Porcelain repairing component with good repairing effect

A porcelain and adhesive technology, applied in the field of porcelain, can solve the problems of poor bonding effect and lack of glue system for porcelain repair, etc., and achieve the effect of low cost, simple composition and good repair effect

Inactive Publication Date: 2018-10-12
温书强
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Existing porcelain used for display is often directly bonded with glue after damage, and the bonding effect is not good, and there is also a lack of glue system for porcelain repair on the market, so how to provide a method that can simultaneously target seams The repair agent system for repairing gaps and gaps, and the porcelain repair components that are cost-effective and firmly bonded are particularly important

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] Embodiment 1: A porcelain repairing component with good repairing effect, including a joint adhesive and a gap adhesive, the joint adhesive is composed of the following raw materials: including 15 parts of blue brick powder, dry slaked lime 4 parts, garlic component 15 parts, peanut oil 3 parts;

[0012] The garlic component includes 10 parts of garlic, 40 parts of water, 8 parts of egg white, and 1 part of turpentine;

[0013] The adhesive for the gap is composed of the following raw materials: 40 parts of porcelain powder, 35 parts of epoxy resin system; 10 parts of gypsum powder, 1 part of magnesium oxychloride cement, and 5 parts of silicon dioxide;

[0014] Epoxy resin in the epoxy resin glue component: curing agent=100:25;

[0015] The epoxy resin glue is selected from one of glycidyl ether epoxy resin, glycidyl ester epoxy resin, glycidyl amine epoxy resin or linear aliphatic epoxy resin, and the curing agent is selected from polyamide, One of phenalkamines, al...

Embodiment 2

[0023] Embodiment 2: A porcelain repairing component with a good repairing effect, including a joint adhesive and a gap adhesive, the joint adhesive is composed of the following raw materials: 22 parts of blue brick and tile powder, dry slaked lime 8 parts, 20 parts of garlic component, 5 parts of peanut oil;

[0024] The garlic component includes 15 parts of garlic, 65 parts of water, 13 parts of egg white, and 2 parts of turpentine;

[0025] The adhesive for the gap is composed of the following raw materials: 50 parts of porcelain powder, 40 parts of epoxy resin system; 30 parts of gypsum powder, 1.5 parts of magnesium oxychloride cement, and 15 parts of silicon dioxide;

[0026] Epoxy resin in the epoxy resin glue component: curing agent=100:70;

[0027] The epoxy resin glue is selected from one of glycidyl ether epoxy resin, glycidyl ester epoxy resin, glycidyl amine epoxy resin or linear aliphatic epoxy resin, and the curing agent is selected from polyamide, One of phen...

Embodiment 3

[0035] Embodiment 3: A porcelain repairing component with a good repairing effect, including a joint adhesive and a gap adhesive, the joint adhesive is composed of the following raw materials: including 18 parts of green brick powder, dry slaked lime 7 parts, garlic component 17 parts, peanut oil 4 parts;

[0036] The garlic component includes 12 parts of garlic, 55 parts of water, 12 parts of egg white, and 1.5 parts of turpentine;

[0037] The adhesive for the gap is composed of the following raw materials: 45 parts of porcelain powder, 38 parts of epoxy resin system; 20 parts of gypsum powder, 1.3 parts of magnesium oxychloride cement, and 10 parts of silicon dioxide;

[0038] Epoxy resin in the epoxy resin glue component: curing agent=100:50;

[0039] The epoxy resin glue is selected from one of glycidyl ether epoxy resin, glycidyl ester epoxy resin, glycidyl amine epoxy resin or linear aliphatic epoxy resin, and the curing agent is selected from polyamide, One of phenal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of porcelain,and particularly relates to a porcelain repairing component with the good repairing effect. The component comprises a joint adhesive and an adhesive fora gap. The joint adhesive is prepared from 15-22 parts of black brick tile powder,4-8 parts of dry slaked lime,15-20 parts of garlic components and 3-5 parts of peanut oil; the garlic components include 10-15 parts of garlic,40-65 parts of clean water,8-13 parts of egg white and 1-2 parts of turpentine oil; the adhesive for the gap includes 40-50 parts of porcelain cement,35-40 parts of epoxy resin system,10-30 parts of gypsum powder,1-1.5 parts of magnesium oxychloride cement and 5-15 parts of silicon dioxide; the ratio of epoxy resin and curing agent in the epoxy resin components is 100:(25-70),the direct adhesive repairing cost of a repairing agent system for porcelain is low,the repairing effect is good,the using requirement for the strength of common porcelain can be met,and the porcelain with a large gap can be repaired.

Description

technical field [0001] The invention belongs to the field of porcelain, and in particular relates to a porcelain repairing component with good repairing effect. Background technique [0002] Existing porcelain used for display is often directly bonded with glue after damage, and the bonding effect is not good, and there is also a lack of glue system for porcelain repair on the market. The repairing agent system for repairing the gap and the porcelain repairing components that are firmly bonded while taking into account the cost are all the more important. Contents of the invention [0003] Based on the defects of the prior art, the object of the present invention is to provide a porcelain repair component with good repair effect. [0004] In order to achieve the above object, the present invention adopts the following technical solutions: a ceramic repairing component with good repairing effect, including a seam adhesive and a gap adhesive, and the seam adhesive is compos...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/32C04B28/10C04B111/72
CPCC04B28/32C04B28/10C04B2111/00637C04B2111/72C04B14/365C04B14/06C04B14/00C04B24/281C04B24/085C04B24/34C04B24/14C04B16/00
Inventor 温书强
Owner 温书强