Fireproof salix mongolica integrated wood machining method

A technology that integrates wood and processing methods, applied in wood processing equipment, cork machining, wood compression, etc., can solve problems such as limited fire resistance, achieve water saving effects, low preparation costs, and good processability

Inactive Publication Date: 2018-07-13
天津市硫美欣科技发展有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Some data show that the carbonization temperature of phenolic resin glue is as low as about 250°C after heat curing, and it collapses into ash at 400°C. Therefore, the large-scale salix wood building materials made of phenolic resin glue glued and cured have limited fire resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0029] Step 1: Prepare the inorganic sulfur-magnesium cement adhesive, with 10 kilograms per part by weight, each component is prepared according to the following parts by weight, lightly burned magnesium oxide 45, magnesium sulfate heptahydrate 22, sepiolite powder 8, citric acid 0.3, temperature 27 of water at 20-60°C; or, 47 of light-burned magnesium oxide, 26 of magnesium sulfate heptahydrate, 5 of sepiolite powder, 0.5 of citric acid, and 30 of water at a temperature of 20-60°C; or, of light-burned magnesia 50, magnesium sulfate heptahydrate 30, sepiolite powder 10, citric acid 0.7, water at a temperature of 20-60°C 35.

[0030] Put light-burned magnesia, magnesium sulfate heptahydrate, sepiolite powder, citric acid and water at a temperature of 20-60°C in the above weight ratio into a mixer, and stir for 5-8 minutes to obtain an inorganic sulfur-magnesium cement adhesive.

[0031] The fluidity of the inorganic sulfur-magnesium cement adhesive is tested according to exist...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
The average diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a fireproof salix mongolica integrated wood machining method. According to the method, an inorganic sulfur magnesium cement binding agent not containing phenol or formaldehydeis adopted for gluing laminated flat salix mongolica strips. The method comprises the steps that the inorganic sulfur magnesium cement binding agent is prepared, salix mongolica trunk branches are subjected to cutting tidying, glue immersing, cold-press pressing fit, cutting and sanding, and then finished wood is obtained. The salix mongolica integrated wood machined through the method has the prominent beneficial effects that combustion is avoided, corrosion resistance, water resistance and durability are achieved, strength is high, sound isolation and heat preservation are achieved, and machinability is good.

Description

technical field [0001] The invention relates to a method for processing refractory salix integrated wood. Background technique [0002] Salix salix is ​​a shrub plant mainly used for sand fixation. It has the characteristics of cold resistance, drought resistance, high temperature resistance, sand burial resistance, easy planting and fast growth. According to the growth habit of Salix salix, stubble must be carried out every three years, which is conducive to the germination of a large number of branches of Salix salix and promotes its growth to tall and thick, otherwise it will cause Salix salix to decay and even die. [0003] The branches of Salix salix are composed of the branches that have not been lignified and the main branches that have been lignified. The branches are usually used as animal feed, and the main branches are mainly used for industrial fuel and domestic fuel. However, the calorific value of the branches of Salix is ​​only coal About 50% of that, so it i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B27J5/00B27C5/00B27K3/02B27K3/52B27M1/08B27M1/02
CPCB27C5/00B27J5/00B27K3/02B27K3/0214B27K3/52B27K2240/30B27K2240/70B27M1/02B27M1/08
Inventor 张永胜胡爱旗崔锡红
Owner 天津市硫美欣科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com