Inscription process of coiled reinforced bar alloy roller ring with groove diameter being below phi 6mm

A technology of alloy roll rings and coils, which is applied in the field of lettering technology, can solve the problems of high consumption of alloy roll rings, unfavorable coil rolling, shallow lettering depth, etc., and achieve the goals of saving tool costs, improving production efficiency, and reducing replacement frequency Effect

Inactive Publication Date: 2018-08-28
GUANGDONG GUANGDONG SHAOGANG ENG TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the EDM engraving technology is used for the engraving process of the trademark of a coil alloy roller ring below Ø6mm in a certain factory. The ring consumption is large and the cost is high, which is not conducive to coil rolling

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Inscription process of coiled reinforced bar alloy roller ring with groove diameter being below phi 6mm

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Example 1: The high-line branch of a steel rolling factory uses cutting tool lettering processing and design technology for the trademark of the coil alloy roller ring below φ6mm, which is characterized by easy use, low cost, high precision and high processing efficiency. It can reduce the replacement frequency of alloy roll rings in the production process and improve production efficiency. And reduce the reprocessing frequency of the alloy roll ring, reduce the processing loss of the alloy roll ring, and improve the service life of the alloy roll ring. So that the snail products of φ6mm and below of Shaogang have its own trademark brand, which has high practical and promotional value.

Embodiment 2

[0030] Example 2: The trademark of the high-line branch of a rolling mill with a diameter of less than 6mm is made of a coiled alloy roll ring using cutting tool lettering processing design technology. After actual operation in the roll sample workshop, it proves that the effect is good and the service life of the alloy roll ring is improved. Moreover, through investigation, all the cutting tools of the lettering milling machine in use can be transformed, which has the value of popularization and application.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an inscription process of a coiled reinforced bar alloy roller ring with the groove diameter being below phi 6mm. The inscription process of the coiled reinforced bar alloy roller ring with the groove diameter being below phi 6mm comprises the process steps of firstly using a universal sharpening machine for sharpening the front end of an existing inscription cutter, and obtaining a 15-degree angle; then using a NantongHuixing WXK-500C type numerical control milling machine to control the inscription cutter; and carrying out procedure setting to ensure that inscriptionmeets the requirement. The inscription process of the coiled reinforced bar alloy roller ring with the groove diameter being below phi 6mm has the characteristics of convenience in use, low cost, high accuracy, high processing efficiency and the like. The alloy roller ring replacement frequency during a production process can be reduced, and the production efficiency is improved. The alloy rollerring reworking frequency is reduced, the alloy roller ring processing loss is reduced, and the service life of the alloy roller ring is prolonged. Enterprise coiled reinforced bar products with the groove diameters being 6mm and below phi 6mm can be processed, so that higher practical and promotional value is achieved.

Description

technical field [0001] The invention belongs to the technical field of lettering technology, and relates to a lettering technology for a spiral alloy roll ring with a groove diameter below φ6mm. Background technique [0002] At present, the EDM engraving technology is used for the trademark engraving process of a coil alloy roller ring below Ø6mm in a certain factory. The ring consumes a lot, and the cost is high, which is not conducive to coil rolling. Contents of the invention [0003] In order to overcome the above-mentioned shortcoming of the prior art, the present invention provides a kind of engraving process for the disc spiral alloy roll ring with a groove diameter below φ6mm, which uses a universal grinding machine to grind the front end angle of the existing engraving tool, and then utilizes relevant program process parameters, It can meet the engraving processing of alloy roller rings below the new rebar standard Ø6mm, and has the characteristics of less invest...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B44B3/00B44B3/06B44B3/04B23C3/00B23C3/28
CPCB23C3/00B23C3/28B44B3/005B44B3/009B44B3/04B44B3/063B44B2700/02B44B2700/12
Inventor 李远旺朱春波蒋卫周逾彭丽萍何龙日张昊李明叶培忠余志红邬伟玲
Owner GUANGDONG GUANGDONG SHAOGANG ENG TECH