UV (ultraviolet)-curable adhesive composition and application thereof

An ultraviolet light and adhesive technology, applied in the direction of adhesive, adhesive type, polyurea/polyurethane adhesive, etc., can solve the problems of occupying screen assembly space, low efficiency, long pressure holding time, etc.

Active Publication Date: 2018-06-29
上海昀通电子科技有限公司
View PDF2 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But its disadvantages are also obvious, mainly as follows: 1. The operating temperature of the glue is high, which can reach 180°C, and the equipment integration is complicated
2. After the hot melt adhesive is dispensed, it is necessary to maintain the pressure to achieve the bonding strength. This pressure holding time is long, it takes about two minutes, and the efficiency is low
3. Due to the need for heating, the hot melt adhesive can only be dispensed with a needle, and the thickness of the glue is greater than 0.3mm
This thickness is too large (the total thickness of the ultra-narrow bezel is required to be ≤0.8mm), which occupies the screen assembly space
4. The process is complicated, and the opening time of hot melt adhesive is only 2-4 minutes. During this time, glue dispensing, two connectors, one foam, one pressing steel sheet and professional screen pasting equipment must be realized. Perform TP positioning and assembly TP. After completing these steps, press and hold pressure
Although UV glue can avoid the above problems, it is difficult for UV glue to meet the anti-light leakage requirements of edge sealant.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • UV (ultraviolet)-curable adhesive composition and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The first step weighs 55kg aliphatic urethane acrylate, 25kg 2-(ethoxy) ethoxyethyl acrylic acid and 10kg hydroxyethyl acrylate and puts it into a mixing tank for stirring, and the stirring speed is set at 90-120rpm. Stir for 10 minutes; in the second step, weigh 3kg 1-hydroxycyclohexyl phenyl ketone and 1kg 2,4,6-trimethylbenzoyl-diphenylphosphine oxide or put them into the mixing tank for stirring, stirring The speed is set at 100-120rpm, and the stirring time is 20 minutes; the third step, 1kg of color-changing powder (trade name is Tangtai BS-7, Shanghai Tangtai Chemical Co., Ltd.) is dropped into the mixing tank for stirring, and the stirring speed is set at 15- 30rpm, the stirring time is 25 minutes, and finally the mixture can be filtered and packaged.

Embodiment 2

[0029] In the first step, weigh 50kg of aliphatic urethane acrylate, 18kg of tetraethylene glycol diacrylate, 10kg of ethoxylated trimethylolpropane triacrylate and 10kg of hydroxypropyl acrylate and put them into the mixing tank for stirring , the stirring speed is set to 60-120rpm, stirring for about 10 minutes; the second step, 2kg 2-methyl-1-(4-methylthiophenyl)-2-morpholino-1-propanone, 0.5kg Isopropylthioxanthone (2, 4 isomeric mixture), 1kg of isooctyl p-N,N-dimethylaminobenzoate and 1.5kg of methyl o-benzoylbenzoate were weighed and put into the mixing tank for stirring , the stirring speed is set to 100-120rpm, and the stirring time is 20 minutes; the third step, 2kg of color changing powder (trade name is Tangtai BS-7, Shanghai Tangtai Chemical Co., Ltd.) is dropped into the mixing tank for stirring, and the stirring speed is set to 15-30rpm, the stirring time is 25 minutes, and finally the mixture can be filtered and packaged.

Embodiment 3

[0031] In the first step, 52kg of aliphatic urethane acrylate, 10kg of 2-(ethoxy)ethoxyethyl acrylate, 10kg of hydroxyethyl acrylate, 8kg of hydroxypropyl acrylate, 5kg of ethoxylated trimethylolpropane triacrylic acid Esters and 5kg tetraethylene glycol diacrylic acid are weighed and dropped into the mixing tank for stirring, the stirring speed is set at 60-120rpm, and stirred for 10 minutes; in the second step, 2kg2-hydroxyl-methylphenylpropane-1 -ketone, 0.5kg benzophenone and 2kg benzoin dimethyl ether BDK are weighed and dropped into the mixing tank to stir, the stirring speed is set as 100-120rpm, and the stirring time is 20 minutes; The trade mark is Tangtai BS-7 (Shanghai Tangtai Chemicals Co., Ltd.) is put into a mixing tank for stirring, the stirring speed is set at 15-30rpm, and the stirring time is 25 minutes, and finally the mixture is filtered and packaged.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to UV (ultraviolet)-curable adhesive composition and an application thereof. The UV-curable adhesive composition is prepared from the following components in parts by weight: 50-60 parts of a polyurethane acrylate oligomer, 30-40 parts of an acrylate monomer, 3-5 parts of a photoinitiator and 1-5 parts of discoloration powder, wherein the discoloration powder is blackened after being irradiated by UV light and is irreversibly discolored. The UV-curable adhesive composition can be used in assembly of LCD (liquid crystal display) and OLED (organic light emitting diode) display products.

Description

technical field [0001] The invention relates to an ultraviolet light curing adhesive composition and its application. Background technique [0002] With changes in market demand, various display screens, such as mobile phones, PADs, and TVs, require a screen-to-body ratio of more than 85%, and the frame size is getting narrower and narrower. The edges of the existing frame are sealed with vinyl. There are currently two types of vinyl on the market, namely hot melt vinyl and UV vinyl (ultraviolet curing vinyl). [0003] At present, the mainstream of the market chooses hot melt adhesives, because hot melt adhesives have no light transmission requirements when they are cured, and the proportion of carbon black in the formula can be relatively high, so as to achieve high OD values ​​(optical density values). But its disadvantages are also obvious, mainly as follows: 1. The operating temperature of the glue is high, which can reach 180°C, and the equipment integration is compli...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J175/14C09J11/00
CPCC09J11/00C09J175/14
Inventor 朱建国魏辰
Owner 上海昀通电子科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com