Racing tire tread rubber formula and preparation method thereof

A racing tire and surface rubber technology, which is applied in the field of racing tire tread rubber formula and its preparation, can solve the problems of difficult dispersion, high specific surface area carbon black filler mixing and heat generation, and difficulty in fully exerting the mechanics and mechanical properties of the formula. To achieve the effect of long mileage, long service life and excellent grip

Inactive Publication Date: 2019-08-30
JIANGSU GENERAL SCI TECH
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional racing treads use high filling to improve grip, and a large amount of carbon black fillers with high structure and high specific surface area

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0018] Example 1

[0019] The formula of racing tread compound, in parts by weight, includes: 20 parts of natural rubber, 100 parts of styrene-butadiene rubber carbon black masterbatch, 30 parts of styrene-butadiene rubber, 5 parts of high styrene resin, 10 parts of carbon black BL101, 4 parts of aromatic oil parts, 4 parts of rosin, 2 parts of antioxidant 4020, 1.5 parts of antioxidant RD, 5 parts of zinc oxide, 2 parts of stearic acid, 1.2 parts of sulfur, 1.5 parts of accelerator NS, and 0.4 part of anti-scorch agent;

[0020] The preparation method of the racing tread rubber comprises the following steps:

[0021] (1) Master batch: The master batch adopts two-stage rubber mixing

[0022] One stage of masterbatch: in parts by weight, 20 parts of natural rubber, 100 parts of styrene-butadiene rubber carbon black masterbatch, 30 parts of styrene-butadiene rubber, 5 parts of high styrene resin, 10 parts of carbon black BL101, and 4 parts of aromatic oil , 4 parts of rosin, 1...

Example Embodiment

[0025] Embodiment 2

[0026] The formula of racing tread compound, in parts by weight, includes: 10 parts of natural rubber, 110 parts of styrene-butadiene rubber carbon black masterbatch, 13 parts of styrene-butadiene rubber, 10 parts of high styrene resin, 25 parts of carbon black BL201, 8 parts of aromatic oil parts, 2 parts of rosin, 2 parts of antioxidant 4020, 1.5 parts of antioxidant RD, 5 parts of zinc oxide, 2 parts of stearic acid, 1.6 parts of sulfur, 1 part of accelerator CZ, and 0.3 part of anti-scorch agent;

[0027] The preparation method of the racing tread rubber comprises the following steps:

[0028] (1) Master batch: The master batch adopts two-stage rubber mixing

[0029] One stage of masterbatch: in parts by weight, 10 parts of natural rubber, 110 parts of styrene-butadiene rubber carbon black masterbatch, 13 parts of styrene-butadiene rubber, 10 parts of high styrene resin, 25 parts of carbon black BL201, 8 parts of aromatic oil , 2 parts of rosin, 1.5...

Example Embodiment

[0032] Example 3

[0033] The formula of racing tread compound, in parts by weight, includes: 15 parts of natural rubber, 120 parts of styrene-butadiene rubber carbon black masterbatch, 5 parts of styrene-butadiene rubber, 3 parts of high styrene resin, 2 parts of carbon black BL101, and 2 parts of carbon black BL201 3 parts, aromatic oil 5 parts, rosin 3 parts, antioxidant 4020 1.5 parts, antioxidant RD 1 part, zinc oxide 5 parts, stearic acid 2 parts, sulfur 0.9 parts, accelerator NS 2 parts, scorch inhibitor 0.1 part ;

[0034] The preparation method of the racing tread rubber comprises the following steps:

[0035] One stage of masterbatch: in parts by weight, 15 parts of natural rubber, 120 parts of styrene-butadiene rubber carbon black masterbatch, 5 parts of styrene-butadiene rubber, 3 parts of high styrene resin, 2 parts of carbon black BL101, 3 parts of carbon black BL201 parts, 5 parts of aromatic oil, 3 parts of rosin, 1 part of antioxidant 4020, 1 part of antioxi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of tire preparation, and particularly relates to a racing tire tread rubber formula and a preparation method thereof. The formula comprises 10-20 parts ofnatural rubber, 100-120 parts of butadiene styrene rubber carbon black masterbatch, 5-30 parts of butadiene styrene rubber, 3-10 parts of high styrene resin, 5-25 parts of carbon black, 4-8 parts of aromatic oil, 2-4 parts of rosin, 1.5-2 parts of an antiager 4020, 1-1.5 parts of an antiager RD, 5 parts of zinc oxide, 2 parts of stearic acid, 0.9-1.6 parts of sulfur, 1-2 parts of an accelerator, and 0.1-0.4 parts of an antiscorching agent. The racing tire tread rubber formula can greatly improve the dispersing performance of the high structure and high specific surface area filler in the butadiene styrene rubber, thereby fully exerting the mechanics and mechanical properties of the formula; a tire prepared by the formula has excellent ground gripping property, wear resistance and mechanical properties, the tire can travel for a long distance, and the service life is long.

Description

technical field [0001] The invention belongs to the technical field of tire preparation, and in particular relates to a racing car tread rubber formula and a preparation method thereof. Background technique [0002] The wear resistance of tire tread rubber is one of the key performance indicators of tires. When the tire is running, the tread is in direct contact with the road surface. Under the action of periodic compression and shear deformation, the tread rubber usually falls off in the form of wear, curl and fatigue. Different from ordinary tires, racing tires have extremely high requirements for grip and handling performance. During high-speed driving, tangential and lateral forces cause great tread deformation and heat generation. Good grip is required to maintain good body stability performance. In addition, racing tires frequently turn and brake, and have higher requirements on the wear resistance of the tread. The traditional racing tread uses high filling to impr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L9/06C08L7/00C08L91/00C08L93/04C08K13/02C08K3/04C08K3/22C08K5/09C08K5/3437C08K5/18B60C1/00
CPCB60C1/0016C08K2003/2296C08L9/06C08L2205/025C08L2205/035C08L7/00C08L91/00C08L93/04C08K13/02C08K3/04C08K3/22C08K5/09C08K5/3437C08K5/18
Inventor 赵江华
Owner JIANGSU GENERAL SCI TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap