A method of using waste hot blast stove balls and introducing recycled stoppers to produce aluminum carbon cladding materials
A hot blast stove and waste technology, applied in the field of refractory materials, can solve the problems of poor self-flow and slag erosion resistance, easy to be washed by molten steel and slag erosion, short service life of aluminum carbon package along the material, etc., to achieve optimization High temperature performance index, significant economic benefits, and the effect of ensuring quality
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0043] A method of using waste hot blast bolts and introducing a recovery stove to produce aluminum carbon bags, producing the performance requirements of the erosion of anti-steel water-shaped and slag, including the following steps:
[0044] Step (1). First, the recycled waste hot blast stove, the surface debris, eliminate the surface debris, crushing the jaw crusher, the cone crusher, and Raymond grinding, the screen screening, processing and crushing process Repair iron, the particle size is 5-8, 8-15mm, 200 mesh materials;
[0045] Step (2) Recovery the fake particles between the bone, the pseudo-particles are removed by the secondary screen sieve, and the particle grade distribution is 0.5-1 mm by the secondary screen screen. 50-60%, ≤0.5mm is 40-50%;
[0046] The above-mentioned recycled waste-old hot wind burner particles and the sturdy car cuts are analyzed. According to the physical and chemical index decision (3) and step (4) product ratio; the physical and chemical ind...
Embodiment 2
[0071] A method of using waste hot blast bolts and introducing a recovery stove to produce aluminum carbon bags, producing the performance requirements of the erosion of anti-steel water-shaped and slag, including the following steps:
[0072] Step (1). First, the recycled waste hot blast stove, the surface debris, eliminate the surface debris, crushing the jaw crusher, the cone crusher, and Raymond grinding, the screen screening, processing and crushing process Repair iron, the particle size is 5-8, 8-15mm, 200 mesh materials;
[0073] Step (2) Recovery the fake particles between the bone, the pseudo-particles are removed by the secondary screen sieve, and the particle grade distribution is 0.5-1 mm by the secondary screen screen. 50-60%, ≤0.5mm is 40-50%;
[0074] The above-mentioned recycled waste-old hot wind burner particles and the sturdy car cuts are analyzed. According to the physical and chemical index decision (3) and step (4) product ratio; the physical and chemical ind...
Embodiment 3
[0099] A method of using waste hot blast bolts and introducing a recovery stove to produce aluminum carbon bags, producing the performance requirements of the erosion of anti-steel water-shaped and slag, including the following steps:
[0100] Step (1). First, the recycled waste hot blast stove, the surface debris, eliminate the surface debris, crushing the jaw crusher, the cone crusher, and Raymond grinding, the screen screening, processing and crushing process Repair iron, the particle size is 5-8, 8-15mm, 200 mesh materials;
[0101] Step (2) Recovery the fake particles between the bone, the pseudo-particles are removed by the secondary screen sieve, and the particle grade distribution is 0.5-1 mm by the secondary screen screen. 50-60%, ≤0.5mm is 40-50%;
[0102] The above-mentioned recycled waste-old hot wind burner particles and the sturdy car cuts are analyzed. According to the physical and chemical index decision (3) and step (4) product ratio; the physical and chemical ind...
PUM
| Property | Measurement | Unit |
|---|---|---|
| particle size | aaaaa | aaaaa |
| particle diameter | aaaaa | aaaaa |
| density | aaaaa | aaaaa |