Imitation wood grain production process and fire-proof plate applying plate produced by process
A production process, imitation wood grain technology, applied in the direction of layered products, metal layered products, hydraulic material layered products, etc., can solve the problems of low efficiency, excessive waste acid, unenvironmental protection, etc. Clear texture and simple structure
Inactive Publication Date: 2019-01-01
龙督实业集团有限公司
View PDF4 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, in the prior art, the wood grain printed on the aluminum profile is first soaked and corroded by a strong acid such as sulfuric acid to form lines on the surface of the aluminum profile. After the lines are formed, the aluminum profile needs to be cleaned. After cleaning, the bottom color and the printed wood grain are sprayed. The efficiency of forming grains during the corrosion process of making imitation wood grains on this kind of aluminum profiles is low, and at the same time, more waste acid will be generated during the cleaning process, which is not environmentally friendly
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0019] refer to figure 1 , a fireproof board, comprising a first surface layer 1, a second surface layer 2, a fireproof layer 3 fixedly arranged between the first surface layer 1 and the second surface layer 2, the first surface layer 1 is imitation wood textured sheet. The material of the second surface layer 2 is aluminum plate. The material of the first surface layer substrate 1 is aluminum plate. The fireproof layer 3 material is cement.
[0020] A kind of imitation wood grain production process, comprises the following steps,
[0021] S1. Carry out pressing lines on the plate;
[0022] S2. Rolling and trimming the back of the plate;
[0023] S3. Paint the base color on the front of the board of S2;
[0024] S4. Print wood grain above the background color on the S3 plate to make imitation wood grain plate.
[0025] In S2, multiple correction wheels are used to trim the back of the sheet. In S1, the front side of the board is rolled to carry out the embossed texture...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention discloses an imitation wood grain production process and a fire-proof plate applying a plate produced by the process. The imitation wood grain production process comprises the steps of grain rolling on the plate, flattening, ground color painting, and wood grain printing. The plate is applied to manufacturing of the fire-proof plate. Grain rolling and flattening treatment of the backsurface are carried out, and then ground color painting and wood grain printing are carried out; in the imitation wood grain manufacturing mode, corrosion treatment with strong acid is avoided, thus,more environmental protection is achieved; and through rolling, the grain forming efficiency is higher. The imitation wood grain plate is applied to the fire-proof plate, the structure is simple, andgrain is clear.
Description
technical field [0001] The invention relates to a production process of imitating wood grain and a fireproof board thereof. Background technique [0002] Aluminum profiles are widely used in decorative building materials due to their structural rigidity and light weight. With people's increasing pursuit of home environment quality, aluminum profiles of a single color cannot satisfy the diversification of decoration. In order to coat the surface of the aluminum profile with a layer of wood grain effect, this method meets the diverse needs of users for the home environment. However, in the prior art, the wood grain printed on the aluminum profile is first soaked and corroded by a strong acid such as sulfuric acid to form lines on the surface of the aluminum profile. After the lines are formed, the aluminum profile needs to be cleaned. After cleaning, the bottom color and the printed wood grain are sprayed. The efficiency of forming grains in the corrosion process of making im...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): B32B13/06B32B15/20B32B33/00B21D21/00B41M1/28
CPCB21D21/00B32B13/06B32B15/20B32B33/00B32B2307/3065B41M1/28B41M5/0011
Inventor 陈勇平郭永叶井养
Owner 龙督实业集团有限公司