Concrete strength enhancer capable of realizing defect maintenance

A technology of concrete strength and reinforcing agent, which is applied in the field of concrete reinforcing agent, which can solve the problems of concrete strength, safety in use and environmental protection, etc., and achieve the effect of improving strength, safety in use and improving rebound value

Inactive Publication Date: 2020-05-12
深圳市保富新型建材有限公司
6 Cites 0 Cited by

AI-Extracted Technical Summary

Problems solved by technology

[0003] However, there are many deficiencies in the strength, wear resistance and durability of concrete in the concrete reinf...
View more

Method used

The product effect of the present invention is to infiltrate, seal, corrode and polish again, by fully infiltrating, its active ingredient can produce chemical reaction with concrete rapidly, increases the compactness of structure, and penetration depth is concrete top layer 5-8mm, forms a kind of The three-dimensional net-like compact whole, matured and blocked, makes the concrete surface form a solid concrete layer, permanently locks the pores, increases the strength density, and thus obtains permanent closure...
View more

Abstract

The invention discloses a concrete strength enhancer capable of realizing defect maintenance. The concrete strength enhancer is prepared from the following components in parts by weight: 3-10 parts ofsilicate, 3-10 parts of an alkaline activator, 3-10 parts of a cement-based capillary crystalline material, 8 to 16 parts of a siloxane emulsion, 2-8 parts of a soluble aluminum salt, 0.1 to 5 partsof an auxiliary agent, 0.05 to 0.1 part of a wetting agent and 50-70 parts of water. The concrete strength enhancer provided by the invention effectively enhances the strength of concrete, has the functions of reinforcing and curing the concrete and enhancing the rebound value of the concrete, and is safe to use and friendly to environment.

Technology Topic

Crystalline materialsEmulsion +7

Examples

  • Experimental program(5)
  • Effect test(1)

Example Embodiment

[0032] Example 1
[0033] A concrete strength defect curing and strengthening agent, which is made of the following components by weight:
[0034] 3 parts of silicate;
[0035] 3 parts of alkaline stimulator;
[0036] 10 parts of cement-based permeable crystalline material;
[0037] 16 parts of silicone emulsion;
[0038] 2 parts of soluble aluminum salt;
[0039] Additive 0.1 part;
[0040] Wetting agent 0.05 parts;
[0041] 50 parts of water.

Example Embodiment

[0042] Example 2
[0043] A concrete strength defect curing and strengthening agent, which is made of the following components by weight:
[0044] 10 parts of silicate;
[0045] 10 parts of alkaline stimulator;
[0046] 3 parts of cement-based infiltrating crystalline material;
[0047] 8 parts of silicone emulsion;
[0048] 8 parts of soluble aluminum salt;
[0049] 5 parts of additives;
[0050] 0.1 part of wetting agent;
[0051] 70 parts of water.

Example Embodiment

[0052] Example 3
[0053] A concrete strength defect curing and strengthening agent, which is made of the following components by weight:
[0054] 6 parts of silicate;
[0055] Alkaline stimulator 5 parts;
[0056] 8 parts of cement-based permeable crystalline material;
[0057] 14 parts of silicone emulsion;
[0058] 3 parts of soluble aluminum salt;
[0059] Additive 0.1 part;
[0060] Wetting agent 0.05 parts;
[0061] 55 parts of water.

PUM

no PUM

Description & Claims & Application Information

We can also present the details of the Description, Claims and Application information to help users get a comprehensive understanding of the technical details of the patent, such as background art, summary of invention, brief description of drawings, description of embodiments, and other original content. On the other hand, users can also determine the specific scope of protection of the technology through the list of claims; as well as understand the changes in the life cycle of the technology with the presentation of the patent timeline. Login to view more.

Similar technology patents

Coal gangue haydite and its prepn process

InactiveCN1337378AExtensive resourceshigh strength
Owner:杨普安

Terylene camouflage waterproof cloth

Owner:FUJIAN SIJIA ENVIRONMENTAL PROTECTION MATERIAL TECH

Implementation method of selective laser sintering (SLS) technology and fiber implantation device

InactiveCN102990933AIncreased fiber aspect ratiohigh strength
Owner:广州市锐鼎机电设备有限公司

Classification and recommendation of technical efficacy words

Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products