Ultraviolet curing solvent-free medical pressure sensitive adhesive and preparation process thereof

A pressure-sensitive adhesive, ultraviolet light technology, applied in the directions of adhesives, adhesive types, ester copolymer adhesives, etc., can solve the problems of skin irritation, difficult to achieve high adhesive force, etc., achieve high cohesion, and simple preparation method Convenient, light-colored effects

Inactive Publication Date: 2019-04-05
KUNSHAN SUMEI FINE CHEM CO LTD
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the medical acrylic pressure-sensitive adhesive products currently on the market are made of traditional acrylic solvent-based glue, and the thickness of the glue layer is mostly 30~50um. If the coating thickness of acrylic solvent-based glue is reduced, the adhesion will also decrease. The performance requirements of general medical adhesive products require at least 1kg / in of adhesive force. If traditional acrylic solvent-based glue is used, its adhesive force can only reach 500-800g / in; During the process, if the solvent is not dried, the remaining solvent will irritate the skin. Therefore, it is difficult for the existing acrylic solvent-based glue to meet the requirements of high adhesion and non-irritation. The above problems need to be solved urgently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A kind of ultraviolet curing solvent-free medical pressure-sensitive adhesive, comprises the following components by weight:

[0034] 45 parts of butyl acrylate;

[0035] 10 parts of 2-ethylhexyl acrylate;

[0036] Acrylic acid 1 part;

[0037] 4 parts of hydroxyethyl acrylate;

[0038] 64 parts of ethyl acetate;

[0039] Benzoyl peroxide 0.8 part;

[0040] 2 parts of dilauroyl peroxide;

[0041] 10 parts of terpene phenolic resin;

[0042] 0.3 parts of photoinitiator.

[0043] The photoinitiator is benzoin ethyl ether, 2-hydroxyl-2-methyl-1-phenyl-1-acetone, 1-hydroxycyclohexyl phenyl ketone, benzophenone, 2,4,6-trimethyl One or more of ethyl benzoylphenylphenate.

[0044] A preparation process of an ultraviolet light curing solvent-free medical pressure-sensitive adhesive, comprising the following process:

[0045] A. Put 45 parts of butyl acrylate, 10 parts of 2-ethylhexyl acrylate, 1 part of acrylic acid, 4 parts of hydroxyethyl acrylate and 60 parts of eth...

Embodiment 2

[0053] A kind of ultraviolet curing solvent-free medical pressure-sensitive adhesive, comprises the following components by weight:

[0054] 50 parts of butyl acrylate;

[0055] 5 parts of 2-ethylhexyl acrylate;

[0056] 2 parts of hydroxyethyl acrylate;

[0057] 80 parts of ethyl acetate;

[0058] Benzoyl peroxide 1.6 parts;

[0059] 3 parts of dilauroyl peroxide;

[0060] 5 parts of terpene phenolic resin;

[0061] 0.8 part of photoinitiator.

[0062] The photoinitiator is benzoin ethyl ether, 2-hydroxyl-2-methyl-1-phenyl-1-acetone, 1-hydroxycyclohexyl phenyl ketone, benzophenone, 2,4,6-trimethyl One or more of ethyl benzoylphenylphenate.

[0063] A preparation process of an ultraviolet light curing solvent-free medical pressure-sensitive adhesive, comprising the following process:

[0064] A. Put 50 parts of butyl acrylate, 5 parts of 2-ethylhexyl acrylate, 2 parts of hydroxyethyl acrylate, and 70 parts of ethyl acetate into a three-necked round-bottomed flask, and th...

Embodiment 3

[0072] A kind of ultraviolet curing solvent-free medical pressure-sensitive adhesive, comprises the following components by weight:

[0073] 10 parts of butyl acrylate;

[0074] 40 parts of 2-ethylhexyl acrylate;

[0075] Acrylic acid 1 part;

[0076] 80 parts of ethyl acetate;

[0077] 2 parts of benzoyl peroxide;

[0078] Dilauroyl peroxide 1.5 parts;

[0079] 20 parts of terpene phenolic resin;

[0080] 0.8 part of photoinitiator.

[0081] The photoinitiator is benzoin ethyl ether, 2-hydroxyl-2-methyl-1-phenyl-1-acetone, 1-hydroxycyclohexyl phenyl ketone, benzophenone, 2,4,6-trimethyl One or more of ethyl benzoylphenylphenate.

[0082] A preparation process of an ultraviolet light curing solvent-free medical pressure-sensitive adhesive, comprising the following process:

[0083] A. Put 10 parts of butyl acrylate, 40 parts of 2-ethylhexyl acrylate, 1 part of acrylic acid and 65 parts of ethyl acetate into a three-necked round-bottomed flask, and then connect the thre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of medical pressure sensitive adhesives, and especially relates to an ultraviolet curing solvent-free medical pressure sensitive adhesive and a preparationprocess thereof. The pressure sensitive adhesive includes, by weight, the following components: 0-50 parts of butyl acrylate, 10-50 parts of 2-ethylhexyl acrylate, 0-2 parts of acrylic acid, 0-5 parts of 2-hydroxyethyl acrylate, 10-80 parts of ethyl acetate, 0.2-2 parts of benzoyl peroxide, 1.5-3 parts of dilauroyl peroxide, 5-30 parts of terpene hydrocarbon and phenolic resin, and 0.1-2 parts ofa photoinitiator. A medical pressure sensitive adhesive product prepared by utilizing the ultraviolet curing solvent-free medical pressure sensitive adhesive of the invention has high adhesion, simultaneously has good retention force, and greatly satisfies requirements for the adhesion more than 1kg / in and the retention force more than 24 hours of the medical pressure sensitive adhesive product.

Description

technical field [0001] The invention relates to the technical field of medical pressure-sensitive adhesives, in particular to an ultraviolet-cured solvent-free medical pressure-sensitive adhesive and a preparation process thereof. Background technique [0002] Pressure-sensitive adhesive products can be widely used in various industries such as printing, packaging, construction, medical treatment, electronics, automobiles and daily necessities, and play various bonding functions such as adhesion, fixing, protection, sealing, insulation and bundling. Traditionally in China, the first generation of medical pressure-sensitive adhesive products composed of natural rubber and resin has been around for a long time, and then evolved to use zinc oxide adhesive plaster to make medical pressure-sensitive adhesive products, but in recent years, synthetic rubber, organic The emergence of silicon and acrylate pressure-sensitive adhesives has gradually become the application material for ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J133/08C09J145/00C09J7/22C09J7/21C08F220/18C08F220/06C08F220/28
CPCC08F220/18C08F220/1804C08L2201/08C08L2205/04C08L2312/06C09J133/08C09J2301/312C09J2433/00C08L45/00C08F220/06C08F220/281
Inventor 徐存
Owner KUNSHAN SUMEI FINE CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com