Adhesive composition and adhesion-reducing adhesive tape applied to optical filter cutting
A composition and adhesive technology, applied in the direction of adhesives, adhesive types, ester copolymer adhesives, etc., can solve the problems of low peeling force, difficult to peel off and difficult to peel off the adhesive tape, and achieve peeling force performance stable effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0071] The invention provides an adhesive composition and a viscous-reducing adhesive tape applied to cutting filters.
[0072] In the adhesive composition, select butyl (meth)acrylate unit (45-55%), methyl (meth)acrylate unit (40-50%) and 2-hydroxyethyl (meth)acrylate A (meth)acrylate copolymer (commercially available product A) composed of units (1-5%), with a weight-average molecular weight of 500,000-600,000, weighing 100 parts by mass; select a polyurethane containing 10 unsaturated double bond functional groups Acrylate oligomer (commercially available product A), molecular weight 40000, weighing 30 parts by mass; choose hexafunctional dipentaerythritol hexaacrylate as polyfunctional acrylic acid monomer (manufactured by Changxing Chemical: EM265), weigh 5.0 parts by mass; choose Toluene diisocyanate was used as a curing agent (manufactured by Tosoh Chemical: CORONATE L), weighing 1.5 parts by mass; 1-hydroxycyclohexyl phenyl ketone was selected as a photoinitiator (manu...
Embodiment 2
[0075] The invention provides an adhesive composition and a viscous-reducing adhesive tape applied to cutting filters.
[0076] In the adhesive composition, select butyl (meth)acrylate unit (45-55%), methyl (meth)acrylate unit (40-50%) and 2-hydroxyethyl (meth)acrylate A (meth)acrylate copolymer (commercially available product A) composed of units (1-5%), with a weight-average molecular weight of 500,000-600,000, weighing 100 parts by mass; select a polyurethane containing 10 unsaturated double bond functional groups Acrylate oligomer (commercially available), molecular weight 40000, weighing 30 parts by mass; choose hexafunctional dipentaerythritol hexaacrylate as polyfunctional acrylic acid monomer (manufactured by Changxing Chemical: EM265), weigh 10 parts by mass; choose toluene Diisocyanate was used as a curing agent (manufactured by Tosoh Chemical: CORONATE L), and 1.5 parts by mass was weighed; 1-hydroxycyclohexyl phenyl ketone was used as a photoinitiator (manufactured...
Embodiment 3
[0079] The invention provides an adhesive composition and a viscous-reducing adhesive tape applied to cutting filters.
[0080] In the adhesive composition, select butyl (meth)acrylate unit (45-55%), methyl (meth)acrylate unit (40-50%) and 2-hydroxyethyl (meth)acrylate A (meth)acrylate copolymer (commercially available product A) composed of units (1-5%), with a weight-average molecular weight of 500,000-600,000, weighing 100 parts by mass; Urethane acrylate oligomer (commercially available product A), molecular weight 40,000, weighed 30 parts by mass; selected hexafunctional dipentaerythritol hexaacrylate as the polyfunctional acrylic monomer (manufactured by Changxing Chemical: EM265), weighed 5.0 parts by mass; Select toluene diisocyanate as a curing agent (manufactured by Tosoh Chemical: CORONATE L), and weigh 1.5 parts by mass; select 1-hydroxycyclohexyl phenyl ketone as a photoinitiator (manufactured by BASF: 184), and weigh 1.5 parts by mass.
[0081] The adhesive comp...
PUM
Property | Measurement | Unit |
---|---|---|
Young's modulus of elasticity | aaaaa | aaaaa |
Young's modulus of elasticity | aaaaa | aaaaa |
Young's modulus of elasticity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap