A kind of fine-grained steel with tensile strength of 1500mpa and preparation method thereof

A technology of tensile strength and fine grain, which is applied in the field of research and development of fine grain steel production, can solve the problems that the production process is difficult to reach the tensile level, and achieve the effect of improving toughness and tensile capacity

Active Publication Date: 2022-02-15
JIANGSU YONGGANG GROUP CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides a fine-grained steel with a tensile strength of 1500MPa and a preparation method thereof, aiming to solve the problem that with the continuous development of science and technology and the continuous improvement of building safety, the demand for rigid-strength steel is getting higher and higher, and the existing production process The problem that it is difficult to meet the requirement that the tensile level reaches 1500MPa

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of fine-grained steel with tensile strength of 1500mpa and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] In order to make the object, technical solution and advantages of the present invention clearer, the present invention will be further described in detail below in conjunction with the accompanying drawings and embodiments. It should be understood that the specific embodiments described here are only used to explain the present invention, not to limit the present invention.

[0022] The invention provides a technical solution: a fine-grained steel with a tensile strength of 1500 MPa, the chemical composition ratio of the fine-grained steel: C: 0.21-0.26wt%, Si: 0.40-0.54wt%, Mn: 1.48-1.66wt% %, Cr: 0.20~0.25wt%, Nb: 0.012~0.017wt%, V: 0.095~0.110wt%, S: ≤0.040wt%, P: ≤0.043wt%, O: ≤0.0070wt%, N: 0.0240 ~0.0265wt%, the rest is Fe and impurities that cannot be purified at this stage.

[0023] In this embodiment, the steel material is firstly heated and melted, and the heating is continued to rapidly reduce the amount of oxygen in the steelmaking furnace. When tapping beg...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention is applicable to the technical field of fine-grained steel production research and development, and provides a fine-grained steel with a tensile strength of 1500 MPa and a preparation method thereof, including the fine-grained steel, and the chemical composition ratio of the fine-grained steel: C: 0.21-0.26 wt%, Si: 0.40~0.54wt%, Mn: 1.48~1.66wt%, Cr: 0.20~0.25wt%, Nb: 0.012~0.017wt%, V: 0.095~0.110wt%, S: ≤0.040wt%, P: ≤0.043wt%, O: ≤0.0070wt%, N: 0.0240-0.0265wt%, and the rest are Fe and impurities that cannot be purified at the present stage. The invention improves the toughness of the steel so that the steel has a tensile strength of at least 1500MPa, Meet the needs of people's production and life.

Description

technical field [0001] The invention belongs to the field of research and development of fine-grained steel production, and in particular relates to a fine-grained steel with a tensile strength of 1500 MPa and a preparation method thereof. Background technique [0002] Steel is a material of a certain shape, size and performance made of steel ingots, billets or steel through pressure processing. Most steel processing is through pressure processing, which causes plastic deformation of the processed steel (billet, ingot, etc.). According to the different processing temperature of steel, it can be divided into cold processing and hot processing. [0003] With the continuous development of science and technology and the continuous improvement of building safety, the demand for rigid steel is getting higher and higher. It is difficult for the existing production process to meet the requirement of tensile grade of 1500MPa. Contents of the invention [0004] The invention provi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/24C22C38/26C22C38/38C21D1/18C21D6/00C21D8/02C21D9/00C22C33/04
CPCC22C38/02C22C38/04C22C38/38C22C38/26C22C38/24C22C38/002C22C38/001C21D1/18C21D6/002C21D6/005C21D6/008C22C33/04C21D8/0221C21D9/0081
Inventor 蔡雪贞徐卫单文瑞
Owner JIANGSU YONGGANG GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com