A Method for Reducing Welding Stress of Steel Structure Products

A welding stress and steel structure technology, applied in the field of steel structure welding, can solve problems affecting the performance of steel structures, reduce the stiffness of welded joints, weld cracks, etc., and achieve the goal of reducing welding stress hazards, reducing structural deformation, and improving stability Effect

Active Publication Date: 2021-11-26
安徽森钢建筑工程有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the metal yield effect in the weld area, while reducing the stiffness of the welded joint, the consequences will affect the performance of the steel structure
If the unreleased welding residual stress is too large, welding cracks may even occur

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A method for reducing the welding stress of steel structure products, the method for reducing the welding stress of steel structure products specifically includes the following steps:

[0024] 1). Preheating: first heat the steel structure products to 600°C under program-controlled heating, and the temperature rise rate is 2.5°C / min. 1.5℃ / min;

[0025] 2). Welding: Combine the steel structure products while they are hot, and use argon arc welding to weld the steel structure products, control the number of welds inside a single weld bead to 50cm / piece, and avoid 2 or 3 welds vertically Cross, control the thickness deviation of the weld to 0-0.3cm, and control the number of weld beads inside a single weld layer to be 3-5 per layer;

[0026] 3). Cooling: Cool the welded steel structure products to 10°C, the temperature drop rate is 0.5°C / min, and keep the temperature for 24 hours when the temperature reaches the lowest point;

[0027] 4). Annealing: raise the temperature...

Embodiment 2

[0038] A method for reducing the welding stress of steel structure products, the method for reducing the welding stress of steel structure products specifically includes the following steps:

[0039] 1). Preheating: first heat the steel structure products to 400°C under program-controlled heating, and the temperature rise rate is 1.0°C / min. 0.5℃ / min;

[0040] 2). Welding: Combine the steel structure products while they are hot, and use argon arc welding to weld the steel structure products, control the number of welds inside a single weld bead to 30cm / piece, and avoid 2 or 3 welds vertically Cross, control the thickness deviation of the weld seam to 0-0.5cm, and control the number of weld beads inside a single welding layer to 3-4 per layer;

[0041] 3). Cooling: Cool the welded steel structure products to 5°C, the temperature drop rate is 0.1°C / min, and keep the temperature at the lowest point for 18 hours;

[0042] 4).Annealing: raise the temperature of the steel structure...

Embodiment 3

[0053] A method for reducing the welding stress of steel structure products, the method for reducing the welding stress of steel structure products specifically includes the following steps:

[0054] 1). Preheating: first heat the steel structure products to 500°C under program-controlled heating, and the temperature rise rate is 1.5°C / min. 1.0℃ / min;

[0055] 2). Welding: Combine the steel structure products while they are hot, and use argon arc welding to weld the steel structure products, control the number of welds inside a single weld bead to 40cm / piece, and avoid 2 or 3 welds vertically Cross, control the thickness deviation of the weld seam to 0-0.2cm, and control the number of weld beads inside a single welding layer to 4-6 per layer;

[0056] 3). Cooling: Cool down the welded steel structure products to 5°C, the temperature drop rate is 0.2°C / min, and keep the temperature at a constant temperature for 20 hours when the temperature reaches the lowest point;

[0057] 4...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for reducing the welding stress of steel structure products, which comprises the following steps: first, the temperature of the steel structure products is raised under program control and kept at a constant temperature, and then the temperature is lowered to the welding temperature; welding is performed while it is hot, and the weld seam and weld bead are controlled. number; after welding, lower it to a low temperature for heat preservation and refrigeration; heat it up to a high temperature again, keep the temperature for a period of time and then cool it down to room temperature; use a vibration aging device for vibration treatment when heating up and constant temperature; finally polish the steel structure, and The grinding area is coated with waterproof grease, and the present invention comprehensively removes the welding stress by performing preheating, welding, cooling, annealing and vibration on the steel structure products to eliminate the welding stress, which reduces the welding stress by more than 90%, and avoids the impact of the welding stress on the steel structure. The destruction of steel structure products, thereby improving the strength, stiffness and hardness of steel structure products, ensuring the safety of steel structure products in use, greatly reducing welding stress hazards, reducing structural deformation, thereby improving the stability of steel structures.

Description

technical field [0001] The invention relates to the technical field of steel structure welding, in particular to a method for reducing welding stress of steel structure products. Background technique [0002] The steel structure has the advantages of high strength, good toughness, good seismic performance, and fast construction speed. It is very suitable for the development of modern engineering structures to towering, long-span, and heavy-duty structures, and engineering applications are increasing. In super high-rise buildings, long-span buildings and long-span bridges, heavy-duty industrial plants and special structures, the thickness of steel plates required for main stress components such as beams, columns, supports, shear walls, and trusses is increasing. Even if a combined structure that can give full play to the respective advantages of steel and concrete and significantly reduce the wall thickness of the steel plate is adopted, the thickness of the steel used to mee...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B23P15/00C21D10/00C21D1/26
CPCB23P15/00C21D1/26C21D10/00
Inventor 丁伟
Owner 安徽森钢建筑工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap