A kind of hierarchical pore structure zeolite adsorption/catalyst and its construction method
A technology of multi-level pores and catalysts, which is applied in the field of structuring of porous materials, can solve problems such as low use efficiency, nanopore blockage, and small relative volume, and achieve the effects of improving use efficiency, increasing zeolite volume fraction, and increasing reaction rate
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0018] Embodiment 1: the preparation of the zeolite adsorption / catalysis material of hierarchical porous structure in the present embodiment is realized according to the following steps: 1) take kaolin, bauxite as main raw material, MoO 3 As a sintering aid, according to (3Al 2 o 3 2SiO2 2 ) 0.9 (MoO 3 ) 0.1 Stoichiometric weighing, mixing, and using absolute ethanol as the medium, the volume ratio of powder and absolute ethanol is 1:2, ball milling for 20 hours; then drying and sieving to obtain a uniform mixed powder; 2) deionized Water, polyvinyl alcohol with 1% powder mass and mixed powder were ball milled for 24 hours to prepare a stable water-based ceramic slurry with a solid phase content of 10 vol%; 3) The stable slurry was dropped into -5°C through a vibrating dripping device In a small amount of corn oil, the amount of corn oil is about 500ml. By adjusting the vibration frequency and the pore size of the pillow, droplets of ceramic slurry with a particle size di...
Embodiment 2
[0021] Example 2: The difference between this embodiment and Example 1 is that the solid content of the water-based ceramic slurry in step 2) is 20vol% and 30vol% respectively, and other steps and parameters are the same as in Example 1.
Embodiment 3
[0022]Example 3: The difference between this embodiment and Example 1 is that the temperatures of the low-temperature oil phase in step 3) are respectively -15°C and -25°C, and other steps and parameters are the same as in Example 1.
PUM
Property | Measurement | Unit |
---|---|---|
pore size | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap