Rolled glass decoration panel with dull polish textures and preparation method of rolled glass decoration panel

A frosted glass, decorative panel technology, applied in the field of decorative panels, can solve the problems of intolerance to scratches, complicated preparation, rough surface, etc.

Inactive Publication Date: 2019-02-01
JIANGSU XIUQIANG GLASSWORK CO LTD
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Compared with the frosted textured glass produced by acid corrosion, sand blasting and other processes, their material surface is rough, not resistant to scratches, not easy to clean, easy to fall off, and has defects such as chemical residues, which cannot meet the needs of customers.
At the same time, the preparation of existing glass panels is relatively complicated, and the aesthetics is not enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rolled glass decoration panel with dull polish textures and preparation method of rolled glass decoration panel
  • Rolled glass decoration panel with dull polish textures and preparation method of rolled glass decoration panel
  • Rolled glass decoration panel with dull polish textures and preparation method of rolled glass decoration panel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] see figure 1 , the present embodiment provides a rolled frosted textured glass decorative panel 100A, which includes a frosted glass substrate 110, a patterned decorative composite coating 120, a texture texture coating 130 and a back cover protective coating 140, and the patterned decorative composite coating 120 and The frosted glass substrate 110 is connected, the textured coating 130 is connected with the patterned decorative composite coating 120 , and the back cover protective coating 140 is connected with the patterned decorative composite coating 120 .

[0047] Specifically, the frosted glass substrate 110 includes a first frosted surface 111 and a first smooth surface 112 opposite to the first frosted surface 111, the patterned decorative composite coating 120 includes a first coating 121 and a second coating 122, the second A coating 121 is connected to the first smooth surface 112, a second coating 122 is connected to the first coating 121, the second coating...

Embodiment 2

[0056] see figure 2 This embodiment provides a rolled frosted textured glass decorative panel 100B, which differs from the rolled frosted textured glass decorative panel 100A provided in Embodiment 1 in that it is provided with a high temperature ink coating 150 on the first frosted surface 111 .

[0057] The difference between the preparation method of the rolled frosted textured glass decorative panel 100B of this embodiment and the preparation method provided in Example 1 is that no pretreatment is performed before screen printing, and the high temperature ink coating 150 is prepared.

[0058] High-temperature ink layer—first print high-temperature ink on the first frosted surface 111 of the frosted glass substrate 110 obtained by cooling, and then sinter at 980° C. to form a high-temperature ink coating 150 .

[0059] Then spray paint on the first smooth surface 112 according to the preparation method provided in Example 1 to obtain a patterned decorative composite coatin...

Embodiment 3

[0064] The rolled frosted textured glass decorative panel provided in this embodiment is consistent with the rolled frosted textured glass decorative panel 100B provided in Embodiment 2.

[0065] The preparation method of the rolled frosted textured glass decorative panel 100B in this embodiment is the same as the preparation method provided in Example 2, except that the operating conditions are changed.

[0066] High temperature ink layer - the sintering temperature is 320°C.

[0067] Pattern decorative composite coating—the mesh cloth of the first coating is 300 mesh, and the drying condition is 200 ° C for 7 minutes; the mesh cloth of the second coating is 350 mesh, and the drying condition of the second coating is 220 ° C ,8 minutes.

[0068] Texture texture coating—the mesh is 200 mesh, and the drying condition is 250°C for 7 minutes. A paint containing glitter powder is used.

[0069] Protective coating on the back cover—the mesh cloth of the protective coating is 350...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of decoration panels, in particular to a rolled glass decoration panel with dull polish textures and a preparation method of the rolled glass decoration panel. The rolled glass decoration panel with the dull polish textures comprises a dull polish glass substrate, a grain decoration composite coating, a texture coating and a back cover protecting coating, whereinthe grain decoration composite coating is connected with the dull polish glass substrate; the texture coating is connected with the grain decoration composite coating; and the back cover protecting coating is connected with the grain decoration composite coating. The rolled glass decoration panel with the dull polish textures has dull polish and metallic reflecting texture effect features, furthermore, the front surface (service surface) of the glass decoration panel is scratch-resistant and impact-resistant, and is easy to clean, and the back coating of the glass decoration panel is aging-resistant and environmentally friendly and resists stress of heat expansion and cold contraction.

Description

technical field [0001] The invention relates to the field of decorative panels, and in particular to a rolled frosted textured glass decorative panel and a preparation method thereof. Background technique [0002] Home appliance panels use frosted texture glass instead of plastic, steel plate, aluminum plate, stainless steel plate, film and UV transfer printing technology, which has been applied in normal advertising decoration and has been recognized and advocated by users at home and abroad. Compared with the frosted textured glass produced by acid corrosion, sandblasting and other processes, their material surface is rough, not resistant to scratches, not easy to clean, easy to fall off, and has defects such as chemical residues, which cannot meet the needs of customers. At the same time, the preparation of the existing glass panels is relatively complicated, and the aesthetic level is insufficient. Contents of the invention [0003] The object of the present invention...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline