Non-slip sole and preparation method thereof

An anti-slip and anti-slip agent technology, applied in the field of anti-slip soles and their preparation, can solve the problems of increasing the wear degree of the anti-slip rubber, increasing the friction force, short service life of the anti-slip rubber, etc., so as to enhance the anti-slip effect Effect

Pending Publication Date: 2021-02-26
蔡美玉
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although the existing anti-slip rubber can play an anti-slip effect, it does not take into account the increased friction due to anti-slip, which in turn increases the degree of wear of the anti-slip rubber, making the service life of the anti-slip rubber short

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-slip sole and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0044] Prepare anti-slip sole, preferred material parts by weight form as follows:

[0045] Nitrile rubber: 50 parts

[0046] Bromobutyl rubber: 10 parts

[0047] White carbon black: 17 parts

[0048] Anti-slip agent ceramic powder: 3 parts

[0049] Polyvinyl acetal modified phenolic resin: 1 part

[0050] Phenolic antioxidants: 0.6 parts

[0051] Anti-fogging agent paraffin: 0.5 parts

[0052] Vulcanizing agent sulfur powder: 2 parts

[0053] Thiuram accelerator: 1.3 parts

[0054] Active agent zinc oxide: 4 parts

[0055] White smoke active agent polyvinyl alcohol: 2 parts

[0056] Petroleum resin: 3 parts

[0057] Tackifying resin: 5 parts

[0058] Zinc stearate: 2 parts

[0059] Rubber wear-resistant oil: 1 part

[0060] Rubber anti-slip agent: 2 parts

[0061] Anti-emetic cream: 1.5 parts

[0062] Anti-yellowing accelerator: 1 part

[0063] 1S-80: 0.2 parts

[0064] TS-80: 0.3 parts

[0065] D-80: 0.3 parts

[0066] DM-80: 0.5 parts

[0067] NS-80: 0.5 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a non-slip sole, which is prepared by blending nitrile rubber and brominated butyl rubber, matching with petroleum resin, tackifying resin, a rubber non-slip agent and non-slip agent ceramic powder, and matching with a corresponding preparation process, and has the advantages of enhancing the non-slip effect, greatly improving the the anti-slip effect of the sole on glass,stainless steel, and the ceramic tile.

Description

Technical field: [0001] The invention relates to an anti-slip sole and a preparation method thereof, in particular, the manufactured sole can walk on water-soaked roads without slipping. Background technique: [0002] The anti-skid ability of shoes is an important indicator, which is directly related to whether you can take a step and walk easily. In normal occasions, the use of the anti-slip texture design of the sole can basically meet the anti-slip requirements, but when walking on the road with water stains, it often slips, which makes people worry. For this reason, the industry is also doing research and development on materials in order to improve the anti-slip ability of sole materials and solve the anti-slip problem from the source. For example, Patent Application No. 201611203175.8 discloses a non-slip rubber sole, which comprises the following components in parts by weight: 60 parts of nitrile rubber, 20 parts of brominated butyl rubber, 15 parts of styrene-butadi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L9/02C08L23/28C08L61/14C08L91/06C08L29/04C08L57/02C08L91/00C08K13/04C08K7/26C08K3/22C08K5/098C08K3/06A43B13/04
CPCC08L9/02A43B13/04C08L2205/02C08L2205/035C08K2201/003C08K2003/2296C08L23/283C08L61/14C08L91/06C08L29/04C08L57/02C08L91/00C08K13/04C08K7/26C08K3/22C08K5/098C08K3/06
Inventor 蔡美玉
Owner 蔡美玉