An ecological permeable brick

A permeable brick and ecological technology, applied in the production of ceramic materials, other household appliances, clay products, etc., can solve the problems of air pollution and low compressive strength of permeable bricks, improve environmental protection, help resource reuse, good toughness

Active Publication Date: 2021-06-04
柳晶(长春)环保科技有限公司
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the permeable brick still has the problem of low compressive strength. At the same time, because the current air pollution problem is becoming more and more serious, automobile exhaust is one of the main pollution sources, and facilities with air purification effects should be selected as much as possible in urban construction.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] An ecological water tile, the ecological water tile includes a weight of the following weight: 150 blast furnace slag, 4 parts of nanosoxide, 3 nanocium carbonate, 2 nano-titanium dioxide, 10 kaolin, 8 diatomaceous earth, Calcium-based solid sulfuride, 6 glass micro-balls, 4 zirconia fibers, 3 curing agents.

[0023] The preparation method of the ecological water tile of the present embodiment includes the following steps:

[0024] (1) We will weigh the raw materials according to the ratio, mix the nano silica, nanocalic carbonate, nano-titanium dioxide, kaolin, and diatomaceous earth, and the grinding machine, the grinding speed is 80R / min, the grinding time is 8 minutes, after passing 80 mesh sieve to obtain mixture a;

[0025] (2) Calcium-based sulfur, glass microbead, zirconia fiber, and mixture A, which are mixed in the blast furnace slag, and mixed with stirring, stirred at 4000 r / min at a rotational speed of 4000 R / min for 10 min, then The rotational speed of 2...

Embodiment 2

[0030] An ecological water, the ecological water, the ecological water, the ecological water, including 300 blast furnace slag, 10 nano silica, 9 nanocium carbonate, 6 nano-titanium dioxide, 20 kaolin, 18 diatomaceous earth, 18 4 parts of calcium-based sulfuride, 12 glass micro-balls, 12 zirconia fibers, 9 curing agents.

[0031] The preparation method of the ecological water tile of the present embodiment includes the following steps:

[0032] (1) We will weigh the raw materials according to the ratio, mix the nano silica, nanocalic carbonate, nano-titanium dioxide, kaolin, and diatomaceous earth, and the grinding machine is grinded, the grinding speed is 120R / min, the grinding time is 10 min, after passing 80 mesh sieve to obtain mixture a;

[0033] (2) The calcium-based solid sulfur, glass microbead, zirconia fiber and mixture A is sequentially added in the blast furnace slag, and the mixture is stirred and stirred, stirred at 6000 r / min at a rotation of 6000 R / min, and t...

Embodiment 3

[0038] An ecological water tile, the ecological melting brick includes a weight of the following weight: 180 blast furnace slag, 5 nano silica, 4 nanocium carbonate, 3 nano-titanium dioxide, 12 kaolin, 9 diatomaceous earth, 9 2 copper-based solid sulfurides, 7 glass microads, 5 zirconia fibers, 4 curing agents.

[0039] The preparation method of the ecological water tile of the present embodiment includes the following steps:

[0040] (1) We will weigh the raw materials according to the ratio, and mix the nano silica, nanocalic carbonate, nano-titanium dioxide, kaolin, and diatomaceous earth, and the grinding machine is grinded, the abrasive speed is 90R / min, the grinding time is 9 minutes, after which 80 mesh sieve to obtain mixture a;

[0041] (2) The calcium-based sulfur, glass microbead, zirconia fiber and mixture A, which are mixed in the blast furnace slag, and mixed with stirring, stirred at 4200 r / min at a rotational speed of 4200 r / min, and then stir The rotational ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of permeable bricks, in particular to an ecological permeable brick. The technical problem to be solved by the present invention is to provide an ecological permeable brick, which not only has high water permeability efficiency and compressive strength, but also has good purification and sterilization effects. In the ecological permeable brick of the present invention, the added nano-titanium dioxide has good dispersibility and weather resistance, and also has the functions of sterilization, antifouling, deodorization, and self-cleaning, which improves the environmental protection of the permeable brick; nano-silica can improve Anti-aging, strength and chemical resistance of permeable bricks; nano-calcium carbonate has the function of toughening and strengthening, which can improve the bending strength and flexural modulus of permeable bricks; zirconia fibers have good high temperature oxygen resistance, low thermal conductivity, Chemical stability can prolong the service life of the permeable bricks; the permeable bricks of the present invention have high water permeability, high compressive strength, good toughness, and good purification and sterilization effects.

Description

Technical field [0001] The present invention relates to the field of penetrating bricks, in particular, to an ecological water tile. Background technique [0002] In recent years, due to severe urban in severe cities that have caused heavy rain, sponge cities have become an important indicator of urban development concept and construction. To build a sponge city, an effective way is to lay a large-area waterproof brick in the city road, residential community, park square, and parking lot. Natural precipitation can be rapidly absorbed by the water, penetrate through the surface, to supplement the groundwater level in a timely manner; the water-impermeable brick can eliminate or reduce the area of ​​water, while producing flood control benefits, many urban contaminants will not pass water to migrate, can be effective Suppress large-area environmental pollution; after the rainfall is over, the moisture in the water-water tile is gradually released into the air, adjusting the surface...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/138C04B33/04
CPCC04B33/04C04B33/138C04B2235/3208C04B2235/3232C04B2235/3418C04B2235/3427C04B2235/36C04B2235/445C04B2235/5236C04B2235/96Y02P40/60
Inventor 任文强
Owner 柳晶(长春)环保科技有限公司