High temperature resistant zinc-based coated steel sheet and its manufacturing method, hot forming method and parts
A coated steel plate, high temperature resistance technology, applied in forming tools, manufacturing tools, coatings, etc., can solve the problems of liquid phase erosion and easy evaporation of pure zinc coating
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0022] The coating is a hot-pressed steel sheet of zinc-aluminum-magnesium alloy. The composition of the coating is: 2% Mg, 3% Al, and the rest is Zn. The steel plate is 22MnB5. The vitrification process is used for online processing, and the vitrification solution is rolled onto the coating. The surface of the steel plate is then dried. The drying temperature is 85 ° C, the thickness of the ceramic film is 100 nm, mainly composed of ZrO 2 , ZrOF 2 、Zr 2 OF 2 , MgO, Al 2 o 3 , ZnO, SiO 2 Composition, especially nano zirconia, alumina, magnesia. The hot-dip coating contains Si, Ti, F, Na and other elements; the main components of the vitrification solution are: fluorozirconium salt, hydrogen peroxide, fluorotitanic acid, zirconium fluoride, tartaric acid, sodium nitrate, tannic acid, KH550.
[0023] In the hot stamping process, in an atmosphere containing oxygen, the heating rate is controlled at 10°C / s in the temperature range below 650°C, and the heat preservation is c...
Embodiment 2
[0026] The coating is a hot-pressed steel sheet of zinc-aluminum-magnesium alloy. The composition of the coating is: 1.5% Mg, 2% Al, and the rest is Zn. The steel plate is 22MnB5. The off-line treatment is carried out by vitrification process, and the coating steel plate is immersed in vitrification solution , take it out and dry it. The drying temperature is 130 ° C, the thickness of the ceramic film is 1000 nm, mainly composed of ZrO 2 , ZrOF 2 、Zr 2 OF 2 , MgO, Al 2 o 3 , ZnO, SiO 2 Composition, especially nano zirconia, alumina, magnesia. The hot-dip coating contains Si, Ti, F, Na, K and other elements; the main components of the vitrification solution are: zirconium fluoride, hydrogen peroxide, fluorotitanic acid, zirconium fluoride, tartaric acid, sodium fluoroborate, potassium nitrate, lauryl alcohol Oxyethylene ether, KH550.
[0027] In the hot stamping process, in an atmosphere containing oxygen, the heating rate is controlled at 8°C / s in the temperature range...
Embodiment 3
[0030] The coating is a hot-pressed steel plate made of zinc-aluminum alloy. The composition of the coating is: 4.7% Al, the rest is Zn, and the steel plate is 30MnB5. The off-line treatment is carried out by vitrification process, and the coated steel plate is immersed in the vitrification solution. drying. The drying temperature is 110 ° C, the thickness of the ceramic film is 400 nm, mainly composed of ZrO 2 , ZrOF 2 、Zr 2 OF 2 、Al 2 o 3 , ZnO, SiO 2 Composition, especially nano-zirconia and alumina-based. The hot-dip coating contains Si, Ti, Mn, Na, F and other elements; the main components of the ceramic solution are: fluorozirconium salt, potassium permanganate, fluorotitanic acid, sodium persulfate, sodium nitrobenzenesulfonate, fluoride Zirconium, Sodium Citrate, KH560.
[0031] In the hot stamping process, in an atmosphere containing oxygen, the heating rate is controlled at 8°C / s in the temperature range below 650°C, and the heat preservation is carried out i...
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap