60kg/m R260 hot-rolled rail moving flash welding method

A technology for rails and welding process, applied in welding equipment, resistance welding equipment, metal processing equipment, etc., can solve the problems of large total width of heat-affected zone, affecting the mechanical properties of rails, uneven total width of heat-affected zone, etc.

Active Publication Date: 2020-10-30
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, both at home and abroad, the rail waist clamping method is used for rail clamping and conduction, and the pulse flash welding process is used for welding. The total width of the heat-affected zone of the welded 60kg / m R260 hot-rolled rail joint is not uniform, and the joint rail waist The phenomenon of "bulging belly" often occurs at the place, the total width of the heat-affected zone is too large, and the difference between the maximum and minimum width of the heat-affected zone is large, which seriously affects the mechanical properties of the rail

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 60kg/m R260 hot-rolled rail moving flash welding method
  • 60kg/m R260 hot-rolled rail moving flash welding method
  • 60kg/m R260 hot-rolled rail moving flash welding method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] When the 60kg / m R260 hot-rolled rail is welded by a mobile rail flash welding machine, the welding heat input of the first stage flash flat is 1.9MJ, the burning displacement is 0.7mm, and the duration is 19.9s. The welding heat input of the second stage flash is 1.1MJ, the displacement is 10.3mm, and the duration is 52.3s. The welding heat input of the third stage of accelerated burning is 0.6MJ, the displacement is 13.4mm, and the duration is 32.9s. The welding heat input of the fourth stage upsetting is 0.2MJ, the displacement is 15.6mm, the live upsetting time is 0.6s, and the duration is 3.7s. The holding pressure of the fifth stage is 30.3t, and the duration is 12.9s. In the welding process, the total heat input is 3.8MJ, the displacement is 40.0mm, and the total welding duration is controlled to 121.7s, so as to achieve the purpose of controlling the width of the heat-affected zone of the joint and the quality of the joint. The specific data are listed in Table...

Embodiment 2

[0026] When the 60kg / m R260 hot-rolled rail is welded by a mobile rail flash welding machine, the welding heat input of the first stage flash flat is 1.9MJ, the burning displacement is 1.0mm, and the duration is 19.8s. The welding heat input of the second stage flash is 1.1MJ, the displacement is 10.4mm, and the duration is 53.6s. The welding heat input of the third stage of accelerated burning is 0.6MJ, the displacement is 13.5mm, and the duration is 32.8s. The welding heat input of the fourth stage upsetting is 0.2MJ, the displacement is 15.7mm, the live upsetting time is 0.9s, and the duration is 2.3s. The holding pressure of the fifth stage is 30.4t, and the duration is 12.9s. In the welding process, the total heat input is 3.8MJ, the displacement is 40.6mm, and the total welding duration is controlled to 121.4s, so as to achieve the purpose of controlling the width of the heat-affected zone of the joint and the quality of the joint. The specific data are listed in Table...

Embodiment 3

[0031] When the 60kg / m R260 hot-rolled rail is welded by a mobile rail flash welding machine, the welding heat input of the first stage flash flat is 1.9MJ, the burning displacement is 0.7mm, and the duration is 19.9s. The welding heat input of the second stage flash is 1.5MJ, the displacement is 10.0mm, and the duration is 59.6s. The welding heat input of the third stage of accelerated burning is 0.6MJ, the displacement is 13.2mm, and the duration is 32.5s. The welding heat input of the fourth stage upsetting is 0.2MJ, the displacement is 15.8mm, the live upsetting time is 1.0s, and the duration is 2.3s. The holding pressure of the fifth stage is 29.5t, and the duration is 12.9s. In the welding process, the total heat input is 4.2MJ, the displacement is 39.7mm, and the total welding duration is controlled to 127.2s, so as to achieve the purpose of controlling the width of the heat-affected zone of the joint and the quality of the joint. The specific data are listed in Table...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Abstract The invention discloses a mobile flash-butt welding method for 60kg / m R260 hot-rolled rail, comprising a pre-flash stage, a flash stage, an boost stage, an upset stage and a forge stage; the total welding heat input is 3.0-4.8MJ, the total welding duration is 110-135s, and the welding upset allowance is 12.4-16.7 mm. The invention can improve the rail welding quality by controlling the total welding heat input, the total welding duration and the upset allowance in the mobile flash-butt welding process, as well as controlling the welding heat input and duration of each stage. According to the invention, the 60kg / m R260 hot-rolled rail can be successfully subjected to mobile flash-butt welding. As a result, the total width of the heat affected zone of the mobile flash-butt welding joint of whole 60kg / m R260 hot-rolled rail can be controlled within 32mm, and the difference between the maximum and the minimum value thereof is not more than 8.2mm, so as to reduce internal defects of the rail joint and ensure stable welding quality. Fig. 1 Fig. 2

Description

technical field [0001] The invention relates to the technical field of rail welding, in particular to a method for moving flash welding of 60kg / m R260 hot-rolled rails. Background technique [0002] The rail flash welding joint is composed of the welding zone and the adjacent rail base metal, and the welding zone is divided into the weld seam and the welding heat-affected zone (HAZ). According to the distance between each point on the base metal of the rail and the weld seam, the heat-affected zone can be roughly divided into three areas: coarse grained area, fine grained area and incomplete recrystallized area. The coarse-grained zone is also called the superheated zone, and the temperature in this zone is generally around 1200°C, which is close to the semi-melted zone. When the rail temperature exceeds 1100°C, the grains will be severely coarsened, and the longer the residence time, the wider the heating zone and the more serious the grains will be coarsened. It is easy ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K11/04
CPCB23K11/04
Inventor 陆鑫李大东王若愚邓健
Owner PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP