Rapid tile laying and fixing method

A ceramic tile and fast technology, applied in the direction of construction and building structure, can solve the problem of time-consuming and laborious tile laying, save the physical strength of construction personnel, avoid stirring dust, and improve construction efficiency.

Active Publication Date: 2018-08-28
FOSHAN DONGPENG CERAMIC +2
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] The purpose of the present invention is to propose a method for quickly laying ceramic tiles to solve the problem of time-consuming and laborious tile laying in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rapid tile laying and fixing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0070] A preparation method of a plate-shaped ceramic tile adhesive, comprising the following steps:

[0071] Material preparation: ball mill the plastic solid waste, add water and granulate to make plastic granules, and the moisture content of the plastic granules is 7%;

[0072] Mixing: Mix the plastic granules and the binder evenly to obtain the mixture. The weight ratio of the plastic granules to the binder is 1:2; the plastic granules and the binder are mixed with a dry powder mortar mixer for 30 minutes. The particle size of the plastic particles is 120 mesh.

[0073] Pressing: pressing the mixture into a plate-shaped green body; the pressing pressure is 30MPa.

[0074] Drying: The green body is dried to obtain a tile adhesive in the form of a plate.

[0075] The obtained tile adhesive has a compressive strength ≥ 1.2 MPa. The tile adhesive obtained had a thickness of 1 mm.

[0076] The plastic solid waste includes one or more of kaolin tailings, calcined shale and c...

Embodiment 2

[0080] A preparation method of a plate-shaped ceramic tile adhesive, comprising the following steps:

[0081] Material preparation: ball mill the plastic solid waste, add water and granulate to make plastic granules, the moisture content of the plastic granules is 8%;

[0082] Mixing: Mix the plastic granules and the binder evenly to obtain the mixture. The weight ratio of the plastic granules to the binder is 0.76:2; the plastic granules and the binder are mixed with a dry powder mortar mixer for 40 minutes. The particle size of the plastic particles is 100 mesh.

[0083] Pressing: pressing the mixture into a plate-shaped green body; the pressing pressure is 25MPa.

[0084] Drying: The green body is dried to obtain a tile adhesive in the form of a plate.

[0085] The obtained tile adhesive has a compressive strength ≥ 1.2 MPa. The thickness of the tile adhesive obtained was 2 mm.

[0086] The plastic solid waste includes one or more of kaolin tailings, calcined shale and ...

Embodiment 3

[0090] A preparation method of a plate-shaped ceramic tile adhesive, comprising the following steps:

[0091] Material preparation: ball mill the plastic solid waste, add water and granulate to make plastic granules, and the moisture content of the plastic granules is 10%;

[0092] Mixing: Mix the plastic granules and the binder evenly to obtain the mixture. The weight ratio of the plastic granules to the binder is 0.5:2; the plastic granules and the binder are mixed with a dry powder mortar mixer for 1 hour. The particle size of the plastic particles is 60 mesh.

[0093] Pressing: pressing the mixture into a plate-shaped green body; the pressing pressure is 10MPa.

[0094] Drying: The green body is dried to obtain a tile adhesive in the form of a plate.

[0095] The obtained tile adhesive has a compressive strength ≥ 1.2 MPa. The thickness of the tile adhesive obtained was 3 mm.

[0096] The plastic solid waste includes one or more of kaolin tailings, calcined shale and c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
thicknessaaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses a rapid tile laying and fixing method. The method includes the following steps of firstly, preparing a base surface; secondly, laying a tile adhesive, wherein the platy tile adhesive is placed on the base surface; thirdly, spraying water, wherein water is sprayed to the platy tile adhesive, and the water spraying amount accounts for 25-35% of the weight of the tile adhesive; fourthly, laying tiles, wherein after standing is conducted 1-2 min after water spraying, the tiles are attached to the tile adhesive; fifthly, filling seams. The rapid tile laying and fixing methodis simple and rapid; by means of the platy tile adhesive, the step of conducting stirring before using a powdery tile adhesive in the prior art is omitted, dust stirring and raising are avoided, andtime and labor are saved during tile laying and fixing. Meanwhile, the step of smearing the base surface and the back surfaces of tiles with adhesive slurry in the prior art is also omitted, labor ofconstructors is saved, and construction speed is increased.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a method for quickly laying ceramic tiles. Background technique [0002] Existing ceramic tile adhesives are powdery, and must be mixed with water to form a paste before use. The current methods of laying tiles using powdered tile adhesives are: [0003] 1. First clean the back of the pre-selected tiles, and check the paste base surface; [0004] 2. According to the ratio agreed in advance, first pour the required clear water into the mixing container, and then slowly pour the tile adhesive powder into the mixing container; [0005] 3. Then use an electric mixer to stir until the paste-like mucilage is uniform and free of particles and precipitation. Let it stand for a few minutes and then stir slightly, then it can be used for tiling tiles; [0006] 4. Use a scraper to evenly scrape the glue on the base surface and the back of the tiles for tiling operation. When t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04F21/18C04B28/04
CPCC04B28/04E04F21/1838
Inventor 钟保民徐瑜
Owner FOSHAN DONGPENG CERAMIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com