The method of singeing and degraining the sackcloth after ario finishing
A linen and finishing machine technology, applied in the directions of singeing, fiber processing, textile material processing, etc., can solve the problems that the head of the linen cannot be completely removed, affect the processing effect of the linen, reduce the structural performance of the linen, etc., so as to improve the protection effect, Good degranulation effect, improve the effect of degranulation effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0025] Example 1. A method for singeing and degraining the linen ARIO after finishing, comprising the following steps:
[0026] ① Pad the desized linen cloth in warm water at 40-45°C to moisten the cloth surface and make the cloth body soft, and obtain A cloth; since the linen cloth does not have water absorption after the desizing process, add 1 ~3g / L penetrating agent, so that the warm water can completely wet the cloth surface after padding. The penetrating agent can choose non-ionic penetrating agent JFC to ensure the penetrating effect of warm water and avoid the impact of penetrating agent on the subsequent process of linen;
[0027] ② Put the cloth A into the ARIO finishing machine. Under the environment of 65-75℃, the cloth A circulates in the air duct of the ARIO finishing machine, and the ARIO finishing machine beats the cloth A mechanically through the grid during the circular rotation. The rotation speed of cloth A is 1800-2200 rpm when it circulates in the air du...
Embodiment 2
[0039] Example 2. A method for singeing and degraining the linen ARIO after finishing, comprising the following steps:
[0040] ① Pad the desized linen cloth in warm water at 40°C, which contains 1g / L penetrant, so that the surface of the cloth is moistened and the cloth body is soft, and A cloth is obtained;
[0041] ② Put the cloth A into the AIRO finishing machine, and the cloth A circulates in the air duct of the ARIO finishing machine under the environment of 65°C, and the ARIO finishing machine beats the cloth A mechanically through the grid to make the cloth body The grains on the surface float up, the rotation speed of cloth A is 1800 rpm when it circulates in the air duct, and the beating time is 20 minutes, and cloth B is obtained;
[0042] ③ Put cloth B into the singeing machine, brush the surface of cloth B through the brush roller on the singeing machine, and remove larger grains with a diameter of 1-3mm on cloth B, and obtain cloth C;
[0043]④ Use the singeing...
Embodiment 3
[0045] Example 3. A method for singeing and degraining the linen ARIO after finishing, comprising the following steps:
[0046] ① Pad the desized linen cloth in 45°C warm water containing 3g / L penetrant to moisten the cloth surface and make the cloth soft, and obtain A cloth;
[0047] ② Put the cloth A into the AIRO finishing machine, and the cloth A circulates in the air duct of the ARIO finishing machine under the environment of 75°C, and the ARIO finishing machine beats the cloth A mechanically through the grid during the circular rotation, so that the cloth body The grains on the surface float up, the rotation speed of cloth A is 2200 rpm when it circulates in the air duct, and the beating time is 30 minutes, and cloth B is obtained;
[0048] ③ Put cloth B into the singeing machine, brush the surface of cloth B through the brush roller on the singeing machine, and remove larger grains with a diameter of 1-3mm on cloth B, and obtain cloth C;
[0049] ④ Use the singeing fl...