A kind of shield slag unfired hollow brick and its preparation method

A hollow brick and shield slag technology, which is applied in the field of shield slag-free burning hollow bricks and its preparation, can solve the problems of unsuitable shield slag, difficulty in breaking shield slag, etc. economic effect

Active Publication Date: 2021-08-27
CENT SOUTH UNIV
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For this reason, one of the objects of the present invention is to provide a shield dregs burn-free hollow brick and its preparation method, to solve the difficulty of shield dregs crushing and shield dregs containing part of the improver which makes the shield dregs unsuitable As a base material for non-fired hollow bricks

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of shield slag unfired hollow brick and its preparation method
  • A kind of shield slag unfired hollow brick and its preparation method
  • A kind of shield slag unfired hollow brick and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] The weight ratio is 40 parts of shield muck, 10 parts of construction waste, 20 parts of machine-made sand, 5 parts of fly ash, 15 parts of cement, 4 parts of quicklime, 5 parts of soil curing agent, and sodium lignosulfonate for water reduction. 2 parts of agent, 3 parts of water glass, 2 parts of activator, 1 part of magnesium oxide, 2 parts of polysiloxane defoamer, 0.5 part of sodium hydroxide, 4 parts of talcum powder and 13 parts of water, according to the free The preparation plan of fired hollow bricks is to make unfired hollow bricks. After 28 days of curing according to the ratio, the unfired hollow bricks are tested for compressive strength, softening coefficient, and relative moisture content.

[0055] The natural moisture content of the shield muck soil sample was tested to be 40%, which is slightly higher than the liquid limit, and the soil is relatively moist. The plasticity index is 17.6, and the liquidity index is 0.86. Judging from the plastic state in...

Embodiment 2

[0060] Different from Example 1, the distribution ratio (weight ratio) of each component is: 50 parts of shield muck, 10 parts of construction waste, 20 parts of machine-made sand, 5 parts of fly ash, 12 parts of cement, 3 parts of quicklime, soil 4 parts of curing agent, 2 parts of polysiloxane defoamer, 0.5 parts of sodium hydroxide, 3 parts of talcum powder, 2 parts of sodium lignosulfonate water reducer, 2 parts of water glass, 2 parts of activator, magnesium oxide 0.5 parts, 13 parts of water.

[0061] After testing, the average compressive strength of the prepared shield slag unfired hollow brick is 11.2MPa, the strength after soaking in water for four days is 9.6MPa, the softening coefficient is 0.86, and the relative moisture content is 29.3%.

Embodiment 3

[0063] Different from Example 1, the distribution ratio (weight ratio) of each component is: 60 parts of shield muck, 20 parts of construction waste, 10 parts of machine-made sand, 10 parts of fly ash, 10 parts of cement, 3 parts of quicklime, soil 3 parts of curing agent, 1 part of polysiloxane defoamer, 0.5 parts of sodium hydroxide, 4 parts of talcum powder, 2 parts of sodium lignosulfonate water reducer, 4 parts of water glass, 2 parts of activator, magnesium oxide 1 part, 15 parts water.

[0064] According to the test, the average compressive strength of the prepared shield slag unfired hollow brick is 7.2MPa, the strength after soaking in water for four days is 5.8MPa, the softening coefficient is 0.81, and the relative moisture content is 34.9%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a non-fired hollow brick of shield tunneling dregs. Sodium oxide, talcum powder and polysiloxane defoamer, eliminate the influence of modifiers in the shield dregs, and stimulate the active substances in the shield dregs to obtain the second-stage dregs; the crushed second-stage dregs and The construction waste is mixed with machine-made sand, fly ash, cement, water glass, activator and water reducer together with water to obtain the admixture; the admixture is pressed and maintained to obtain an unfired hollow brick. The strength of the non-fired hollow brick prepared by the invention can be close to MU15 grade, the softening coefficient is between 0.78-0.92, the water absorption rate is below 15%, and the relative water content can reach below 25%, which meets the specification requirements of building bricks and solves the problem of shield slag Soil emission problem, and no secondary pollution in the production process, through the cooperation of optimal production line equipment, it can produce unfired hollow bricks in batches with high efficiency and high quality.

Description

technical field [0001] The invention relates to the field of treatment of shield dregs, in particular to a shield dregs burning-free hollow brick and a preparation method thereof Background technique [0002] As the main construction method of subway construction, the shield tunneling method has many problems, such as high cost of shield tunneling muck, easy to cause pollution, and potential safety hazards in muck stacking. Because the shield muck contains more secondary clay minerals, etc., it can be used to make clay non-fired hollow bricks by adding a certain amount of consolidation agent, so as to realize the recycling of resources. The patent with the application number CN201911021709.9 discloses an environment-friendly non-fired hollow brick and its preparation method for clay layer shield improved dregs, which solves the problem of shield improved muck treatment and reduces environmental pollution and land occupation. However, the patent provides The addition of defo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/26C04B18/16B28B3/00C04B111/40
CPCB28B3/00C04B18/16C04B28/26C04B2111/40C04B2201/50C04B14/06C04B18/08C04B7/02C04B2103/0068C04B24/18C04B22/064C04B14/042C04B22/062C04B22/066C04B24/42C04B22/002Y02W30/91
Inventor 王树英占永杰付循伟令凡琳王海波冯志耀
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com