Composition containing bioglass ceramic and application of composition in scar repair

A technology of biological glass and composition, which is applied in the field of medical materials, can solve the problems of insignificant scar repair effect and weak repair function, and achieve great clinical application value and human body safety and reliability.

Active Publication Date: 2020-12-11
温州医科大学慈溪生物医药研究院
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, rubbing preparations for external use are popular because they are convenient to use, painless, and low in cost. However, the existing rubbing preparations for external use have the disadvantages of weak repair function and insignificant scar repair effect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composition containing bioglass ceramic and application of composition in scar repair
  • Composition containing bioglass ceramic and application of composition in scar repair

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The composition containing biological glass-ceramics of this embodiment is made of the following raw materials in parts by weight: 20 parts of biological glass with a particle size of <5 μm, 3 parts of biological glass-ceramics with a particle size of less than 5 μm, 25 parts of organic silicon elastomers, organic 38 parts of silicone oil, 0.4 parts of collagen solution, 2.3 parts of Brucea javanica oil, 2.3 parts of peach kernel oil, 1.8 parts of natural borneol, 2 parts of ethanol, 0.5 parts of menthol, 0.8 parts of titanium dioxide, 0.3 parts of vitamin A, polyethylene glycol 400 8 parts, purified water 18 parts, cetearyl alcohol 3 parts, citric acid 1 part.

[0033] Its preparation method comprises the following steps:

[0034] 1) Raw material preparation: weigh each raw material according to the formula;

[0035] 2) Mix the silicone elastomer, silicone oil, ethanol and polyethylene glycol 400, and then add bioglass, bioglass ceramics, collagen solution, javanica o...

Embodiment 2

[0038] The composition containing biological glass ceramics of this embodiment is made from the following raw materials in parts by weight: 15 parts of biological glass with a particle size of <5 μm, 10 parts of biological glass ceramics with a particle size of <5 μm, 35 parts of organic silicon elastomers, organic 35 parts of silicone oil, 0.5 parts of collagen solution, 1.8 parts of Brucea javanica oil, 3 parts of peach kernel oil, 1.2 parts of natural borneol, 3 parts of ethanol, 0.5 parts of menthol, 0.8 parts of titanium dioxide, 0.5 parts of vitamin E, polyethylene glycol 400 6 parts, 18 parts of purified water, 3 parts of glyceryl stearate, 1.2 parts of sodium lactate.

[0039] Its preparation method is with embodiment 1.

Embodiment 3

[0041] The composition containing biological glass-ceramics of this embodiment is made from the following raw materials in parts by weight: 8 parts of biological glass with a particle size of <5 μm, 8 parts of biological glass-ceramics with a particle size of less than 5 μm, 42 parts of organic silicon elastomers, organic 20 parts of silicone oil, 0.6 parts of collagen solution, 1.8 parts of Brucea javanica oil, 5 parts of peach kernel oil, 1.2 parts of natural borneol, 3.5 parts of ethanol, 0.3 parts of menthol, 1.2 parts of titanium dioxide, 0.5 parts of vitamin E, polyethylene glycol 400 4 parts, 12 parts of purified water, 4.5 parts of sorbitan olive oil, 1.2 parts of malic acid.

[0042] Its preparation method is with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The embodiment of the invention discloses a composition containing bioglass ceramic and application of the composition in scar repair, and belongs to the technical field of medical materials. The composition is prepared from bioglass, bioglass ceramic, an organic silicon elastomer, organic silicone oil, collagen liquid, brucea javanica oil, peach kernel oil, natural borneol, ethyl alcohol, menthol, titanium dioxide, an antioxidant, polyethylene glycol, purified water, an emulsifier and an acid-base stabilizer. The composition has the effects of removing slough and promoting growth of tissue regeneration, diminishing inflammation and swelling and repairing tissue, fibroblast proliferation and differentiation can be remarkably inhibited, and therefore the effect of relieving or treating scars is achieved. The composition is safe and reliable to the human body, free of adverse reactions and worthy of application and popularization.

Description

technical field [0001] The embodiments of the present invention relate to the technical field of medical materials, in particular to a composition containing biological glass ceramics and its application in scar treatment and repair. Background technique [0002] Scar is the damage of physical, biological, chemical and other factors on the human skin and soft tissue, resulting in serious damage to the skin and soft tissue, which cannot be completely repaired normally by itself, and is replaced by fibrous tissue to repair the local symptoms that affect both appearance and function. The scar tissue formed after wound healing often brings long-term psychological burden and physiological obstacles to patients. [0003] At present, there are various treatments for scars, including compression of scar tissue, drug injection, and topical rubbing preparations. Among them, rubbing preparations for external use are popular because they are convenient to use, painless, and low in cost...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L31/06A61L31/04A61L31/02A61L31/00A61L31/14A61L31/16
CPCA61L31/005A61L31/026A61L31/028A61L31/044A61L31/06A61L31/14A61L31/16A61L2300/216A61L2300/30A61L2300/412C08L71/02C08L83/04
Inventor 张宏宇李力群孔晓霞许可
Owner 温州医科大学慈溪生物医药研究院
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products