Supporting steel for containment vessel of nuclear power station and manufacturing method thereof

A nuclear power plant containment and manufacturing method technology, applied in the field of metals, can solve the problems of inability to guarantee strength performance and low element content, and achieve the effects of good plasticity, toughness, high safety factor and stable performance

Inactive Publication Date: 2020-07-03
ANGANG STEEL CO LTD +1
View PDF11 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This type of steel is designed with a low carbon equivalent composition, and the content of C, Si, Ni and other elements is low, which cannot guarantee the strength performance of the steel plate when the thickness reaches 100mm or more. Performance is not concerned

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Supporting steel for containment vessel of nuclear power station and manufacturing method thereof
  • Supporting steel for containment vessel of nuclear power station and manufacturing method thereof
  • Supporting steel for containment vessel of nuclear power station and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0034] Below by embodiment the present invention will be further described.

[0035] The embodiments of the present invention carry out smelting, continuous casting, heating, rolling and heat treatment according to the composition ratio of the technical solution. The composition of the steel of the embodiment of the present invention is shown in Table 1. The main process parameters of the steel of the embodiment of the present invention are shown in Table 2. The main technological parameters of the heat treatment of the steel of the embodiment of the present invention are shown in Table 3. The performance of the steel of the embodiment of the present invention is shown in Table 4.

[0036] Table 1 Composition (wt %) of the embodiment steel of the present invention

[0037] Example C Si mn Ni Cr Mo Alt Cu V Ti P S N 1 0.12 0.30 1.45 0.48 0.35 0.26 0.026 0.064 0.038 0.015 0.008 0.004 0.0064 2 0.16 0.45 1.65 0.65 0.48 0.5...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides supporting steel for a containment vessel of a nuclear power station and a manufacturing method thereof. The steel comprises the following components in percentage by weight: 0.10%-0.16% of C, 0.25%-0.45% of Si, 1.40%-1.65% of Mn, 0.45%-0.65% of Ni, 0.20%-0.50% of Cr, 0.20%-0.55% of Mo, 0.02%-0.04% of Alt, 0.05%-0.10% of Cu, 0.03-0.05% of V, 0.005-0.020% of Ti, 0.008% or less of P, 0.005% of less of S, 0.010% or less of N, and the balance being Fe and unavoidable impurities. The manufacturing method comprises smelting, continuous casting, heating, rolling and heat treatment. The thickness of a steel plate produced from the steel is 30-80 mm, the steel plate in the quenched and tempered state, simulated post-weld heat treatment state and 200 DEG C high temperature state completely meets the requirements of technical indicators, and meanwhile -40 DEG C impact absorption energy is still remained at a high level.

Description

technical field [0001] The invention belongs to the field of metals, and in particular relates to a support steel for a containment vessel of a nuclear power plant and a manufacturing method thereof. Background technique [0002] Due to the rapid development of my country's nuclear power industry in recent years, especially after experiencing the lessons of the Fukushima nuclear power plant accident, higher requirements have been put forward for the safety of nuclear power related equipment, and the safety and reliability of nuclear power plants are very important. The nuclear power plant containment is a sealed structure outside the nuclear reactor, and it is the landmark building of the nuclear power plant. All the equipment of the nuclear steam supply system are installed in it, as the last barrier against radiation, and it is also the equipment with the largest amount of steel in the nuclear power unit. Preventing or mitigating the release of radioactive substances into ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/58C22C38/50C22C38/46C22C38/44C22C38/42C22C38/06C22C38/04C22C38/02C22C33/04C21C7/10C21C7/072B22D11/16C21D8/02C21D1/25
CPCB22D11/16C21C7/072C21C7/10C21D1/25C21D8/0205C21D8/0226C21D2211/009C22C33/04C22C38/001C22C38/002C22C38/02C22C38/04C22C38/06C22C38/42C22C38/44C22C38/46C22C38/50C22C38/58
Inventor 王爽胡海洋乔馨颜秉宇段江涛李黎明石锋涛王勇崔福祥孙殿东
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com