Separation disposal process for stainless steel thin-film plate waste roll
A technology of stainless steel and scrap coils, which is applied in the field of separation and disposal of stainless steel thin film scrap coils, can solve the problems of continuous separation and difficulty in recycling, and achieve the effect of classified recycling and high-efficiency separation
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment example 1
[0020] to combine figure 1 For description, a galvanized sheet with a thickness of 0.95mm and a width of 1219mm is selected as the substrate and a 304 stainless steel with a thickness of 0.25mm and a width of 1219mm is bonded by an adhesive. The strip steel travel speed is 5m / min for waste disposal. The stainless steel composite plate waste roll is uncoiled by the uncoiler 1, pinched by the pinch roller 2, and then sent to the entrance shear 3 to cut the head neatly. The previous roll of waste and the next roll of waste are snapped together by the seaming machine 4, and the deviation is corrected by the entrance. After the roller 5 enters the single-sided radiation heating furnace 6, under the single-sided heating condition of the electromagnetic radiation tube 7, the furnace temperature is kept at 270°C, and after entering the water mist cooling pool 8, under the action of the water mist cooling nozzle 9, the water volume is controlled at 10m 3 / h, so that the stainless stee...
Embodiment example 2
[0022] to combine figure 1 To describe, choose a galvanized sheet with a thickness of 1.1mm and a width of 1219mm as the substrate and a 304 stainless steel with a thickness of 0.1mm and a width of 1219mm, which is bonded by an adhesive. The strip steel travel speed is 5m / min for waste disposal. The stainless steel composite plate waste roll is uncoiled by the uncoiler 1, pinched by the pinch roller 2, and then sent to the entrance shear 3 to cut the head neatly. The previous roll of waste and the next roll of waste are snapped together by the seaming machine 4, and the deviation is corrected by the entrance. After the roller 5 enters the single-sided radiation heating furnace 6, under the single-sided heating condition of the electromagnetic radiation tube 7, the furnace temperature is kept at 250°C, and after entering the water mist cooling pool 8, under the action of the water mist cooling nozzle 9, the water volume is controlled at 10m 2 / h, so that the stainless steel cl...
Embodiment example 3
[0024] to combine figure 1 To describe, choose a galvanized sheet with a thickness of 2.0mm and a width of 1219mm as the substrate and a 304 stainless steel with a thickness of 0.4mm and a width of 1219mm, which is bonded by an adhesive. The strip steel travel speed is 10m / min for waste disposal. The stainless steel composite plate waste roll is uncoiled by the uncoiler 1, pinched by the pinch roller 2, and then sent to the entrance shear 3 to cut the head neatly. The previous roll of waste and the next roll of waste are snapped together by the seaming machine 4, and the deviation is corrected by the entrance. After the roller 5 enters the single-sided radiation heating furnace 6, under the single-sided heating condition of the electromagnetic radiation tube 7, the furnace temperature is kept at 330°C, and after entering the water mist cooling pool 8, under the action of the water mist cooling nozzle 9, the water volume is controlled at 15m 3 / h, so that the stainless steel c...