High temperature resistant and flame retardant computer cable and preparation method thereof

A technology for computer cables and high temperature resistance, applied in the direction of insulating cables, cables, circuits, etc., can solve the problems of low structural strength, poor performance of high temperature resistance and flame retardancy, and short service life, so as to improve structural strength and service life, Increased toughness and improved service life

Active Publication Date: 2019-01-29
安徽华电线缆股份有限公司
View PDF9 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome the deficiencies of the prior art and provide a high-temperature-resistant and flame-retardant computer cable and its preparation method to solve the problem of poor high-temperature resistance and flame-retardant performance, low structural strength, and short service life of existing computer cables. and other technical problems, the computer cable produced by the present invention has high structural strength, long service life, excellent high temperature resistance, flame retardancy and other properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High temperature resistant and flame retardant computer cable and preparation method thereof
  • High temperature resistant and flame retardant computer cable and preparation method thereof
  • High temperature resistant and flame retardant computer cable and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Embodiment 1 discloses a preparation method of a high temperature resistant flame retardant computer cable, comprising the following preparation steps:

[0050] Step a: use a wire drawing machine to stretch the copper rod to obtain a copper wire, and then anneal the copper wire to obtain a conductor. The steps specifically include:

[0051] First put the copper wire into the heating furnace and heat it to 560-670°C and keep it warm for 2-3 hours;

[0052] Then stop heating the heating furnace, let the copper wire cool down to 300-350°C with the heating furnace;

[0053] Then the copper wire is taken out from the heating furnace, cooled naturally to normal temperature to obtain a conductor;

[0054] Step b: twisting the conductors of 20 to each other to obtain a guide core;

[0055] Step c: Use an extruder to extrude a layer of insulating layer on the outside of the guide core, then wrap a layer of shielding layer on the outside of the insulating layer, and finally wr...

Embodiment 2

[0068] Embodiment 2 discloses a preparation method of a high temperature resistant flame retardant computer cable, comprising the following preparation steps:

[0069] Step a: use a wire drawing machine to stretch the copper rod to obtain a copper wire, and then anneal the copper wire to obtain a conductor. The steps specifically include:

[0070] First put the copper wire into the heating furnace and heat it to 560-670°C and keep it warm for 2-3 hours;

[0071] Then stop heating the heating furnace, let the copper wire cool down to 300-350°C with the heating furnace;

[0072] Then the copper wire is taken out from the heating furnace, cooled naturally to normal temperature to obtain a conductor;

[0073] Step b: Twisting 20 conductors with each other to obtain a guide core;

[0074] Step c: Use an extruder to extrude a layer of insulating layer on the outside of the guide core, then wrap a layer of shielding layer on the outside of the insulating layer, and finally wrap a ...

Embodiment 3

[0087] Embodiment 3 discloses a preparation method of a high temperature resistant flame retardant computer cable, comprising the following preparation steps:

[0088] Step a: use a wire drawing machine to stretch the copper rod to obtain a copper wire, and then anneal the copper wire to obtain a conductor. The steps specifically include:

[0089] First put the copper wire into the heating furnace and heat it to 560-670°C and keep it warm for 2-3 hours;

[0090] Then stop heating the heating furnace, let the copper wire cool down to 300-350°C with the heating furnace;

[0091] Then the copper wire is taken out from the heating furnace, cooled naturally to normal temperature to obtain a conductor;

[0092] Step b: Twisting 30 conductors with each other to obtain a guide core;

[0093] Step c: Use an extruder to extrude a layer of insulating layer on the outside of the guide core, then wrap a layer of shielding layer on the outside of the insulating layer, and finally wrap a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high temperature resistant and flame retardant computer cable and a preparation method thereof. The preparation method comprises the preparation steps of a, carrying out drawing and annealing to obtain conductors; b, mutually twisting the conductors to obtain conductor cores; c, extruding an insulating layer outside each conductor core by adopting an extruding machine, then wrapping a shielding layer outside the insulating layer, and finally wrapping a fire resistant layer outside the shielding layer to obtain a wire core; d, mutually twisting the wire cores around the outer surface of a reinforcement core to obtain a cable core; e, wrapping a filling layer; f, wrapping an inner wrapping belt layer; g, extruding a fireproof layer; h, wrapping an outer wrapping belt layer; and i, extruding an outer sheath layer. The preparation method carries out improvement in allusion to the existing computer cable preparation method so as to improve the problems such as poorhigh temperature resistance, poor flame retardance, low structural strength and short service life of the existing computer cable. The computer cable prepared according to the invention is high in structural strength and long in service life and has excellent high temperature resistance and flame retardance.

Description

technical field [0001] The invention relates to the technical field of computer cables, in particular to a high temperature resistant flame retardant computer cable and a preparation method thereof. Background technique [0002] Computer cables are one of the special cables for electronic computer systems. They are urgently needed supporting products for modern industrial construction. They are widely used in electronic computers, instruments and meters, various Signal transmission and control system for automatic detection equipment and other information processing equipment. These fields require computer cables to be able to transmit electric energy stably for a long time. The materials of existing computer cables are mostly flammable rubber or plastics. Therefore, the existing computer cables are insufficient in high temperature resistance and flame retardancy. When working in a high-temperature environment, the outer sheath and insulation layer of the cable will melt an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01B7/18H01B7/02H01B7/295H01B7/22H01B7/24H01B7/28
CPCH01B7/0258H01B7/1875H01B7/1895H01B7/225H01B7/24H01B7/28H01B7/295
Inventor 刘登瑞肖剑呜卢鹏程何宏亮
Owner 安徽华电线缆股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com