Lead-acid storage battery polar plate manufacturing Method and device

A technology for lead-acid batteries and manufacturing methods, which is applied to the electrodes of lead-acid batteries, and can solve problems such as low efficiency, falling off of active materials, and affecting the quality of plates, so as to achieve the effects of ensuring production quality and improving production efficiency

Pending Publication Date: 2020-12-04
CHAOWEI POWER CO LTD
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Lead-acid battery plates need to be cured during the manufacturing process. Before curing, the stacked plates are manually shaped, and then the plates are forked onto the curing frame with a fork. On the one hand, manual stacking of plates is inefficient, and on the other hand During the shaping process, due to the weight of the plates, there will be a large friction between the plates during the process of pushing the plates, which will cause the active material on the plate surface to fall off and affect the quality of the plates.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lead-acid storage battery polar plate manufacturing Method and device
  • Lead-acid storage battery polar plate manufacturing Method and device
  • Lead-acid storage battery polar plate manufacturing Method and device

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] The present invention will be further described below in conjunction with specific embodiments.

[0026] Such as figure 1 , figure 2 and Figure 7 As shown, the lead-acid battery pole plate manufacturing device of the present invention includes a continuous pole plate slicing device, a conveyor belt 5, a pole plate collecting device 10, a curing device (not shown in the figure), and the continuous pole plate slicing device includes a first point Sheet device 4 and the second slice device 6, the first slice device 4 comprises traction wheel 7 and the cutter wheel 8 that is positioned at described traction wheel top, conveyer belt 5 comprises drive wheel 9, and the second slice device 6 comprises cutter The cutter wheel 14, the cutter wheel includes a vertical cutting knife formed on its surface. 1. The cutter wheel 8 includes a cross-cut knife 11 formed on its surface. The cutter wheel 11 has a central axis X of the cutter wheel. The cross-cut knife 11 extends along ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a lead-acid storage battery polar plate manufacturing method, which is characterized by comprising the following steps of: 1, fragmenting a continuous polar plate to obtain unit polar plates; 2, conveying the unit polar plates to a polar plate collecting device; 3, carrying out automatic shaping on the unit polar plates by means of the polar plate collecting device; and 4,feeding the shaped polar plate into a curing chamber for curing. The invention further discloses a lead-acid storage battery polar plate manufacturing device adopting a polar plate fragmentation method. According to the lead-acid storage battery polar plate manufacturing device and the lead-acid storage battery polar plate manufacturing method, the production efficiency can be improved, and the polar plate production quality is guaranteed.

Description

technical field [0001] The invention relates to the field of pole plate production in the storage battery field. Background technique [0002] Lead-acid battery plates need to be cured during the manufacturing process. Before curing, the stacked plates are manually shaped, and then the plates are forked onto the curing frame with a fork. On the one hand, manual stacking of plates is inefficient, and on the other hand During the shaping process, due to the weight of the polar plates, there will be greater friction between the polar plates during the process of pushing the polar plates, which will cause the active material on the surface of the polar plates to fall off and affect the quality of the polar plates. Contents of the invention [0003] In order to solve the above-mentioned technical problems, the present invention provides a method for manufacturing lead-acid battery pole plates, which is characterized in that it includes the following steps: Step 1: slice the con...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/22H01M4/23H01M4/20
CPCH01M4/20H01M4/22H01M4/23Y02E60/10
Inventor 杨新新叶剑程兴
Owner CHAOWEI POWER CO LTD