High-performance environmentally friendly waterborne single-component finish paint used on plastic substrate and production process
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A single-component, high-performance technology, applied in the direction of coating, etc., can solve the problems of poor scratch resistance, poor alcohol resistance, silver displacement, etc., and achieve the effect of good orientation and improved alcohol resistance
Pending Publication Date: 2019-03-15
HANGZHOU LIWEI CHEM INDAL PAINT
View PDF3 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
The original water-based single-pack topcoat has shortcomings such as poor silver displacement, poor alcohol resistance, and poor scratch resistance.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0015] Embodiment 1: Its proportioning composition by weight is as follows: 60 parts by weight of water-based one-component modified acrylic acid emulsion (AS2610, the glass transition temperature is more than 90), 100 parts by weight of deionized water, and 5 parts by weight of water-based film-forming aid , 5 parts by weight of water-based cellulose (HPMC), 0.3 parts by weight of water-based leveling agent, and 0.1 part by weight of water-based defoamer.
Embodiment 2
[0016] Embodiment 2: Its proportioning composition by weight is as follows: 80 parts by weight of water-based one-component modified acrylic acid emulsion (AS2610, glass transition temperature is more than 90), 20 parts by weight of deionized water, 10 parts by weight of water-based film-forming aid , 10 parts by weight of water-based cellulose (HPMC), 0.5 parts by weight of a water-based leveling agent, and 0.2 parts by weight of a water-based defoamer.
Embodiment 3
[0017] Embodiment 3: Its proportioning composition by weight is as follows: 70 parts by weight of water-based one-component modified acrylic acid emulsion (AS2610, glass transition temperature is more than 90), 15 parts by weight of deionized water, 6 parts by weight of water-based film-forming aid , 6 parts by weight of water-based cellulose (HPMC), 0.4 parts by weight of a water-based leveling agent, and 0.15 parts by weight of a water-based defoamer.
[0023] Fine pen (μm) depends on the product effect
[0024] Gloss 60° conforms to the standard template
[0025] Viscosity (25°C, apply 4 cups)≧35S
[0026] Storage stability (50±2℃7d) no caking
[0027] Water resistance 48h without blistering, cracking, peeling and other phenomena
[0028] Alcohol resistance (500g)≧80 times
[0029] R...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a high-performance environmentally friendly waterborne single-component finish paint used on a plastic substrate and a production process. The high-performance environmentallyfriendly waterborne single-component finish paint used on the plastic substrate comprises the following components in parts by weight: 60-80 parts of waterborne single-component modified acrylic emulsion, 10-20 parts of deionized water, 5-10 parts of a waterborne film-forming aid, 5-10 parts of waterborne celluloses, 0.3-0.5 part of a waterborne leveling agent and 0.1-0.2 part of a waterborne defoaming agent. The high-performance environmentally friendly waterborne single-component finish paint used on the plastic substrate has the beneficial effects that silver arrangement is good, and the advantage of good directionality of waterborne acrylic emulsion with large molecular weight is adopted. Alcohol resistance is good, the waterborne single-component emulsion with the vitrification temperature being 90 or above is adopted, the waterborne single-component emulsion is combined to nitrogen-containing fibers, and the alcohol tolerance is greatly improved. The scratching resistance is high, the vitrification temperature is high, the self-hardness of the resin with the high vitrification temperature is high, and by use of a large amount of directional wax slurry and wax powder with extinction capability, the use amount of digestion powder is greatly reduced, and therefore, the scratching resistance is qualitatively improved.
Description
technical field [0001] The invention belongs to the field of water-based paints, in particular to a high-performance, environment-friendly water-based one-component topcoat for plastic substrates and a production process. Background technique [0002] The successive implementation of the "Environmental Protection Law" and the "Air Pollution Prevention and Control Law" has forced enterprises to strictly abide by the amount of VOC emissions and reduce the degree of pollution to the environment. The original water-based single-pack topcoat has deficiencies such as poor silver displacement, poor alcohol resistance, and poor scratch resistance. Contents of the invention [0003] The purpose of the present invention is to overcome the deficiencies in the prior art, and provide a high-performance environmental protection water-based one-component topcoat and production process for plastic substrates. [0004] The purpose of the present invention is accomplished through the follo...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more