α-manganese dioxide nanotube, silver nanoparticle loaded α-manganese dioxide nanotube, preparation method and application

A nanoparticle and nanotube technology, applied in the field of air fuel cells, can solve the problem of low catalytic activity

Active Publication Date: 2020-08-21
BEIHANG UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing preparation of α-MnO by hydrothermal method 2 Nano-hollow tubes suffer from low catalytic activity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • α-manganese dioxide nanotube, silver nanoparticle loaded α-manganese dioxide nanotube, preparation method and application
  • α-manganese dioxide nanotube, silver nanoparticle loaded α-manganese dioxide nanotube, preparation method and application
  • α-manganese dioxide nanotube, silver nanoparticle loaded α-manganese dioxide nanotube, preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] The present invention provides a kind of α-MnO 2 A method for preparing nanotubes, comprising the steps of:

[0032] (1) Potassium permanganate is mixed with water to obtain potassium permanganate solution;

[0033] (2) carry out reduction reaction after hydrochloric acid is added dropwise in the potassium permanganate solution that described step (1) obtains, obtain α-MnO 2 For nanotubes, the molar ratio of potassium permanganate to hydrochloric acid is 1:1-10.

[0034] The invention mixes potassium permanganate with water to obtain a potassium permanganate solution. The present invention has no special limitation on the concentration of the potassium permanganate solution, and any concentration of potassium permanganate solution can be used. In the present invention, the volume ratio of the mass of potassium permanganate to water is preferably 1.517g:80mL. The present invention has no special limitation on the mixing method, and a mixing method well known to those...

Embodiment 1

[0064] 1.517gKMnO 4 Dissolve in 80mL deionized water, stir evenly, weigh 3.0g 37% HCl and add dropwise to KMnO 4 solution, stirred for 30min.

[0065] Transfer the above solution to a 150mL reactor and carry out the oxidation reaction at 130°C for 10h. After the reaction, let the reactor cool down to room temperature naturally, centrifuge, wash the precipitate with deionized water and ethanol three times each, and dry the precipitate in vacuum at 100°C. 24h, get α-MnO 2 nanotube.

[0066] For the α-MnO prepared in this example 2 The nanotubes were characterized by XRD, and the results were as follows: figure 1 shown by figure 1 It can be seen that the α-MnO prepared in this example 2 Nanotube XRD diffraction patterns and a-MnO 2 (JCPDS No.44-0141, tetragonal, I4 / m, ), it is determined that the synthesized sample is a-MnO 2 square phase.

[0067] For the α-MnO prepared in this example 2 The nanotubes were characterized by SEM and TEM, and the results are as follows ...

Embodiment 2

[0070] The preparation method is the same as that of Example 1, except that the amount of hydrochloric acid added is 2g, 5g and 7g respectively.

[0071] For the α-MnO that embodiment 1 and 2 make 2 The specific surface area of ​​nanotubes was tested, and the results are shown in Table 1. It can be seen from Table 1 that the addition of hydrochloric acid can adjust the α-MnO 2 The specific surface area of ​​nanotubes, when the added amount is 3g, the BET specific surface area reaches the maximum of 52.9030m 2 / g.

[0072] Table 1 Preparation of α-MnO with different additions of hydrochloric acid 2 BET specific surface area of ​​nanotubes

[0073]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method for an alpha-MnO2 nanotube, and belongs to the technical field of air fuel cells. The addition amount of hydrochloric acid is changed to regulate the specific surface area of the alpha-MnO2 nanotube, the alpha-MnO2 nanotube with a large specific surface area is prepared, a contact area between an active locus and electrolyte is increased through the large specific surface area, in addition, a hollow structure is favorable for the diffusion migration of ions, and the ORR (Oxygen Reduction Reaction) catalytic performance of the alpha-MnO2 nanotube is improved. The data of an embodiment indicates that the specific surface area of the alpha-MnO2 nanotube is as high as 52.9030m<2> / g, and the ORR activity can be on a par with that of 20%wt Pt / C (commercial electrode).

Description

technical field [0001] The invention relates to the technical field of air fuel cells, in particular to an α-manganese dioxide nanotube, a silver nanoparticle-loaded α-manganese dioxide nanotube, a preparation method and an application. Background technique [0002] In the electrochemical reaction of aluminum-air batteries, when there is no oxygen reduction catalyst, the reduction of oxygen at the cathode is very slow, resulting in a very large overvoltage. In order to reduce the electrochemical polarization of the cathode reaction process, it is necessary to use high-efficiency Catalysts that promote oxygen reduction, so it is necessary to find cheap and efficient air electrode catalysts. [0003] For Mn-based oxygen reduction catalysts, the crystal type, surface area, and surface element valence state distribution are the main factors affecting the catalytic performance. The existing preparation of α-MnO by hydrothermal method 2 Nano hollow tubes have the problem of low ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01G45/02B82Y30/00B82Y40/00H01M4/90H01M12/06
CPCB82Y30/00B82Y40/00C01G45/02C01P2004/13C01P2006/12H01M4/9016H01M12/06
Inventor 卢惠民许彬彬蔡伟邓燕曹媛杨文文
Owner BEIHANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com