Preparation method for flower-shaped micron-sized silver powder with slender and large petals

A micron silver powder and flower-shaped technology, which is applied in the field of preparation of flower-shaped micron silver powder, can solve problems such as complicated preparation process

Pending Publication Date: 2019-05-21
TIANJIN POLYTECHNIC UNIV
View PDF12 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the patent CN106424752A, the first reducing agent solution, the second reducing agent solution, and the surfactant solution need to be used. In

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for flower-shaped micron-sized silver powder with slender and large petals
  • Preparation method for flower-shaped micron-sized silver powder with slender and large petals

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0013] Example 1

[0014] The silver nitrate is dissolved in water to obtain a 0.9 mol / L silver nitrate aqueous solution. The reducing agent ascorbic acid was dissolved in water to obtain 0.9 mol / L ascorbic acid aqueous solution. 9.6 mL of ascorbic acid aqueous solution was quickly added to 10 mL of silver nitrate aqueous solution with a stirring rate of 100 rpm, and reacted at 20°C for 10 minutes, and then immediately washed the silver powder with a large amount of deionized water. After drying, a flower shape with elongated and large petals was obtained Micron silver powder.

Example Embodiment

[0015] Example 2

[0016] Dissolve silver nitrate in water to obtain 1.1 mol / L silver nitrate aqueous solution. The reducing agent ascorbic acid was dissolved in water to obtain 1.1 mol / L ascorbic acid aqueous solution. Quickly add 106mL ascorbic acid aqueous solution to 100mL silver nitrate aqueous solution with a stirring rate of 500 rpm, react at 30°C for 5 minutes, then immediately wash the silver powder with a large amount of deionized water, and obtain flower-like micrometers with slender and large petals after drying. Silver powder.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Concentrationaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method for flower-shaped micron-sized silver powder with slender and large petals. The preparation method includes the following steps that silver nitrate water solution is prepared, ascorbic acid aqueous solution is quickly added to the silver nitrate solution at a certain stirring rate, reaction is conducted at 20-30 DEG C for 5-10 minutes, silver powder iswashed with a large number of deionized water immediately, and the flower-like micron-sized silver powder with the slender and large petals is obtained after drying. The method does not need to add substances such as surfactants, the preparation process is simple and easy to operate, and the obtained silver powder is uniform in appearance, high in purity, and high in conversion rate, and suitablefor actual production.

Description

technical field [0001] The invention belongs to the technical field of metal particle synthesis, and in particular relates to a preparation method of flower-shaped micron silver powder with slender and long petals. Background technique [0002] Silver powder can be widely used in conductive rubber, conductive adhesive, conductive coating, etc., involving many fields such as electronic equipment, catalysis, antibacterial, electromagnetic shielding, etc. At present, widely used silver powder is mainly flaky, spherical and spherical silver powder prepared by ball milling method or chemical synthesis method, such as the preparation method of a small particle size flaky silver powder in Chinese patent (CN108405859A), good dispersion The preparation method of fine silver powder (CN105345023A) etc. In addition, there are also reports about preparing polygonal silver powder (CN1401452A), rod-shaped silver powder (CN1059211765A), and dendritic silver powder (CN101811196A, CN10135381...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22F9/24
Inventor 纪艳红何本桥苗鹏吴鑫黄晨波赵兰兰于跃阴育辰
Owner TIANJIN POLYTECHNIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap