Method of preparing gold-silver alloy with precious antimony

A gold-silver alloy, rich and noble technology, applied in the field of metal smelting, can solve the problems of cumbersome process, high cost, and affecting the recovery rate of antimony, and achieve the effect of short process flow, low cost and good application value

Active Publication Date: 2018-08-17
广西万仕智稀贵金属科技有限公司
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the high antimony content of this kind of rich antimony, it is easy to affect the recovery rate of antimony. The common method in China is to extract precious metals by chlorination. mine development

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The weight percent of the main chemical components of the treated precious antimony raw material is: Sb72.73%, Pb2.06%, Cu1.34%, Fe12.36%, Au content is 158.00g / t, Ag content is 2321.50g / t, It is processed through the following steps:

[0024] (1) According to the size of the reverberatory furnace, the precious antimony raw materials are added in batches to the reverberatory furnace, and the slag is removed after being filled; 2 , the particle size of the noble antimony raw material is 50-100mm, and the weight added in each batch is 1.5-2.0t;

[0025] (2) adding quartz sand to remove iron, the addition of said quartz sand is 2 to 4 times of the total amount of iron impurities, and the iron content after the removal of impurities is required <0.01%;

[0026] (3) After the iron content test meets the requirements, start blasting and ash blowing. The operation method is to blow air against the inner surface of the reverberatory furnace to generate sparks, oxidize the anti...

Embodiment 2

[0034] The weight percent of the main chemical components of the processed precious antimony raw material is: Sb65.38%, Pb2.60%, Cu1.88%, Fe21.54%, Au content is 356.00g / t, Ag content is 4321.15g / t, It is processed through the following steps:

[0035] (1) According to the reverberatory furnace size, the precious antimony raw material is added in the reverberatory furnace in batches, and the slag is removed after being filled; the reverberatory furnace is a commonly used reverberatory furnace for smelting antimony, and the size is 16m 2 , the particle size of the noble antimony raw material is 50-100mm, and the weight added in each batch is 1.5-2.0t;

[0036] (2) adding quartz sand to remove iron, the addition of said quartz sand is 2 to 4 times of the total amount of iron impurities, and the iron content after the removal of impurities is required <0.01%;

[0037] (3) After the iron content test meets the requirements, start blasting and ash blowing. The operation method is ...

Embodiment 3

[0045] The weight percent of the main chemical components of the treated precious antimony raw material is: Sb67.39%, Pb2.48%, Cu1.27%, Fe20.52%, Au content is 326.58g / t, Ag content is 3988.14g / t, It is processed through the following steps:

[0046] (1) According to the reverberatory furnace size, the precious antimony raw material is added in the reverberatory furnace in batches, and the slag is removed after being filled; the reverberatory furnace is a commonly used reverberatory furnace for smelting antimony, and the size is 16m 2 , the particle size of the noble antimony raw material is 50-100mm, and the weight added in each batch is 1.5-2.0t;

[0047](2) adding quartz sand to remove iron, the addition of said quartz sand is 2 to 4 times of the total amount of iron impurities, and the iron content after the removal of impurities is required <0.01%;

[0048] (3) After the iron content test meets the requirements, start blasting and ash blowing. The operation method is to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a method of preparing gold-silver alloy with precious antimony. The method comprises the following steps of sequentially adding a precious antimony raw material in a reverberatory furnace, a lead smelting furnace and a vacuum furnace, and performing the steps of precious antimony smelting, precious antimony impurity removal, precious antimony cupellating, lead adding, continuous cupellating, copper removal with sulphur addition, coarse lead preparation with condensation and the like to prepare the gold-silver alloy. By directly preparing high-value gold-silver alloy with the precious antimony, the method provided by the invention is short in technological process and relatively low in cost, is efficient and environmentally friendly, saves the energy, is the first invention in the antimony industry, has better application value and is worthy of large-scale popularization and use.

Description

【Technical field】 [0001] The invention belongs to the technical field of metal smelting, and in particular relates to a method for preparing gold-silver alloys from precious antimony. 【Background technique】 [0002] In the antimony industry, with the fluctuation of the antimony market and the consumption of single antimony raw materials, the processing capacity of antimony gold raw materials is gradually increasing. Precious metals such as gold and silver to obtain noble antimony containing antimony, gold, silver and other impurities. At present, reverberatory furnaces are usually used to treat noble antimony to improve the taste of gold and silver and obtain rich antimony. However, due to the high antimony content of this kind of rich antimony, it is easy to affect the recovery rate of antimony. The common method in China is to extract precious metals by chlorination. mine development. 【Content of invention】 [0003] The present invention aims to provide a method for p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22B11/02C22B30/02
CPCC22B11/02C22B30/02
Inventor 姚广生赵俊华周威赵海平
Owner 广西万仕智稀贵金属科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products