A kind of composite reactive black dye and its application

A reactive black and dye technology, applied in the field of dyes, can solve the problems of poor washability, low fixation rate, low dye depth, sticky color, etc., and achieve the effects of increasing washability, reducing the amount of dyes used for dyeing, and reducing production costs.

Active Publication Date: 2021-02-02
HUBEI HUALI DYESTUFF INDAL
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Black reactive dyes are the most widely used and produced varieties of dyes. At present, most of the dyes used in the market are compounded by adding orange components to C.I. reactive black 5, but there is still a color fixation rate in the dyeing process. It has low dyeing and deepness, and there are also problems such as poor washing performance and serious color sticking

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of composite reactive black dye and its application
  • A kind of composite reactive black dye and its application
  • A kind of composite reactive black dye and its application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036]Mix 80 parts of the dye of formula (1), 20 parts of the dye of formula (2), and 1 part of the dye of formula (3) and then fully mechanically mix to obtain the composite reactive black dye of the present invention. This dye can print and dye fiber material fibers. High level dyeing, high fixing rate, high jet black fullness and good dyeing depth.

[0037]Dip dyeing: respectively, 1g of the dye prepared according to Example 1 is first fully dissolved with an appropriate amount of water, and then the volume is fixed to a 250ml volumetric flask, and 50ml of dye solution is mixed with 50ml of water, and then 5g cotton cloth and 6g sodium sulfate are added. Then increase the temperature to 60°C at a rate of 1°C / min, keep for 30 minutes, add 2g of sodium carbonate, keep at 60°C and dye for 30 minutes, then take out the dyed cotton cloth and boil it with a non-ionic detergent for 15 minutes, then wash with water. Dry at around 70℃.

[0038]Anti-dyeing printing: Sprinkle 3 parts of the dye p...

Embodiment 2

[0040]Mix 70 parts of formula (1) dye, 25 parts of formula (2) dye, and 5 parts of formula (3) dye and then fully mechanically mix to obtain the composite reactive black dye of the present invention. This dye can print and dye fiber material fibers. High level dyeing, high fixing rate, high jet black fullness and good dyeing depth

[0041]Dip dyeing: 1g of the dye prepared according to Example 2 is first fully dissolved in an appropriate amount of water, and then the volume is fixed in a 250ml volumetric flask, 50ml of dye solution is mixed with 50ml of water, and then 5g of cotton cloth and 6g of sodium sulfate are added. Then increase the temperature to 60°C at a rate of 1°C / min, keep for 30 minutes, add 2g of sodium carbonate, keep at 60°C and dye for 30 minutes, then take out the dyed cotton cloth and boil it with non-ionic detergent for 15 minutes, then wash with water Dry at around 70℃.

[0042]Anti-dye printing: Sprinkle 2 parts of the dye prepared in Example 7 into 100 parts conta...

Embodiment 3

[0044]Mix 60 parts of the dye of formula (1), 35 parts of the dye of formula (2), and 5 parts of the dye of formula (3) to obtain the composite reactive black dye of the present invention. This dye can print and dye fiber materials High level dyeing, high fixing rate, high jet black fullness and good dyeing depth.

[0045]Dip dyeing: 1g of the dye prepared according to Example 3 is first fully dissolved with an appropriate amount of water, then the volume is fixed in a 250ml volumetric flask, 50ml of dye solution is mixed with 50ml of water, and then 5g of cotton cloth and 6g of sodium sulfate are added. Then increase the temperature to 60°C at a rate of 1°C / min, keep for 30 minutes, add 2g of sodium carbonate, keep at 60°C and dye for 30 minutes, then take out the dyed cotton cloth and boil it with a non-ionic detergent for 15 minutes, then wash with water. Dry at around 70℃.

[0046]Anti-dye printing: Sprinkle 3 parts of the dye prepared in Example 7 into 100 parts containing 50 parts o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of dyes, in particular to a composite reactive black dye, comprising a dye shown in formula (1), a dye shown in formula (2) and a dye shown in formula (3), in parts by weight The proportioning ratio is as follows: 50-100 parts of the dye of the formula (1), 5-45 parts of the dye of the formula (2), and 0-5 parts of the dye of the formula (3). The present invention also provides a black dye composition, including a color-fixing alkali agent, a dyeing accelerator and the above-mentioned composite reactive black dye. The composite reactive black dye provided by the present invention has higher dyeing depth, good color fixation rate and washing performance, and low raw material cost. The compounding of the three dyes of formula (3) makes the dyed fabric have higher level dyeing property, high color fixing rate and high fastness, and achieves unprecedented jet-black fullness and dyeing depth, and increases the washability of the dye It solves the problems of poor washability and serious color sticking of existing reactive black dyes, and is suitable for exhaust dyeing, pad dyeing and resist printing of fiber materials.

Description

Technical field[0001]The invention belongs to the technical field of dyes, and specifically relates to a composite reactive black dye and its application.Background technique[0002]In recent years, composite dye technology has developed rapidly, and composite reactive dyes have become more and more widely used. Mixing different reactive dyes can play a synergistic effect.[0003]Black reactive dyes are a variety of dyes with more applications and larger yields. At present, most of the dyes used in the market are compounded by adding orange components to CI Reactive Black 5, but they still have a fixation rate during the dyeing process. It has low dyeing depth, poor detergency and serious color sticking.Summary of the invention[0004]In order to overcome the shortcomings of the above-mentioned prior art, the purpose of the present invention is to provide a composite reactive black dye and its application, which not only has low production cost, high dye depth, good color fixation rate, h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09B67/24C09B67/36C09B62/513C09B62/507C09B62/51D06P1/384D06P1/673D06P1/48D06P1/649D06P1/62D06P3/66
CPCC09B62/507C09B62/51C09B62/513C09B67/005C09B67/0073C09B67/0079D06P1/384D06P1/48D06P1/628D06P1/6491D06P1/6735D06P3/666
Inventor 崔孟元朱纯杰熊建平张志华
Owner HUBEI HUALI DYESTUFF INDAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products