A kind of gravure back coating ink and its preparation method and application
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of back coating and ink, applied in the printing field, can solve problems such as poor dispersion of silica, influence on paper separation, and inconvenience of close bonding, so as to prevent paper bonding and sticking, vacuum phenomenon, and avoid pollution effect
Active Publication Date: 2022-01-14
SHENZHEN GLAREWAY TECH CO LTD
View PDF0 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, the traditional back-coating ink is only for the purpose of improving paper warping and deformation, ignoring that back-coating can easily fill the fiber gap on the back of the paper, resulting in a significant improvement in the smoothness of the back of the paper, resulting in a very small gap between the back of the upper paper and the front of the lower paper, and the air is exhausted. Causes tight fit and inconvenient post-process paper feeding
For example, Lingying PG-2105I water-based back coating, its composition is polyvinyl alcohol 5-10wt%, silicon dioxide 0-0.5wt%, ethanol 1-10wt% and water 50-90wt%, the ink is emulsified with polyvinyl alcohol The dispersion of silicon dioxide is not good, and sedimentation occurs; and when printing, all the silicon dioxide is filled into the paper fiber gap, forming a flat back-coated thin layer, which makes the paper flatness too high, and the air between the papers in the delivery process If the paper is exhausted, the paper will be closely bonded under the action of pressure, resulting in paper sticking, which will affect the subsequent process of paper feeding
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
preparation example Construction
[0033] The present invention provides the preparation method of gravure back-coating ink described in the technical scheme, comprising the following steps: mixing polyethylene wax, polyvinyl alcohol, styrene-acrylic acid copolymer, sodium dioctyl succinic acid sulfonate, silicon dioxide Mix with solvent to get gravure backcoat ink.
[0034] In the present invention, the consumption of described polyethylene wax, polyvinyl alcohol, styrene-acrylic acid copolymer, sodium dioctyl succinic acid sulfonate, silicon dioxide and solvent is the same as the consumption of each raw material in the above-mentioned technical scheme, in This will not be repeated here.
[0035]In the present invention, the polyethylene wax, polyvinyl alcohol, styrene-acrylic acid copolymer, dioctyl sodium sulfosuccinate, silicon dioxide and solvent are preferably mixed in such a way that the solvent, polyvinyl alcohol and dioctyl Sodium succinate sulfate is mixed with ethanol, silicon dioxide and polyethyle...
Embodiment 1
[0039] In parts by weight, 2 parts of polyethylene wax, 5 parts of polyvinyl alcohol, 2 parts of styrene-acrylic acid copolymer, 0.5 part of dioctyl sodium sulfosuccinate, 0.1 part of silicon dioxide (particle size 15 μm), 6 parts Parts of ethanol and 84.4 parts of water were stirred at 90 rpm for 60 min to obtain gravure back-coated ink.
Embodiment 2～3
[0041] The gravure back-coating ink was prepared according to the preparation method of Example 1, and the dosage of each raw material in Examples 2-3 is shown in Table 1.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
particle size
aaaaa
aaaaa
Login to View More
Abstract
The invention provides a kind of gravure back-coating ink and its preparation method and application, belonging to the field of printing technology. The gravure back-coating ink provided by the invention comprises the raw materials of the following components: polyethylene wax, polyvinyl alcohol, styrene- Acrylic acid copolymer, sodium dioctyl sulfosuccinate, silicon dioxide and solvent. The invention can effectively improve the internal lubricity of the gravure back-coating ink and improve the dispersion of silicon dioxide by adding polyethylene wax, styrene-acrylic acid copolymer, and sodium dioctyl succinate sulfonate to the components of the traditional water-based back-coating ink It has anti-sedimentation effect, gravure back-coated ink changes the moisture content of the paper, fills the fiber gaps on the back of the paper, and inhibits the paper from warping and deformation; at the same time, a thin surface layer with gaps between microcrystalline particles is formed to maintain air retention and prevent It prevents the generation of vacuum phenomenon, thereby eliminating the occurrence of paper sticking and sticking phenomenon.
Description
technical field [0001] The invention relates to the technical field of printing, in particular to a gravure back-coating ink and a preparation method and application thereof. Background technique [0002] During the paper printing process, the moisture content (that is, the degree of dryness), the printing ink level and the pressure of the printing roller will all affect the flatness and warping degree of the paper after printing. Specifically, due to the single-sided printing of the paper, under the action of drying and plate roller pressure, the moisture in the paper evaporates until the moisture content of the printed sheet is lower than 4.5%. The paper is curled and deformed. If the paper is deformed, it will easily lead to uneven delivery, causing the needle position of the printing machine to jump and register poorly, and the reject rate is high. [0003] In the prior art, the degree of deformation of the paper is slowed down through the back coating process. Howeve...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 