A ceramsite filter material and water treatment technology, applied in water/sewage treatment, adsorption water/sewage treatment, light water/sewage treatment, etc., can solve the problems of inhibiting biofilm growth and purification ability

Inactive Publication Date: 2018-10-16
SHENYANG LIGONG UNIV
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when the pollution contains toxic and harmful substance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A method for preparing a multifunctional water treatment ceramsite filter material, comprising the following process steps:

[0023] Step 1: Reaming of ceramsite

[0024] 1.1 Add 300mL of 0.5mol / L hydrochloric acid solution into a 500mL round bottom flask, then add 30g of ceramsite, install a condenser tube on the flask, and pass in tap water to cool;

[0025] 1.2 Put the flask in a constant temperature water bath, the temperature of the water bath is 85°C, keep it warm for 3 hours, filter the above mixture, rinse it repeatedly with deionized water, and obtain the expanded ceramsite;

[0026] 1.3 Place the expanded ceramsite in an electric blast drying oven, dry at 200°C for 30 hours, and set aside;

[0027] Step 2: Preparation of titanium alkoxide-ceramsite mixture

[0028] 1.1 Take a 500mL beaker, add 220mL ethanol, 23mL n-propanol, 20mL n-butyl titanate and 5mL glycerin in sequence, and stir well;

[0029] 1.2 Put the dry expanded ceramsite into the solution and s...

Embodiment 2

[0037] A method for preparing a multifunctional water treatment ceramsite filter material, comprising the following process steps:

[0038] Step 1: Reaming of ceramsite

[0039] 1.1 Add 300mL of 0.5mol / L hydrochloric acid solution into a 500mL round bottom flask, then add 30g of ceramsite, install a condenser tube on the flask, and pass in tap water to cool;

[0040] 1.2 Put the flask in a constant temperature water bath, the temperature of the water bath is 85°C, keep it warm for 3 hours, filter the above mixture, rinse it repeatedly with deionized water, and obtain the expanded ceramsite;

[0041] 1.3 Place the expanded ceramsite in an electric blast drying oven, dry at 200°C for 30 hours, and set aside;

[0042] Step 2: Preparation of titanium alkoxide-ceramsite mixture

[0043] 1.1 Take a 500mL beaker, add 230mL ethanol, 25mL n-propanol, 21mL n-butyl titanate and 6mL glycerin in sequence, and stir evenly;

[0044] 1.2 Put the dry expanded ceramsite into the solution and...

Embodiment 3

[0052] A method for preparing a multifunctional water treatment ceramsite filter material, comprising the following process steps:

[0053] Step 1: Reaming of ceramsite

[0054] 1.1 Add 300mL of 0.5mol / L hydrochloric acid solution into a 500mL round bottom flask, then add 30g of ceramsite, install a condenser tube on the flask, and pass in tap water to cool;

[0055] 1.2 Put the flask in a constant temperature water bath, the temperature of the water bath is 85°C, keep it warm for 3 hours, filter the above mixture, rinse it repeatedly with deionized water, and obtain the expanded ceramsite;

[0056] 1.3 Place the expanded ceramsite in an electric blast drying oven, dry at 200°C for 30 hours, and set aside;

[0057] Step 2: Preparation of titanium alkoxide-ceramsite mixture

[0058] 1.1 Take a 500mL beaker, add 250mL of ethanol, 27mL of n-propanol, 23mL of n-butyl titanate and 7mL of glycerin in sequence, and stir well;

[0059] 1.2 Put the dry expanded ceramsite into the so...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Bulk densityaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a multifunctional water treatment ceramisite filter material, and belongs to the field of environmental purification functional materials. The preparation method comprises the following technological steps: putting ceramisite into a hydrochloric acid solution with the concentration of 0.5 mol/L, carrying out constant temperature treatment on the solution and reaming ceramisites; preparing a titanium alkoxide and ceramisite mixture from ethanol, n-propanol, tetrabutyl titanate, glycerol and the ceramsites; adding a copper chloride aqueous solutionwith the solution of 0.3 mol/L into the titanium alkoxide and ceramisite mixture, stirring and filtering to obtain biofilm culturing ceramisites; drying the biofilm culturing ceramisites at 80 DEG Cfor 24 hours, calcining at the calcining temperature of 620 to 870 DEG C for 3 hours and naturally cooling to obtain the multifunctional water treatment ceramisite filter material. The filter materialcan utilize adsorption and biodegradation to purify sewage and also has self-cleaning ability under illumination, so that the multifunctional water treatment ceramisite filter material is suitable for water pollution treatment process with various forms.

Description

technical field [0001] The invention belongs to the field of environmental purification functional materials, and in particular relates to a preparation method of multifunctional water treatment ceramsite filter material. Background technique [0002] Ceramsite is a lightweight aggregate produced by foaming in a rotary kiln. It has a spherical shape, a smooth and hard surface, and a honeycomb-like interior. The density of ceramsite is small, the thermal conductivity is low, and the strength is high. The bulk density of ceramsite itself is generally 300-900kg / m 3 . The appearance of ceramsite is hard, and the interior is rich in micropores, which makes ceramsite light in weight. Because of these excellent properties, ceramsite has been widely used in environmental protection, building materials, gardening, food and beverage, refractory insulation materials, chemical industry, petroleum and other fields. Bio-ceramic filter material can be used as bio-film carrier of bio-fil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01D39/06C02F1/28C02F1/30C04B38/00
CPCB01D39/06C02F1/281C02F1/30C04B38/009
Inventor 张文杰董英昊张悦韩铭李昊伦
Owner SHENYANG LIGONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap