Underglaze color flashing and noctilucent combined glazed tile and preparation method thereof

A technology of underglaze color and polished glazed tiles, which is applied in the field of ceramics, can solve the problems of lost ornamental and display effects of polished glazed tiles, and achieve the effect of unique individual color and artistic effect

Active Publication Date: 2021-02-19
FOSHAN ZHANGSHI BROS BUILDING MATERIALS
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, at night or in a dark environment, glazed tiles lose their ornamental and display effects.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Underglaze color flashing and noctilucent combined glazed tile and preparation method thereof
  • Underglaze color flashing and noctilucent combined glazed tile and preparation method thereof
  • Underglaze color flashing and noctilucent combined glazed tile and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0060] The preparation steps of the finished product A specifically include:

[0061] S1) Take the brick adobe containing the fired bottom glaze, and print a pattern on the surface of the brick adobe to obtain a pattern layer;

[0062] S2) printing a luminous glaze on a set area on the surface of the pattern layer, and drying to obtain a first luminous layer;

[0063] S3) Printing a flashing glaze on the surface of the first luminous layer, and drying to obtain a flashing layer;

[0064] S4) Applying a transparent glaze on the surface of the adobe including the pattern layer, the glitter layer and the first luminous layer to prepare a semi-finished product A containing a transparent glaze layer;

[0065] S5) Put the semi-finished product A into a kiln, and fire it for 65-90 minutes at a firing temperature of 850°C-910°C to obtain the finished product A

[0066] The method for preparing glazed glazed tiles with underglaze flashing luminous combination in the present invention...

Embodiment 1

[0133] Embodiment 1: It is the finished product A containing the first luminous layer and the flashing layer;

[0134] Calculated by weight percentage, the raw materials of the flash glaze of embodiment 1 include: 8% flash powder and 92% raw glaze;

[0135] Glitter powder is white gold titanium metal powder.

[0136] Calculated by weight percentage, the raw materials of luminous glaze include: 10% sky blue luminous powder and 90% raw glaze;

[0137] Calculated by weight percentage, the chemical composition of the raw material glaze includes:

[0138] Al 2 o 3 11%, SiO 2 53%, Fe 2 o 3 0.05%, CaO 3%, MgO 0.9%, TiO 2 0.03%, B 2 o 3 27%, ZnO 1%, BaO 4% and Li 2 O 0.02%.

[0139] Calculated by weight percentage, the chemical composition of the transparent glaze includes:

[0140] Al 2 o 3 9%, SiO 2 67%, Fe 2 o 3 0.03%, CaO 2%, MgO 0.9%, TiO 2 0.02%, B 2 o 3 17%, ZnO 1%, BaO3% and Li 2 O 0.05%.

[0141] The drying temperature in the steps S2) and S3) i...

Embodiment 2

[0144] Embodiment 2: It is finished product C containing the first luminous layer, mixed luminous layer and second luminous layer;

[0145] Calculated by weight percentage, the raw materials of the flash glaze of embodiment 2 include: 10% flash powder and 90% raw glaze;

[0146] Glitter powder is white gold titanium metal powder.

[0147] Calculated by weight percentage, the raw materials of luminous glaze include: 10% sky blue luminous powder and 90% raw glaze;

[0148] The mixing ratio of the luminous glaze and the flash glaze contained in the mixed glaze is 1.5:2.5;

[0149] Calculated by weight percentage, the chemical composition of the raw material glaze includes:

[0150] Al2 o 3 8%, SiO 2 56%, Fe 2 o 3 0.05%, CaO 3%, MgO 0.9%, TiO 2 0.03%, B 2 o 3 27%, ZnO 2%, BaO 3% and Li 2 O 0.02%; And said raw material glaze is added with Zhudan red powder;

[0151] Calculated by weight percentage, the chemical composition of the transparent glaze includes:

[0152...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an underglaze color flashing and noctilucent combined glazed tile and a preparation method thereof. The underglaze color flashing and noctilucent combined glazedtile comprisesa finished product A, a finished product B and a finished product C, wherein the finished product A, the finished product B and the finished product C are combined for use during paving; the finishedproduct A sequentially comprises a green tile layer, a pattern layer, a first noctilucent layer, a flashing layer and a transparent glaze layer from bottom to top; the finished product B sequentiallycomprises a green tile layer, a pattern layer, a first noctilucent layer, a flashing layer, a second noctilucent layer and a transparent glaze layer from bottom to top; and the finished product C sequentially comprises a green tile layer, a pattern layer, a first luminous layer, a mixed luminous layer, a second luminous layer and a transparent glaze layer from bottom to top. Light emitted by the noctilucent powder irradiates the outer surface of the flashing powder and is mutually reflected to form a three-dimensional luminous pattern. The invention further provides a preparation method of theunderglaze color flashing and noctilucent combined glazed tile. The prepared underglaze color flashing and noctilucent combined glazed tile has noctilucent and flashing effects at the same time.

Description

technical field [0001] The invention relates to the technical field of ceramics, in particular to a composite polished glazed brick with flashing underglaze color at night and a preparation method thereof. Background technique [0002] The flash bricks in the prior art are ever-changing, and can display their own styles under common lighting environments, and have very good individual characteristics. [0003] However, at night or in a dark environment, glazed tiles lose their ornamental and display effects. [0004] How to make the individual display of flash bricks better play at night or in a dark environment is a topic worthy of further development. Contents of the invention [0005] The purpose of the present invention is to overcome the above-mentioned defects in the prior art, combine the actual needs, and use the luminous and reflective physical properties of the luminescent powder and the flashing powder to propose a combined polished glazed brick with underglaze...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B41/89C03C8/00C03C8/14
CPCC03C8/00C03C8/14C04B41/52C04B41/89C04B41/5022C04B41/524
Inventor 章云党
Owner FOSHAN ZHANGSHI BROS BUILDING MATERIALS