Waterproof, anti-cutting, flame-retardant, high-temperature-resistant and wear-resistant flyknit shoes
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A cutting-resistant and high-temperature-resistant technology, which is applied in the field of flying woven shoes, can solve the problems of being easily cut by knives, being susceptible to fire, and poor fire resistance, so as to achieve simple manufacturing processes, reduce manufacturing costs, and save materials. Effect
Inactive Publication Date: 2021-03-26
江伟明
View PDF9 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] Nowadays, when consumers buy shoes, they no longer only consider the appearance of the shoes, but also focus on the comfort of the shoes. Therefore, the appearance and comfort of the shoes are the key to determining the sales of a shoe. However, the existing shoes , poor fire resistance, easy to be burned by fire, and at the same time, the existing shoes will be easily cut by knives, which will easily cause damage to the feet and cause a lot of inconvenience to the wearer
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0064] Embodiment 1, a kind of waterproof, anti-knife cut, anti-flame retardant, high temperature resistance, wear-resistant flying woven shoes manufacturing process steps are as follows:
[0065] Step 1: Make the midsole fabric, draw a line 15mm wide from the edge on the surface of the midsole fabric;
[0066] Step 2: Make the midsole waterproof membrane, the size of the midsole waterproof membrane is the same as that of the midsole cloth;
[0069] The fifth step: making the front lining Hong Kong treasure and the back lining Hong Kong treasure;
[0070] Step 6: Make the heel sponge, the thickness of the sponge is 8mm;
[0071] Step 7: Make the waterproof membrane of the shoe body;
[0072] Step 8: cut the anti-knife upper material;
[0073] Step 9: Press the shoe upper made in step 8 with the waterproof membrane made in step 7, the pressing temperature is 150°C, and the pressing time is 8-10s;
...
Embodiment 2
[0118] Embodiment 2, a waterproof, anti-knife, anti-flame retardant, high temperature resistant, wear-resistant flying woven shoes. The manufacturing process and processing steps are as follows:
[0119] Step 1: Make the midsole fabric, draw a line 15mm wide from the edge on the surface of the midsole fabric;
[0120] Step 2: Make the midsole waterproof membrane, the size of the midsole waterproof membrane is the same as that of the midsole cloth;
[0123] The fifth step: making the front lining Hong Kong treasure and the back lining Hong Kong treasure;
[0124] Step 6: Make the heel sponge, the thickness of the sponge is 8mm;
[0125] Step 7: Make the waterproof membrane of the shoe body;
[0126] Step 8: cut the anti-knife upper material;
[0127] Step 9: Press the shoe upper made in step 8 with the waterproof membrane made in step 7. The pressing temperature is 150°C and the pressing time is 10s;...
Embodiment 3
[0172] Embodiment 3, a waterproof, anti-knife, anti-flame retardant, high temperature resistance, wear-resistant flying woven shoes. The manufacturing process and processing steps are as follows:
[0173] Step 1: Make the midsole fabric, draw a line 15mm wide from the edge on the surface of the midsole fabric;
[0174] Step 2: Make the midsole waterproof membrane, the size of the midsole waterproof membrane is the same as that of the midsole cloth;
[0177] The fifth step: making the front lining Hong Kong treasure and the back lining Hong Kong treasure;
[0178] Step 6: Make the heel sponge, the thickness of the sponge is 8mm;
[0179] Step 7: Make the waterproof membrane of the shoe body;
[0180] Step 8: cut the anti-knife upper material;
[0181] Step 9: Press the shoe upper made in step 8 with the waterproof membrane made in step 7. The pressing temperature is 150°C and the pressing time is 9s;...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
Thickness
aaaaa
aaaaa
Login to View More
Abstract
The invention belongs to the technical field of shoe manufacturing processes, and relates to waterproof, anti-cutting, flame-retardant, high-temperature-resistant and wear-resistant flyknit shoes. Themanufacturing process of the waterproof, anti-cutting, flame-retardant, high-temperature-resistant and wear-resistant flyknit shoes comprises the following steps of: making insole cloth; manufacturing insole waterproof films; manufacturing heel braids; manufacturing linings; applying powder glue onto the inner surfaces of the linings; applying powder glue onto the elastic edge wrapping strips ofheelpieces; wrapping heel splicing parts with the elastic edge wrapping strips; applying powder glue at the heel splicing parts; stitching the heelpiece braids; trimming front lining counters and rearlining counters; applying yellow glue onto the linings and combined positions of vamps; applying yellow glue onto the linings; sewing the heels of the linings; sewing and opening the heelpieces; pasting the front lining counters and the rear lining counters; turning side lines of the linings; pressing the vamps into cold molds for shaping the vamps; baking the vamps and the insole cloth in a baking box; pasting waterproof films on sole parts; performing die pressing; drawing lines and wiping glue positions; applying waterproof glue A; performing baking in the baking box; pasting soles; pressing the soles; and freezing and sizing. The manufacturing process is simple, can effectively save materials and reduce the production and manufacturing cost; and the manufactured shoes can be waterproof, flame-retardant, high-temperature-resistant, wear-resistant and anti-cutting, so that the feet of a user are protected, the protection effect is good; and the manufacturing process is worthy of application and popularization.
Description
technical field [0001] The invention relates to the technical field of shoe manufacturing technology, in particular to a waterproof, knife-resistant, flame-resistant, high-temperature-resistant and wear-resistant flying woven shoe. Background technique [0002] Nowadays, when consumers buy shoes, they no longer only consider the appearance of the shoes, but also focus on the comfort of the shoes. Therefore, the appearance and comfort of the shoes are the key to determining the sales of a shoe. However, the existing shoes , poor fire resistance, easy to be burned by fire, and existing shoes can be easily cut by knives simultaneously, thereby easily causing damage to feet, causing a lot of inconvenience to the wearer. Contents of the invention [0003] The purpose of the present invention is to propose a waterproof, knife-proof, flame-retardant, high-temperature-resistant and wear-resistant flying woven shoe in order to solve the shortcomings in the prior art. [0004] In o...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.