Manufacturing method and moulding method for three-dimensional additive moulding material

A technology of additive molding and manufacturing method, applied in the direction of additive processing, etc., can solve the problems of restricting the development of the field of additive molding artwork manufacturing, curing difficulties, etc.

Active Publication Date: 2018-12-04
赵晴堂
View PDF14 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the curing of ceramic materials after molding is very difficult and requires professional equipment for sintering. This shortcoming limits the development of the field of additive molding art manufacturing.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method and moulding method for three-dimensional additive moulding material
  • Manufacturing method and moulding method for three-dimensional additive moulding material
  • Manufacturing method and moulding method for three-dimensional additive moulding material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] In order to make the technical means, creative features, goals and effects achieved by the present invention easy to understand, the present invention will be further described below in conjunction with specific illustrations.

[0026] The material manufacturing method involved in the present invention is,

[0027] Such as figure 1 Method 1 shown: First mix the resin and additives in a certain ratio (the specific mixing ratio should be increased or decreased according to different molding temperatures by 3-30% for resin, 0-2.5% for urotropine), and then mixed with solvent to dissolve. Prepared as a phenolic resin solution. Pour the solution into ceramic powder and stir and mix in a closed container to form ceramic mud. The mixing ratio of the solution and the ceramic powder shall be proportioned according to the site requirements. The above mixing steps are required to be carried out at normal temperature.

[0028] Such as figure 2 Method 2 shown: Mix resin powde...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a formula, a manufacturing method, and a moulding process for a ceramic material. A thermosetting effect of phenolic resin is introduced into the field of 3D ceramic printing, so that the moulding difficulty and requirements for sintering are greatly reduced.

Description

technical field [0001] The invention relates to a formula, a manufacturing method and a molding process of an additive molding material. Specifically, it is a formula, a manufacturing method and a molding process of a kind of ceramic material. Background technique [0002] In recent years, with the advancement of science, "additive molding technology" has developed rapidly and vigorously, including ceramic materials. However, the curing of ceramic materials after molding is very difficult and requires professional equipment for sintering. This shortcoming limits the development of the field of additive molding art manufacturing. Contents of the invention [0003] The invention provides a formula, a manufacturing method and a molding process of a kind of ceramic material, which introduces the thermosetting effect of phenolic resin into the field of 3D ceramic printing, so that the difficulty of molding and the requirement of sintering are greatly reduced. [0004] The mat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/626C04B35/634C04B35/01C04B35/56C04B35/58
CPCB33Y70/00C04B35/01C04B35/56C04B35/58C04B35/62635C04B35/63476C04B2235/48
Inventor 赵晴堂
Owner 赵晴堂