to make new changes. Contents of the invention [0...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/18C04B35/14C04B41/86B28B11/04
CPCB28B11/044B28B11/047C03C8/18C04B35/14C04B41/009C04B41/5022C04B41/86C04B2235/3217C04B2235/349C04B41/4545
Inventor 陆锦荣
Owner 广东永航新材料实业股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com