High-performance environment-friendly water-based single-component primer for plastic base materials and production process of primer

A high-performance, one-component technology, applied in coatings, cellulose coatings, etc., can solve problems such as silver displacement, poor adhesion, slow drying, etc., and achieve high fullness, excellent adhesion, and good orientation Effect

Pending Publication Date: 2019-02-01
HANGZHOU LIWEI CHEM INDAL PAINT
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The original water-based single-pack primer has shortcomings such as silver displacement, slow drying, and poor adhesion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Embodiment 1: Its proportioning composition by weight is as follows: 50 parts by weight of water-based one-component acrylic emulsion, 10 parts by weight of deionized water, 5 parts by weight of water-based film-forming aid, 10 parts by weight of water-based cellulose, 5 parts by weight of water-based wax slurry Parts by weight, 0.1 part by weight of water-based defoamer, 0.2 part by weight of water-based wetting agent, and 1 part by weight of water-based adhesion promoter.

Embodiment 2

[0016] Example 2: 65 parts by weight of water-based one-component acrylic emulsion, 15 parts by weight of deionized water, 10 parts by weight of water-based film-forming aid, 15 parts by weight of water-based cellulose, 10 parts by weight of water-based wax slurry, and 0.3 parts by weight of water-based defoamer parts, 0.5 parts by weight of water-based wetting agent, and 2 parts by weight of water-based adhesion promoter.

Embodiment 3

[0017] Example 3: 60 parts by weight of water-based one-component acrylic emulsion, 12 parts by weight of deionized water, 8 parts by weight of water-based film-forming aid, 12 parts by weight of water-based cellulose, 8 parts by weight of water-based wax slurry, and 0.2 parts by weight of water-based defoamer parts, 0.4 parts by weight of water-based wetting agent, and 1.5 parts by weight of water-based adhesion promoter.

[0018] Main Specifications

[0019] Solid content (%)≧35

[0020] Drying conditions (surface dry) 5-10min

[0021] Pencil hardness (abrasion) HB

[0022] Cross-cut test (level)≦1

[0023] Fineness (μm) depends on the product effect

[0024] Gloss 60° conforms to the standard template

[0025] Viscosity (25℃, 2#)≧30S

[0026] Storage stability (50±2℃7d) no caking

[0027] Water resistance 48h without blistering, cracking, peeling and other phenomena.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a high-performance environment-friendly water-based single-component primer for plastic base materials and a production process of the primer. The primer consists of the following components in parts by weight: 50-65 parts of a water-based single-component acrylic emulsion, 10-15 parts of deionized water, 5-10 parts of a water-based film-forming assistant, 10-15 parts of water-based cellulose, 5-10 parts of water-based wax liquor and 0.1-0.3 part of a water-based defoaming agent. The primer has the beneficial effects that the silver discharge performance is good, the large-molecular-weight water-based acrylic emulsion is adopted, the advantage of good directionality is adopted, and the cellulose is combined, so that silver discharge is improved. Drying is fast, a conventional mode of "twice coating and twice baking" is converted into a mode of "twice coating and once baking", and the effect of high fullness and high metal feeling after coating can be guaranteed. The adhesive force is high, and the water-based acrylic emulsion containing trace hydroxyl is beneficial for combination with hydrogen bonds on materials; and meanwhile, an adhesive force promoter is added, so that the adhesion force of the primer to the material and the interlayer is improved.

Description

technical field [0001] The invention belongs to the field of water-based paints, in particular to a high-performance, environment-friendly water-based one-component primer for plastic substrates and a production process. Background technique [0002] The successive implementation of the "Environmental Protection Law" and the "Air Pollution Prevention and Control Law" has forced enterprises to strictly abide by the amount of VOC emissions and reduce the degree of pollution to the environment. The original water-based single-pack primer has deficiencies such as silver displacement, slow drying, and poor adhesion. Contents of the invention [0003] The purpose of the present invention is to overcome the deficiencies in the prior art, and provide a high-performance environmental protection water-based one-component primer and production process for plastic substrates. [0004] The purpose of the present invention is accomplished through the following technical solutions. The...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D133/00C09D101/02C09D123/06C09D7/65
CPCC08L2205/035C09D7/65C09D133/00C08L1/02C08L23/06C08L83/12C08L23/28
Inventor 张磊张涛
Owner HANGZHOU LIWEI CHEM INDAL PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products