A kind of preparation method of continuous casting and rolling aluminum alloy material

An aluminum alloy, casting and rolling technology, which is applied in the field of continuous casting and rolling of aluminum alloy materials, can solve the problems of low strength of finished products, improper composition ratio, and affecting service life, etc.

Active Publication Date: 2021-09-14
包头常铝北方铝业有限责任公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the continuous casting and rolling aluminum alloy materials for louvers in the prior art, due to improper composition ratio of raw materials in the preparation process, as well as improper processes such as smelting, casting and rolling, resulting in low strength of the finished product and affecting the service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] The preparation method of the continuous casting and rolling aluminum alloy material of the present invention comprises the following steps:

[0027] (1) Proportioning the raw materials of the aluminum alloy material according to the composition and weight percentage, the raw materials include 0.4-0.6% by weight of Fe, 0.5-0.8% by weight of Si, 0.2-0.4% by weight of Mn, 0.2-0.3% by weight % by weight of Cu, 0.6-0.8% by weight of Mg, 0-0.1% by weight of Zn, 0-0.05% by weight of Ti, 0.005-0.008% by weight of B and 0.06-0.08% by weight of rare earth elements, the balance being aluminum , wherein the rare earth element is Yb and / or Lu;

[0028] (2) Melting the proportioned raw materials at 715-735°C for 1-3 hours, followed by refining, slag removal, online degassing and filtration;

[0029] (3) Continuously casting the aluminum alloy melt obtained in step (2) at a casting rate of 600-800mm / min at 660-680°C to obtain a cast-rolled coil with a thickness of 5-7mm;

[0030] (...

Embodiment 1

[0046] (1) Proportioning the raw materials of the aluminum alloy material according to the composition and weight percentage, the raw materials include 0.45% by weight of Fe, 0.7% by weight of Si, 0.25% by weight of Mn, 0.25% by weight of Cu, 0.75% by weight Mg, 0.05% by weight of Zn, 0.025% by weight of Ti, 0.006% by weight of B and 0.07% by weight of rare earth elements, and the balance is aluminum, wherein the rare earth elements are a mixture of Yb and Lu;

[0047] (2) Melting the proportioned raw materials at 725°C for 2 hours, then refining at 700°C for 2 hours, removing slag, degassing online, and filtering with an 80-mesh ceramic filter;

[0048] (3) Continuously cast and roll the aluminum alloy melt obtained in step (2) at a casting rate of 680mm / min at 670°C to obtain a cast-rolled coil with a thickness of 6mm;

[0049] (4) cooling the cast-rolled coil obtained in step (3) to 45° C. for cold rolling to obtain a cold-rolled aluminum coil with a thickness of 1.5 mm;

...

Embodiment 2

[0053] (1) Proportioning the raw materials of the aluminum alloy material according to the composition and weight percentage, the raw materials include 0.6% by weight of Fe, 0.5% by weight of Si, 0.4% by weight of Mn, 0.2% by weight of Cu, 0.65% by weight Mg, 0.09% by weight of Zn, 0.05% by weight of Ti, 0.008% by weight of B and 0.06% by weight of rare earth elements, the balance is aluminum, wherein the rare earth element is Yb;

[0054] (2) Melting the proportioned raw materials at 715°C for 3 hours, then refining at 720°C for 1 hour, removing slag, degassing online, and filtering with a 50-mesh ceramic filter;

[0055] (3) Continuous casting and rolling of the aluminum alloy melt obtained in step (2) at a casting rate of 600 mm / min at 660° C. to obtain a cast-rolling coil with a thickness of 5 mm;

[0056] (4) cooling the cast-rolled coil obtained in step (3) to 35° C. for cold rolling to obtain a cold-rolled aluminum coil with a thickness of 2 mm;

[0057] (5) performing...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of aluminum alloy material preparation, and discloses a preparation method of continuous casting and rolling aluminum alloy material. The method comprises: (1) proportioning the raw materials of the aluminum alloy; (2) melting the raw materials at 715-735° C. for 1-3 hours, followed by refining, slag removal, online degassing and filtering; (3) mixing The aluminum alloy melt is continuously cast and rolled at 660-680°C at a casting rate of 600-800mm / min to obtain cast-rolled coils with a thickness of 5-7mm; (4) cooling the cast-rolled coils to 35-55°C for cooling (5) Cut the edge of the cold-rolled aluminum coil and perform intermediate annealing at 220-250°C and keep it warm for 5-10 hours; (6) Cold-roll the aluminum coil to an aluminum material with a thickness of 0.1-0.15mm, straighten and straighten After cutting into finished products. In the method, by optimizing the composition and content of the raw material of the aluminum alloy material and adopting an intermediate annealing method, the finished product of the aluminum alloy material has excellent tensile strength.

Description

technical field [0001] The invention relates to the technical field of aluminum alloy preparation, in particular to a preparation method of continuous casting and rolling aluminum alloy. Background technique [0002] Aluminum alloy shutters are deeply loved by consumers because of their beautiful appearance, good ventilation and shading properties, and waterproof, moisture-proof, and mildew-proof. However, the continuous casting and rolling aluminum alloy materials for louvers in the prior art, due to improper composition ratio of raw materials in the preparation process, as well as improper processes such as smelting, casting and rolling, lead to low strength of the finished product and affect the service life. Contents of the invention [0003] The purpose of the present invention is to overcome the problems existing in the prior art and provide a method for preparing continuous casting and rolling aluminum alloy materials. The method optimizes the composition and conten...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/02C22C21/08C22C1/02C22C1/06C22F1/043C22F1/047C22F1/05E06B7/08
CPCC22C1/026C22C1/06C22C21/02C22C21/08C22F1/043C22F1/047C22F1/05E06B7/08
Inventor 陆伟良张海平吕兵辉叶普庆
Owner 包头常铝北方铝业有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More