A rolling finishing method for hot-rolled steel

A rebar and screw thread technology, which is applied in the field of hot-rolled rebar manufacturing and rolling finishing, can solve problems such as affecting the appearance, difficult to remove impurities and burrs, and scratches on the surface of rebar

Active Publication Date: 2020-06-16
大冶华鑫实业有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, there are following problems in the existing threaded steel processing process: one, after the threaded steel is water-cooled, there are often protrusions such as impurities and burrs between the rib lines, which affect the appearance, and are easy to scratch the workers during use. 2. It is often difficult to clean the inner wall of the finishing equipment for rebar, which makes it difficult to remove impurities and burrs, which makes the surface of rebar scratches

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A rolling finishing method for hot-rolled steel
  • A rolling finishing method for hot-rolled steel
  • A rolling finishing method for hot-rolled steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0032] The embodiments of the present invention will be described in detail below with reference to the accompanying drawings, but the present invention can be implemented in many different ways defined and covered by the claims.

[0033] Such as Figure 1 to Figure 6 Shown, a kind of rebar hot-rolled manufacturing rolling finishing method comprises the following steps:

[0034] S1. Rebar feeding: the rebar is fed through the feed roller 23, and the rebar is fed in isolation through the feeding partition 21;

[0035] S2, water cooling of threaded steel: water-cooling treatment is carried out to the threaded steel being fed in step S1 through the water cooling device 4;

[0036] S3, finishing treatment: perform finishing treatment on the threaded steel after the water-cooling treatment in step S2 by rotating the inner cylinder 34;

[0037] S4, cooling bed placement: place the threaded steel after the finishing treatment in step S3 on the step-by-step cooling bed for natural c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a rolling finish machining method for hot rolled ribbed bar hot rolling manufacturing. The method is characterized in that a base, a feeding unit, finish machining units and awater cooling device are involved, the feeding unit is mounted at the upper end of the base, the finish machining units are mounted on the inner walls of the left end and the right end of the base, and the water cooling device is mounted at the left end of the base. According to the provided rolling finish machining method for hot rolled ribbed bar hot rolling manufacturing, finish machining treatment of surface lines is carried out on a hot rolled ribbed bar subjected to hot rolling, so that impurities and burrs are removed, the problems that the burrs affect attractiveness, and meanwhile, workers are prone to being scratched and hurt in the using process are solved, a finish machining mechanism is cleaned while the hot rolled ribbed bar is water cooled through the water cooling device,so that the situation that due to the fact that the impurities such as the burrs scratch the surface of the hot rolled ribbed bar, the attractiveness is affected is prevented.

Description

technical field [0001] The invention relates to the technical field of sheet material processing, in particular to a method for hot-rolling, manufacturing, and rolling finishing of rebar. Background technique [0002] Rebar is a common name for hot-rolled ribbed steel bar. The grade of ordinary hot-rolled steel bar is composed of HRB and the minimum yield point of the grade. H, R, and B are the English initials of the three words Hotrolled, Ribbed, and Bars, respectively. Rebar is an important building material, which is widely used in the construction of houses, bridges, roads and other civil engineering. my country is a big producer of rebar, with an output of 131 million tons in 2010, accounting for more than 70% of the global output. At present, our country is at the peak of modernization construction, housing and infrastructure construction is booming, which strongly supports the pace of social modernization. [0003] However, there are following problems in the exist...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B21B15/00B21B43/12B21B43/00B21B45/02
CPCB21B15/00B21B15/0007B21B43/003B21B43/12B21B45/0224B21B2015/0014
Inventor 郭东东姚孝明
Owner 大冶华鑫实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products