A kind of PC composition with high whiteness and high toughness and preparation method thereof
A high-toughness and composition technology, applied in the field of high-whiteness and high-toughness PC composition and its preparation, can solve the problems of incomplete application, no titanium dioxide treatment, etc., to maintain hiding power, improve toughness, improve toughness and whiteness. degree of effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment Construction
[0023] In order to make the purpose, technical solutions and advantages of the embodiments of the present invention clearer, the technical solutions will be clearly and completely described below in conjunction with the embodiments of the present invention. Obviously, the described embodiments are part of the embodiments of the present invention, not all of them. the embodiment. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without creative efforts fall within the protection scope of the present invention.
[0024] The present invention provides Examples 1-4 and Comparative Examples 1-2.
[0025] Table 1: Composition and proportioning according to weight proportion of embodiment and comparative example
[0026]
[0027] Wherein, preferably, the number-average molecular weight of the PC resin is between 22000-30000, and the melt index at 300° C. under a load of 1.2 kg is 5 g / 10 min-20 g / 10 min.
[...
PUM
Property | Measurement | Unit |
---|---|---|
melt flow index | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
length | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com