Method for preparing antistatic black master batch from graphene-coated carbon black, and product
A technology for alkene-coated carbon black and black masterbatch, applied in the field of preparation of carbon black colored masterbatch, can solve the problems of difficult dispersion of polymer matrix, substandard antistatic performance, low concentration of black masterbatch, etc. Electrostatic properties, excellent antistatic properties, the effect of improving product stability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0055] Example 1
[0056] First, 1g sodium lauryl sulfate (the mass ratio of carbon black and sodium lauryl sulfate is 40:1), CSX-941 carbon black and ethanol (the mass ratio of carbon black and ethanol is 1:1) Stir evenly at 60°C, and obtain modified carbon black dispersion after mixing and reaction, and then obtain modified carbon black after drying; then disperse graphene oxide and modified carbon black in 100 ml of water (graphene oxide and modified carbon black) The mass ratio of carbon black is 1:50), the graphene oxide aqueous solution is added to the modified carbon black aqueous solution, and stirred evenly to obtain a graphene oxide-coated carbon black dispersion; finally, the prepared graphene oxide-coated carbon black is After the black dispersion is centrifuged, washed and dried, graphene oxide-coated carbon black is obtained. Figure 1a The optical microscope image of the graphene oxide-coated carbon black dispersion prepared by Example 1; Figure 1b It is the ...
Example Embodiment
[0059] Example 2
[0060] First, 1g of DL-602 (the mass ratio of carbon black and DL-602 is 40:1), CSX-941 carbon black and ethanol (the mass ratio of carbon black and ethanol is 1:1) are stirred evenly at 60 °C , obtain modified carbon black dispersion liquid after mixing reaction, obtain modified carbon black after drying; then disperse graphene oxide and modified carbon black in 100ml of water respectively (the difference between the quality of graphene oxide and modified carbon black is ratio of 1:50), adding the graphene oxide aqueous solution to the modified carbon black aqueous solution, stirring evenly to obtain a graphene oxide-coated carbon black dispersion; finally, centrifuging and washing the prepared graphene oxide-coated carbon black dispersion After drying, graphene oxide-coated carbon black is obtained. Add 1 g of graphene oxide-coated modified carbon black to 100 ml of deionized water for ultrasonic dispersion, add reducing agent ascorbic acid and react at 6...
Example Embodiment
[0062] Example 3
[0063] First, 1g APS and DL-602 (the mass ratio of carbon black and DL-602 is 40:1; the mass ratio of APS and DL-602 is 1:1), CSX-941 carbon black and ethanol (carbon black and ethanol) The mass ratio is 1:5) at 60 ℃, stir evenly, and after mixing reaction, the modified carbon black dispersion is obtained, and after drying, the modified carbon black is obtained; then the graphene oxide and the modified carbon black are dispersed separately. In 100ml of water (the mass ratio of graphene oxide and modified carbon black is 1:70), the graphene oxide aqueous solution is added to the modified carbon black aqueous solution, and stirred evenly to obtain a graphene oxide-coated carbon black dispersion; After centrifuging the prepared graphene oxide-coated carbon black dispersion, washing and drying, the graphene oxide-coated carbon black is obtained. Add 1 g of graphene oxide-coated modified carbon black to 100 ml of deionized water for ultrasonic dispersion, add re...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap