Forming method of fiber-reinforced sandwich-structure composite material

A sandwich structure, composite material technology, applied in additive processing, 3D object support structure, additive manufacturing, etc., can solve the problems of poor bonding between sandwich and panel, complicated process, etc., to improve bending resistance and wide application prospects , the effect of huge market economic value

Pending Publication Date: 2019-01-11
ZHEJIANG SCI-TECH UNIV
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional molding method has the disadvantages of complex process, special mold and poor combination at the joint between the interlayer and the panel, which cannot meet the requirements of modern industrial development.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Forming method of fiber-reinforced sandwich-structure composite material
  • Forming method of fiber-reinforced sandwich-structure composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] In order to make the object, technical solution and advantages of the present invention clearer, the present invention will be further described in detail below with reference to the accompanying drawings and embodiments. However, it should be understood that the specific embodiments described here are only used to explain the present invention, and are not intended to limit the scope of the present invention. Also, in the following description, descriptions of well-known structures and techniques are omitted to avoid unnecessarily obscuring the concept of the present invention.

[0024] An embodiment of the present invention provides a method for forming a fiber-reinforced sandwich structure composite material, and the specific steps are as follows:

[0025] Firstly, aramid fiber and polylactic acid are used as raw materials to clean and modify the aramid fiber. First, use acetone solution to clean for 10 minutes, then use absolute ethanol to clean the surface, and dry...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
Login to view more

Abstract

The invention is suitable for the technical field of sandwich-structure composite materials and discloses a forming method of a fiber-reinforced sandwich-structure composite material. A sandwich structure is prepared by using a 3D (three-Dimensional) printing technology; the sandwich shape can be freely designed without chemical bonding and compression molding forming; a designed mold is relatively high in precision; on one hand, the material formed by the 3D printing technology is relatively high in precision; the sandwich-structure material prepared by the method is relatively high in precision, and meets the requirements of industrial production; on the other hand, by adding the high-performance fiber-reinforced material, the bending resistance and impact resistance of the sandwich structure can be further improved so that the performances thereof can approach or even reach the performance of a solid to implement the lightweight and high-performance effect; and the forming method ofthe fiber-reinforced sandwich-structure composite material has huge market economic values and wide application prospects.

Description

【Technical field】 [0001] The invention relates to the technical field of sandwich structure composite materials, in particular to composite materials combined with fibers and polylactic acid, and a rapid prototyping method for sandwich structure composite materials. 【Background technique】 [0002] The preparation of sandwich structure composite materials usually adopts the method of segmented manufacturing and chemical agent bonding. The traditional molding method has the disadvantages of complicated process, special mold and poor combination at the junction of the interlayer and the panel, which cannot meet the requirements of modern industrial development. [0003] In order to improve the above shortcomings, it is necessary to propose a molding method for fiber-reinforced sandwich structure composite materials. The use of 3D printing rapid prototyping method can effectively solve the above problems, improve the molding efficiency and molding accuracy of the material, and a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B29C64/118B29C64/386B29C64/35B33Y10/00B33Y40/00B33Y50/00
CPCB29C64/118B29C64/35B29C64/386B33Y10/00B33Y40/00B33Y50/00
Inventor 祝成炎宋星田伟张红霞金肖克李婷婷
Owner ZHEJIANG SCI-TECH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap