A kind of heat-resistant resin for thermal transfer coating and preparation method thereof

A technology of high heat resistance and thermal transfer printing, which is applied in the field of resin materials, can solve the problems of high transparency and good stability, and achieve the effect of simple process, good stability and poor printing suitability

Active Publication Date: 2021-06-18
XIAN TIANYI ADHESIVE MATERIAL CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the deficiencies of the above-mentioned prior art, provide a kind of heat-resistant resin for thermal transfer coating and its preparation method, overcome the problem that the resin in the prior art cannot have good heat resistance and good printing adaptability at the same time , good stability and high transparency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of heat-resistant resin for thermal transfer coating and preparation method thereof
  • A kind of heat-resistant resin for thermal transfer coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach

[0026] It should be noted that the structures, proportions, sizes, etc. shown in the drawings attached to this specification are only used to match the content disclosed in the specification, for those who are familiar with this technology to understand and read, and are not used to limit the implementation of the present invention Any modification of the structure, change of the proportional relationship or adjustment of the size shall still fall within the scope of the technical content disclosed in the present invention without affecting the effect and purpose of the present invention. In the range.

[0027] At the same time, terms such as "upper", "lower", "left", "right", "middle" and "one" quoted in this specification are only for the convenience of description and are not used to limit this specification. The practicable scope of the invention and the change or adjustment of its relative relationship shall also be regarded as the practicable scope of the present inventi...

Embodiment 1

[0029] The invention discloses a heat-resistant resin for thermal transfer coating, which is made of phosphate-modified acrylate resin, polyamide resin, styrene-modified alkyd resin, plasticizer and organic solvent, wherein each component In parts by weight: 15-30 parts of phosphate-modified acrylate resin, 1-5 parts of polyamide resin, 1-5 parts of styrene-modified alkyd resin, 0.5-3 parts of plasticizer, 60-80 parts of organic solvent.

Embodiment 2

[0031] The invention discloses a heat-resistant resin for thermal transfer coating, which is made of phosphate-modified acrylate resin, polyamide resin, styrene-modified alkyd resin, plasticizer and organic solvent, wherein each component In parts by weight: 15-30 parts of phosphate-modified acrylate resin, 1-5 parts of polyamide resin, 1-5 parts of styrene-modified alkyd resin, 0.5-3 parts of plasticizer, 60-80 parts of organic solvent.

[0032] Preferably, the components by weight are: 20-25 parts of phosphate-modified acrylate resin, 2-4 parts of polyamide resin, 2-4 parts of styrene-modified alkyd resin, 1-2 parts of plasticizer, 65-75 parts of organic solvent.

[0033] Preferably, the components by weight are: 22 parts of phosphate-modified acrylate resin, 3 parts of polyamide resin, 3 parts of styrene-modified alkyd resin, 2 parts of plasticizer, 70 parts of organic solvent .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
softening pointaaaaaaaaaa
thermal resistanceaaaaaaaaaa
Login to View More

Abstract

The invention discloses a heat-resistant resin for thermal transfer coating and a preparation method thereof, which is made of phosphate-modified acrylate resin, polyamide resin, styrene-modified alkyd resin, plasticizer and organic solvent. The components are calculated in parts by weight: 15-30 parts of phosphate-modified acrylate resin, 1-5 parts of polyamide resin, 1-5 parts of styrene-modified alkyd resin, and 0.5 parts of plasticizer ~3 parts, 60~80 parts of organic solvent.

Description

technical field [0001] The invention belongs to the technical field of resin materials, and in particular relates to a heat-resistant resin for thermal transfer coating and a preparation method thereof. Background technique [0002] With the improvement of human living standards and the advancement of science and technology, more and more coatings are used in various fields of society, among which transfer coatings for paper coating attract the most attention. It has changed from heat-resistant transfer resin coating to high heat-resistant transfer resin coating, and the heat resistance of heat-resistant resin is getting higher and higher. Next, to complete the follow-up molding and printing ink process, the protective coating needs to be resistant to temperature and friction to protect the aluminized layer from being oxidized and losing its brightness, thereby affecting the aesthetics. [0003] The principle of heat-resistant resin for thermal transfer coating is to coat t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/12C09D177/00C09D151/08
Inventor 王伊尹常杰
Owner XIAN TIANYI ADHESIVE MATERIAL CO LTD