A kind of composite powder and its preparation method and application

A technology of composite powder and drug core wire, which is applied in transportation and packaging, metal processing equipment, coating, etc., can solve the problems of increasing the complexity of the preparation process of inorganic-organic composite powder, and achieve low cost, short process flow, The effect of simple ingredients

Active Publication Date: 2020-01-14
NINGBO INST OF MATERIALS TECH & ENG CHINESE ACADEMY OF SCI
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This undoubtedly increases the complexity of the inorganic-organic composite powder preparation process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of composite powder and its preparation method and application
  • A kind of composite powder and its preparation method and application
  • A kind of composite powder and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] In this embodiment, the coat of the drug core wire material is stainless steel, and the drug core is SiO 2 Particles are prepared by arc spraying process, and the composite powder is collected in the atmospheric environment. The specific steps are: adding SiO with a weight ratio of 20% to the stainless steel strip 2 Particles, prepare a drug core wire with a diameter of 1.97mm, and use arc spraying. The specific parameters are: current 120A, voltage 40V, compressed air pressure 0.8MPa, prepare composite powder, and collect the prepared composite powder in the atmosphere;

[0038] Carry out following performance test to the coating of above-mentioned preparation:

[0039] (1) Observation of the cross-sectional microstructure of the composite powder: the microscopic morphology of the particle cross-section was detected by a field emission scanning electron microscope (SEM), and it was confirmed that the particles contained SiO 2 .

[0040] (2) Observation of the surface...

Embodiment 2

[0042] In this embodiment, the coat of the drug core wire material is stainless steel, and the drug core is polytetrafluoroethylene particles and SiO 2 The particles are prepared by arc spraying process, and the atmosphere protects the environment to collect the composite powder. The specific steps are: adding 4% polytetrafluoroethylene particles and 16% SiO in the stainless steel strip 2 Particles, prepare a drug core wire with a diameter of 1.97mm, and use arc spraying. The specific parameters are: current 120A, voltage 40V, nitrogen pressure 0.8MPa, prepare composite powder, and collect the prepared composite powder in an atmosphere protected environment;

[0043] Carry out following performance test to the coating of above-mentioned preparation:

[0044] (1) Observation of the cross-sectional microstructure of the composite powder: the microscopic morphology of the particle cross-section was detected by a field emission scanning electron microscope (SEM), and it was confir...

Embodiment 3

[0047] In this example, the coat of the drug core wire is made of stainless steel, and the drug core is made of polyperfluoroethylene propylene particles and aluminum particles. It is prepared by arc spraying process, and the composite powder is collected in an atmospheric environment. The specific steps are: adding a weight ratio to the stainless steel strip 10% FEP particles and 10% micron aluminum powder were used to prepare a drug core wire material with a diameter of 1.97mm, which was sprayed by electric arc. The specific parameters were: current 120A, voltage 30V, compressed air pressure 1.4MPa, prepared Composite powder, the prepared composite powder is collected in the atmospheric environment;

[0048] Carry out following performance test to the coating of above-mentioned preparation:

[0049] (1) Observation of the cross-sectional microstructure of the composite powder: The microscopic morphology of the particle cross-section was detected by a field emission scanning ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a composite powder. The drug core wire is used as a raw material, and the drug core wire is melted by thermal spraying to form liquid droplets, which are directly sprayed in a vacuum environment or a gas atmosphere to condense to form the composite powder. The invention provides a preparation method of a composite powder, the composition of raw materials is simple, the process is simple and convenient, the prepared composite powder is spherical, has a core-shell structure, and the particle size is 10 μm to 100 μm, and the particle size range can be adjusted by changing the preparation process parameters . The composite powder is suitable for 3D printing technology.

Description

technical field [0001] The invention relates to the field of preparation of composite materials, in particular to a composite powder and its preparation method and application. Background technique [0002] 3D printing, a type of rapid prototyping technology, is based on digital model files and uses bondable materials such as powdered metal or plastic to construct objects by layer-by-layer printing. Its manufacturing is fast, and it can fully reproduce the three-dimensional effect, so that product design and mold production can be carried out simultaneously, and the integration of design and manufacturing can be realized. At present, the materials that can be used on 3D printing equipment include metal materials, inorganic powder materials, ceramic materials, polymer materials and so on. [0003] Due to their excellent mechanical properties and physical and chemical properties, composite materials have always been the focus of scientific research and industrial applications...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F1/00B22F9/06C23C4/131B33Y70/00
CPCB22F9/06B33Y70/00B22F1/065
Inventor 所新坤黄晶房立家刘奕周平龚永锋李华
Owner NINGBO INST OF MATERIALS TECH & ENG CHINESE ACADEMY OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com