Colorful purple gold oil drop ware and preparation method thereof

A gold oil and green body technology, which is applied in the field of construction of lamps and its preparation, can solve the problems of unclear formula selection and temperature control, large number of pinholes on the glaze surface, and difficulty in generating oil droplets, etc. The effect of less and higher yield

Active Publication Date: 2018-06-08
邱芙蓉
View PDF5 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In recent decades, experts and artists in the field of ceramics have done a lot of restoration research work and achieved certain results, but the situation that good recipes are hard to find and high-quality goods are rare has not been completely changed. This precious historical and cultural heritage has almost been lost.
[0004] The main types of built-in cups are rabbit hair cups and oil drop cu

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Colorful purple gold oil drop ware and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Colorful purple gold oil drop construction lamp, including green body and glaze; the green body is made of the following components in parts by weight: 35 parts of kaolin, 50 parts of loess, 12 parts of field soil, 2 parts of plant ash and 5 parts of potassium feldspar parts; the glaze consists of the following components in parts by weight: 40 parts of raw ore glaze stone, 10 parts of iron red, 0.5 part of plant ash, 10 parts of limestone, 20 parts of potassium feldspar and 0.5 part of loess.

[0045] The preparation method of the plant ash is as follows: the following weight components are dried in the sun: 12 parts of tea stems, 8 parts of lotus leaves, 4 parts of mugwort leaves and 2 parts of agarwood, and then calcined at high temperature to obtain powdery ash, which is ground to 110 mesh. The tea stalks are selected from Lapsang Souchong tea stalks.

[0046] The preparation method of the above-mentioned colorful purple gold oil drop built lamp includes the followi...

Embodiment 2

[0069] Colorful purple gold oil drop construction lamp, including green body and glaze; the green body is made of the following components according to the ratio of parts by weight: 30 parts of kaolin, 50 parts of loess, 12 parts of field soil, 2 parts of plant ash and 3 parts of potassium feldspar parts; the glaze consists of the following components in parts by weight: 43 parts of raw ore glaze stone, 10 parts of iron red, 0.7 part of plant ash, 12 parts of limestone, 19 parts of potassium feldspar and 1 part of loess.

[0070] The preparation method of the plant ash is as follows: the following weight components are dried in the sun: 15 parts of tea stems, 5 parts of lotus leaves, 6 parts of mugwort leaves and 3 parts of agarwood, and are calcined at high temperature to obtain powdery ash, which is ground to 100 mesh. The tea stalks are selected from Lapsang Souchong tea stalks.

[0071] The preparation method of the above-mentioned colorful purple gold oil drop built lamp ...

Embodiment 3

[0094] Colorful purple gold oil drop construction lamp, including green body and glaze; the green body is made of the following components in parts by weight: 40 parts of kaolin, 55 parts of loess, 10 parts of field soil, 3 parts of plant ash and 4 parts of potassium feldspar parts; the glaze includes the following components in parts by weight: 38 parts of raw ore glaze stone, 8 parts of iron red, 0.8 part of plant ash, 11 parts of limestone, 18 parts of potassium feldspar and 0.7 part of loess.

[0095] The preparation method of the plant ash is as follows: the following weight components are dried in the sun: 10 parts of tea stems, 7 parts of lotus leaves, 5 parts of mugwort leaves, and 4 parts of agarwood, and then calcined at high temperature to obtain powdery ash, which is ground to 120 mesh. The tea stalks are selected from Lapsang Souchong tea stalks.

[0096] The preparation method of the above-mentioned colorful purple gold oil drop built lamp includes the following ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses colorful purple gold oil drop ware and a preparation method thereof. The colorful purple gold oil drop ware comprises a green body and glaze; the green body is prepared from the following components in part by weight: 30-40 parts of kaolin, 50-55 parts of loess, 10-12 parts of field soil, 2-3 parts of plant ash and 3-5 parts of potash feldspar; and the glaze is prepared from the following components in part by weight: 38-43 parts of undressed ore glaze stones, 8-10 parts of iron oxide red, 0.5-0.8 part of plant ash, 10-12 parts of limestone, 18-20 parts of potash feldspar and 0.5-1 part of loess. The colorful purple gold oil drop ware and the preparation method thereof, disclosed by the invention, have the benefits that a reasonable formula is obtained at a scientific ratio; the high-grade purple gold oil drop ware is finally obtained by adopting an innovative firing method; the ware is small in quantity of pinholes on the glaze, thorough in crystallization, strong in crystal three-dimensional sensation and bulky and colorful in oil drop, is based on purple gold and shines with colorful luster, thereby having strong artistic sense of beauty.

Description

technical field [0001] The invention relates to the technical field of porcelain, in particular to Jianzhan and a preparation method thereof. Background technique [0002] Jianzhan is a bright pearl in the history of Chinese ceramics. Jianzhan has a beautiful shape and a changeable glaze like the vastness of the universe. Compared with other porcelains, it has a unique beauty and is still fashionable after thousands of years. [0003] In recent decades, experts and artists in the field of ceramics have done a lot of restoration research and achieved certain results. However, the situation that good recipes are hard to find and high-quality goods are rare has not been completely changed. This precious historical and cultural heritage has almost been lost. [0004] The main types of built-in cups are rabbit hair cups and oil drop cups. The methods for preparing oil drop cups reported so far have the following limitations: first, the choice of formula and temperature control a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B33/04C04B33/13C04B33/34C03C8/02C03C8/14C04B41/86
CPCC03C8/02C03C8/14C04B33/04C04B33/131C04B33/34C04B41/5022C04B41/86C04B2235/3201C04B2235/3472C04B2235/6562C04B2235/6567C04B2235/661
Inventor 邱芙蓉
Owner 邱芙蓉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap