Cloisonne manufacturing process free of wire inlaying

A production process, cloisonne technology, applied in the field of cloisonne preparation, can solve the problems of time-consuming and laborious, manual filigree and other problems, and achieve the effect of strong expressiveness

Inactive Publication Date: 2021-01-29
铜陵铜官府文化创意股份公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is that the existing cloisonne production process requires manual filigr

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Embodiment 1: The production process of cloisonné without filigree, which includes the following steps: (1), material selection: cut the qualified copper sheet according to the figure, cut it into shape, heat the copper sheet through fire and soften it, and use a hammer to continuously (2) drawing: select a thin copper plate whose shape and size match the copper sheet, and carve out the required pattern on the thin copper plate; (3), bonding: put the carved thin copper plate on one side Dip in Bletilla striata paste, and stick it on the surface of the copper sheet; (4), welding wire; (5), tire making: bend the copper sheet with the engraved thin copper plate and weld it to make a copper tire; (6), point Blue; (7), burnt blue; (8), polished gold-plated.

Embodiment 2

[0013] Embodiment 2: The manufacturing process of cloisonné without filigree, which includes the following steps: (1), material selection: cut the qualified copper sheet according to the figure, cut it into shape, heat the copper sheet through fire and soften it, and use a hammer to continuously (2) drawing: select a thin aluminum plate whose shape and size match the copper sheet, and carve out the required pattern on the thin aluminum plate; (3), bonding: put the carved thin aluminum plate on one side Dip in Bletilla striata paste and stick it on the surface of the copper sheet; (4), welding wire; (5), tire making: bend and weld the copper sheet coated with the engraved thin aluminum plate to make a copper tire; (6), point Blue; (7), burnt blue; (8), polished gold-plated.

Embodiment 3

[0014] Embodiment 3: In order to select a thin copper plate or a thin aluminum plate that accurately matches the copper sheet, step (2) uses a three-dimensional imaging scanner to scan the copper sheet to obtain appearance data, so as to select a thin copper plate or thin aluminum plate whose shape and size match the copper sheet .

[0015] The innovation of the present invention is to break the existing cloisonne production process, advance the filigree step to complete before the tire production, and stick the prepared pattern on the surface of the copper sheet in the form of a plane, which is easier to operate and greatly improves the production of cloisonné. The efficiency and accuracy of the process, compared with the traditional filigree process, the material selection, drawing, and bonding of the present invention are easy to operate, have lower requirements on people, and are suitable for mass production.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a cloisonne manufacturing process free of wire inlaying. The cloisonne manufacturing process comprises the following steps that (1) material selection is conducted, and a qualified copper sheet is blanked according to a drawing, cut and formed; (2) the drawing is made, a thin copper plate or a thin aluminum plate with the shape and the size being matched with those of the copper sheet is selected, and the required patterns are hollowed on the thin copper plate or the thin aluminum plate; (3) bonding is performed, one surface of the hollowed thin copper plate or thin aluminum plate is dipped with bletilla striata lint paste to be bonded onto the surface of the copper plate; (4) wire welding is carried out; (5) a blank is made, and the copper sheet dipped with the hollowed thin copper plate or thin aluminum plate is made into a copper blank; (6) bluing is performed; (7) enameling is conducted; and (8) polishing and gold plating are carried out. The cloisonne manufacturing process free of wire inlaying has the beneficial effects that the wire inlaying process steps are changed into the steps that the patterns are manufactured on the thin copper plate or the thin aluminum plate in advance, then the patterns are bonded onto the surface of the copper sheet, and afterwards, the copper sheet is manufactured into the blank, so that the problems of low efficiencyand low speed caused by wire inlaying on the surface of the copper blank are solved, and the patterns obtained through plane drawing are more attached to the surface of the copper blank and have stronger expressive force.

Description

technical field [0001] The invention relates to the field of cloisonne preparation. Background technique [0002] Cloisonne is forged with red copper to make the body of utensils. The copper wire is pinched into various patterns and welded on the copper body, filled with enamel and colored glaze, and then fired. The process is called "copper body filigree enamel". . In the middle of the 15th century, the Jingtai period of the Ming Dynasty began to be mass-produced and popular in Beijing. The enamel glaze was mostly blue, so it got its name. It has more than ten processes such as tire making, shaping, painting, filigree, welding wire, bluing, bluing, grinding, finishing, gilding, etc. Most of them are time-consuming and labor-intensive manual operations, which are difficult to meet the batch demand of the modern market. , being able to mass produce cast tires with filigree is the key to the mass production of cloisonné. [0003] The existing filigree process uses tweezers ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B44C5/00B44C1/14B44C3/08
CPCB44C5/00B44C1/14B44C3/087
Inventor 赵敏郭飞
Owner 铜陵铜官府文化创意股份公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap