A kind of medium temperature pearl polishing method

A pearl and medium temperature technology, which is applied in the direction of polishing composition, chemical instruments and methods, grinding/polishing equipment, etc., to improve the polishing effect and work efficiency, ensure the polishing effect, and achieve good polishing effect

Inactive Publication Date: 2020-05-05
浙江梵沛珍珠股份有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the continuous development of society, traditional pearl polishing can no longer meet the needs. Therefore, a medium-temperature pearl polishing method with good polishing effect and high work efficiency is needed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of medium temperature pearl polishing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] a) The pearls are heated by a heating device, the heating temperature is 65 degrees, and the heating time is 25 minutes;

[0020] b) Pour the polishing material into the polishing device, and start the operation of the polishing device, so that the working temperature of the polishing device reaches 65 degrees;

[0021] c) Pour the heated pearls into the polishing device for polishing, and ensure the working temperature of 65 degrees until the polishing is completed;

[0022] The polishing material is formed by drying the polishing carrier particles soaked in the polishing liquid, the soaking temperature is 65 degrees, the soaking time is 1.5 hours, and the polishing carrier particles are walnut shells;

[0023] The mass ratio of each component of the polishing liquid is: paraffin: 4 parts, ethanol: 85 parts, glycerin: 2 parts, stearic acid: 1.5 parts;

[0024] For the preparation of the polishing solution, add paraffin, ethanol, glycerin and stearic acid into the mixi...

Embodiment 2

[0026] a) The pearls are heated by a heating device, the heating temperature is 65 degrees, and the heating time is 25 minutes;

[0027] b) Pour the polishing material into the polishing device, and start the operation of the polishing device, so that the working temperature of the polishing device reaches 65 degrees;

[0028] c) Pour the heated pearls into the polishing device for polishing, and ensure the working temperature of 65 degrees until the polishing is completed;

[0029] The polishing material is formed by drying the polishing carrier particles soaked in the polishing solution, the soaking temperature is 65 degrees, and the soaking time is 1.5 hours. The polishing carrier particles are cork materials composed of cork oak and cork oak husk Made, the mass ratio of described cork oak and cork oak husk is 5:3;

[0030] The mass ratio of each component of the polishing liquid is: paraffin: 4 parts, ethanol: 85 parts, glycerin: 2 parts, stearic acid: 1.5 parts;

[0031...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a medium-temperature pearls polishing method. The medium-temperature pearl polishing method comprises the following steps that a ) pearls are heated by a heating device, wherein the heating temperature is 60-70 DEG C, and the heating time is 20-30 minutes; b ) a polishing material is poured into a polishing device, and the polishing device is started to run, wherein the working temperature of the polishing device is enabled to reach 60-70 DEG C; and C ) the heated pearls are poured into the polishing device for polishing, wherein the working temperature of 60-70 DEG Cis guaranteed until the polishing is finished. Compared with the prior art, the medium-temperature pearls polishing method has the advantages of being good in polishing effect and high in working efficiency.

Description

【Technical field】 [0001] The invention relates to a medium-temperature pearl polishing method, which belongs to the technical field of pearl processing. 【Background technique】 [0002] Pearl is a kind of organic gemstone. From the perspective of polishing principle, pearl is different from other gemstones. The polishing process of other gemstones such as diamonds and jade is a grinding process, which is mechanical action (grinding), chemical action (formation of surface plastic layer or melting layer and molecular layer redistribution) and physical and chemical action (polishing agent , physical and chemical reactions between water and gemstone surface substances) process. Pearl polishing is a process of grinding and filling. On the one hand, the polishing carrier can grind the unevenness of the pearl surface to make the pearl surface smoother; on the other hand, the bright substance (that is, wax) is added to the tiny pores and surface defects on the pearl surface, so tha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More